Graphene oxide(GO)with excellent dispersion ability can assist the dispersion of single-walled carbon nanotube(SWCNT)and promote the formation of uniform and stable GO/SWCNT coating liquid.The highly conductive polyet...Graphene oxide(GO)with excellent dispersion ability can assist the dispersion of single-walled carbon nanotube(SWCNT)and promote the formation of uniform and stable GO/SWCNT coating liquid.The highly conductive polyethylene terephthalate/reduced graphene oxide/SWCNT(PET/rGO/SWCNT)electromagnetic shielding composite fabric was successfully prepared by anchoring rGO/SWCNT on PET fabric via dip-coating piror to low-temperature thermal reduction.The results showed that the carboxyl groups and hydroxyl groups formed of hydrophilic-treated PET were conducive to the formation of hydrogen bonds with that of GO,which enhanced the interaction between PET fabric and GO/SWCNT coating;the loading of GO/SWCNT increased with the number of dip-coating,the unit area loading of rGO/SWCNT in the final composite fabric was 2.7 mg/cm^(2) after 10 dip-coating cycles and thermal reduction;the PET/rGO/SWCNT composite fabric had a continuous and dense conductive network,with a conductivity of up to 41.6 S/m and the average electromagnetic interference shielding effectiveness in X-band was 22 dB;the flexible PET/rGO/SWCNT composite fabric was not only easy to process,but also exhibited excellent conductivity and shielding efficiency,showing great potential in the application of electromagnetic shielding fabrics.展开更多
文摘Graphene oxide(GO)with excellent dispersion ability can assist the dispersion of single-walled carbon nanotube(SWCNT)and promote the formation of uniform and stable GO/SWCNT coating liquid.The highly conductive polyethylene terephthalate/reduced graphene oxide/SWCNT(PET/rGO/SWCNT)electromagnetic shielding composite fabric was successfully prepared by anchoring rGO/SWCNT on PET fabric via dip-coating piror to low-temperature thermal reduction.The results showed that the carboxyl groups and hydroxyl groups formed of hydrophilic-treated PET were conducive to the formation of hydrogen bonds with that of GO,which enhanced the interaction between PET fabric and GO/SWCNT coating;the loading of GO/SWCNT increased with the number of dip-coating,the unit area loading of rGO/SWCNT in the final composite fabric was 2.7 mg/cm^(2) after 10 dip-coating cycles and thermal reduction;the PET/rGO/SWCNT composite fabric had a continuous and dense conductive network,with a conductivity of up to 41.6 S/m and the average electromagnetic interference shielding effectiveness in X-band was 22 dB;the flexible PET/rGO/SWCNT composite fabric was not only easy to process,but also exhibited excellent conductivity and shielding efficiency,showing great potential in the application of electromagnetic shielding fabrics.