A seed-directed approach to synthesizing Fe ZSM-22 zeolite without organic structure directing agent(OSDA)was developed by using Fe-rich diatomite as all aluminum and iron sources.The Fe ZSM-22zeolite with optimal cry...A seed-directed approach to synthesizing Fe ZSM-22 zeolite without organic structure directing agent(OSDA)was developed by using Fe-rich diatomite as all aluminum and iron sources.The Fe ZSM-22zeolite with optimal crystallinity and purity can be obtained by systematically adjusting feed composition and synthesis conditions.Characterizations show that Fe ZSM-22 zeolite synthesized with OSDA-free owns high crystallinity,obvious thin needle-shaped morphology and high Bronsted/Lewis acid ratio.Significantly,when used for n-octane hydroisomerization reaction,its derived catalyst exhibits the best catalytic performance reflected by the highest selectivity to C_(8)isomers compared to the two reference catalysts prepared based on a Fe-containing and a Fe-free ZSM-22 synthesized through an OSDA-directed route from natural diatomite and conventional chemicals,respectively.This work provides an alternative route to sustainably synthesizing heteroatomic zeolites with high performance.展开更多
NaY zeolites are synthesized using submolten salt depolymerized natural perlite mineral as the main silica and alumina sources in a 0.94 L stirred crystallizer.Effects of alkalinity ranging from 0.38 to 0.55(n(Na_(2)O...NaY zeolites are synthesized using submolten salt depolymerized natural perlite mineral as the main silica and alumina sources in a 0.94 L stirred crystallizer.Effects of alkalinity ranging from 0.38 to 0.55(n(Na_(2)O)/n(SiO_(2)))on the relative crystallinity,textural properties and crystallization kinetics were investigated.The results show that alkalinity exerts a nonmonotonic influence on the relative crystallinity and textural properties,which exhibit a maximum at the alkalinity of 0.43.The nucleation kinetics are studied by fitting the experimental data of relative crystallinity with the Gualtieri model.It is shown that the nucleation rate constant increases with increasing alkalinity,while the duration period of nucleation decreases with increasing alkalinity.For n(Na_(2)O)/n(SiO_(2))ratios ranging from 0.38 to 0.55,the as-synthesized NaY zeolites exhibit narrower crystal size distributions with the increase in alkalinity.The growth rates determined from the variations of average crystal size with time are 51.09,157.50,46.17 and 24.75 nm·h^(-1),respectively.It is found that the larger average crystal sizes at the alkalinity of 0.38 and 0.43 are attributed to the dominant role of crystal growth over nucleation.Furthermore,the combined action of prominent crystal growth and the longer duration periods of nucleation at the alkalinity of 0.38 and 0.43 results in broader crystal size distributions.The findings demonstrate that control of the properties of NaY zeolite and the crystallization kinetics can be achieved by conducting the crystallization process in an appropriate range of alkalinity of the reaction mixture.展开更多
基金the financial supports from the National Natural Science Foundation of China(22322803,22178059,22208054,22221005,22072019)Key Technologies Innovation and Industrialization Projects of Fujian Province(2022G031)Qingyuan Innovation Laboratory(00121002,00523005)。
文摘A seed-directed approach to synthesizing Fe ZSM-22 zeolite without organic structure directing agent(OSDA)was developed by using Fe-rich diatomite as all aluminum and iron sources.The Fe ZSM-22zeolite with optimal crystallinity and purity can be obtained by systematically adjusting feed composition and synthesis conditions.Characterizations show that Fe ZSM-22 zeolite synthesized with OSDA-free owns high crystallinity,obvious thin needle-shaped morphology and high Bronsted/Lewis acid ratio.Significantly,when used for n-octane hydroisomerization reaction,its derived catalyst exhibits the best catalytic performance reflected by the highest selectivity to C_(8)isomers compared to the two reference catalysts prepared based on a Fe-containing and a Fe-free ZSM-22 synthesized through an OSDA-directed route from natural diatomite and conventional chemicals,respectively.This work provides an alternative route to sustainably synthesizing heteroatomic zeolites with high performance.
基金supports from National Natural Science Foundation of China(21938009,22308358,22208346,22078332)National Key Research and Development Program(2022YFC3902701)+2 种基金Ningxia Natural Science Foundation(2021AAC01002)the External Cooperation Program of BIC,Chinese Academy of Sciences(122111KYSB20190032)CAS Project for Young Scientists in Basic Research(YSBR-038)are gratefully acknowledged.
文摘NaY zeolites are synthesized using submolten salt depolymerized natural perlite mineral as the main silica and alumina sources in a 0.94 L stirred crystallizer.Effects of alkalinity ranging from 0.38 to 0.55(n(Na_(2)O)/n(SiO_(2)))on the relative crystallinity,textural properties and crystallization kinetics were investigated.The results show that alkalinity exerts a nonmonotonic influence on the relative crystallinity and textural properties,which exhibit a maximum at the alkalinity of 0.43.The nucleation kinetics are studied by fitting the experimental data of relative crystallinity with the Gualtieri model.It is shown that the nucleation rate constant increases with increasing alkalinity,while the duration period of nucleation decreases with increasing alkalinity.For n(Na_(2)O)/n(SiO_(2))ratios ranging from 0.38 to 0.55,the as-synthesized NaY zeolites exhibit narrower crystal size distributions with the increase in alkalinity.The growth rates determined from the variations of average crystal size with time are 51.09,157.50,46.17 and 24.75 nm·h^(-1),respectively.It is found that the larger average crystal sizes at the alkalinity of 0.38 and 0.43 are attributed to the dominant role of crystal growth over nucleation.Furthermore,the combined action of prominent crystal growth and the longer duration periods of nucleation at the alkalinity of 0.38 and 0.43 results in broader crystal size distributions.The findings demonstrate that control of the properties of NaY zeolite and the crystallization kinetics can be achieved by conducting the crystallization process in an appropriate range of alkalinity of the reaction mixture.