Granular precipitate that was a new kind ofβ-Mg17Al12 phase found in aged AZ80 wrought Mg alloy at all aging temperature was studied. The structure and precipitation behavior of this granularβ-Mg17Al12 precipitate w...Granular precipitate that was a new kind ofβ-Mg17Al12 phase found in aged AZ80 wrought Mg alloy at all aging temperature was studied. The structure and precipitation behavior of this granularβ-Mg17Al12 precipitate were studied by environmental scanning electron microscopy (ESEM) and transmission electron microscopy (TEM). The effect of the granular precipitate on mechanical properties of AZ80 alloy was also studied. The new precipitate that was granular and nucleated both on grain boundaries (GBs) and twin boundaries, has the same crystal structure and lattice parameter as those of the continuous or discontinuous precipitatedβ-Mg17Al12. And the nucleation and growth of the granular precipitate are faster than those of the other two precipitates at higher temperatures (above 583 K), but are suppressed at lower temperatures (below 423 K). At lower temperatures, the discontinuousβ-Mg17Al12 precipitates firstly and the granularβ-Mg17Al12 precipitates after aged more than 40 h. The crack is easily nucleated on the phase boundaries of granular phase and matrix because of the weak binding force. As a result, the strength and ductility of AZ80 Mg alloy are decreased by the granularyβ-Mg17Al12 precipitate.展开更多
Development of immediate fitting socket system for artificial leg (evaluation of strength and casting performance);Development of new 55%AI-Zn coated steel sheets with excellent corrosion resistance and formability &q...Development of immediate fitting socket system for artificial leg (evaluation of strength and casting performance);Development of new 55%AI-Zn coated steel sheets with excellent corrosion resistance and formability """"SUPERGENIUS"""";Developments in the texturing of sheet-metal surfaces;Double-sided high-pressure tubular hydroforming;Effect of adiabatic heating in some processes of plastic展开更多
基金Project (2001AA331050) supported by the Hi-Tech Research And Development Program Of China
文摘Granular precipitate that was a new kind ofβ-Mg17Al12 phase found in aged AZ80 wrought Mg alloy at all aging temperature was studied. The structure and precipitation behavior of this granularβ-Mg17Al12 precipitate were studied by environmental scanning electron microscopy (ESEM) and transmission electron microscopy (TEM). The effect of the granular precipitate on mechanical properties of AZ80 alloy was also studied. The new precipitate that was granular and nucleated both on grain boundaries (GBs) and twin boundaries, has the same crystal structure and lattice parameter as those of the continuous or discontinuous precipitatedβ-Mg17Al12. And the nucleation and growth of the granular precipitate are faster than those of the other two precipitates at higher temperatures (above 583 K), but are suppressed at lower temperatures (below 423 K). At lower temperatures, the discontinuousβ-Mg17Al12 precipitates firstly and the granularβ-Mg17Al12 precipitates after aged more than 40 h. The crack is easily nucleated on the phase boundaries of granular phase and matrix because of the weak binding force. As a result, the strength and ductility of AZ80 Mg alloy are decreased by the granularyβ-Mg17Al12 precipitate.
文摘Development of immediate fitting socket system for artificial leg (evaluation of strength and casting performance);Development of new 55%AI-Zn coated steel sheets with excellent corrosion resistance and formability """"SUPERGENIUS"""";Developments in the texturing of sheet-metal surfaces;Double-sided high-pressure tubular hydroforming;Effect of adiabatic heating in some processes of plastic