A novel room-temperature ionic liquid (RTIL),1-allyl,3-methylimidazolium chloride (［AMIM］Cl),was synthesized,ch aracterized and used for dissolving cellulose.The solubility of cellulose in ［ AMIM］Cl was better tha...A novel room-temperature ionic liquid (RTIL),1-allyl,3-methylimidazolium chloride (［AMIM］Cl),was synthesized,ch aracterized and used for dissolving cellulose.The solubility of cellulose in ［ AMIM］Cl was better than in 1-butyl,3-methylimidazolium (［BMIM］Cl).The pris tine cellulose and two cellulose samples regenerated from ［AMIM］Cl and ［BMIM ］Cl solutions were compared by FTIR,WAXD and TGA measurements.Results show t hat these two RTILs are non-derivatizing solvents for cellulose.After regenera tion from RTIL solutions,the crystalline form of cellulose films is completely transformed from cellulose Ⅰ to cellulose Ⅱ.Compared to pristine cellulose,t he regenerated cellulose exhibits a lower onset temperature of thermal decomposi tion,with a higher char yield.展开更多
PLA/MWNT/HA hybrid nanofibers were prepared via electrospinning technology.Multi walled carbon nanotube (MWNT) were first treated by anodic oxidation,which resulted in various functional groups such as C—O,CO and O—...PLA/MWNT/HA hybrid nanofibers were prepared via electrospinning technology.Multi walled carbon nanotube (MWNT) were first treated by anodic oxidation,which resulted in various functional groups such as C—O,CO and O—CO on the surface of oxidized MWNT.Then the MWNT/hydroxyapatite (HA) nano composites (MWNT content 3?wt%) were in situ synthesized by wet method with the help of ultrasonic treatment.Because of the strong interaction between the functional groups on the surface of MWNT and Ca 2+ in HA,the obtained HA nano particles were deposited onto the surface of oxidized MWNT.The as received MWNT/HA nano composites with excellent biocompatibility and osteoinduction were introduced into a bioabsorbable polymer,polylactide (PLA),and the PLA/MWNT/HA hybrid nanofibers were electrospun through a double solvent method under the voltage of 18 kV and the capillary to target distance was 4?cm.The structure and morphology of hybrid nanofibers were characterized by SEM.Because of the nanoscaled diameters,microscaled interconnected pores and suitable surface chemistry,the hybrid nanofibers would match the requirements of ideal bone tissue engineering scaffold and may be a potential material for preparing bone tissue engineering scaffold.展开更多
文摘A novel room-temperature ionic liquid (RTIL),1-allyl,3-methylimidazolium chloride (［AMIM］Cl),was synthesized,ch aracterized and used for dissolving cellulose.The solubility of cellulose in ［ AMIM］Cl was better than in 1-butyl,3-methylimidazolium (［BMIM］Cl).The pris tine cellulose and two cellulose samples regenerated from ［AMIM］Cl and ［BMIM ］Cl solutions were compared by FTIR,WAXD and TGA measurements.Results show t hat these two RTILs are non-derivatizing solvents for cellulose.After regenera tion from RTIL solutions,the crystalline form of cellulose films is completely transformed from cellulose Ⅰ to cellulose Ⅱ.Compared to pristine cellulose,t he regenerated cellulose exhibits a lower onset temperature of thermal decomposi tion,with a higher char yield.
文摘PLA/MWNT/HA hybrid nanofibers were prepared via electrospinning technology.Multi walled carbon nanotube (MWNT) were first treated by anodic oxidation,which resulted in various functional groups such as C—O,CO and O—CO on the surface of oxidized MWNT.Then the MWNT/hydroxyapatite (HA) nano composites (MWNT content 3?wt%) were in situ synthesized by wet method with the help of ultrasonic treatment.Because of the strong interaction between the functional groups on the surface of MWNT and Ca 2+ in HA,the obtained HA nano particles were deposited onto the surface of oxidized MWNT.The as received MWNT/HA nano composites with excellent biocompatibility and osteoinduction were introduced into a bioabsorbable polymer,polylactide (PLA),and the PLA/MWNT/HA hybrid nanofibers were electrospun through a double solvent method under the voltage of 18 kV and the capillary to target distance was 4?cm.The structure and morphology of hybrid nanofibers were characterized by SEM.Because of the nanoscaled diameters,microscaled interconnected pores and suitable surface chemistry,the hybrid nanofibers would match the requirements of ideal bone tissue engineering scaffold and may be a potential material for preparing bone tissue engineering scaffold.
