Removal of cadmium from aqueous solutions using red mud granulated with cement

A novel adsorbent was prepared from granular red mud mixed with cement and its potential to be a suitable adsorbent for the removal of cadmium ions from aqueous solutions was evaluated. The wet red mud was directly mixed up with cement at different mass fractions of 2%-8% and their properties were investigated. Based on the textural characteristics and strength, the granular red mud with 2% addition of cement maintaining for 6 d is identified to have better properties. The batch adsorption experiments for adsorption of Cd2+ ions from solution were performed at 30, 40 and 50 °C at different initial concentrations under the condition of constant pH of 6.5. The equilibrium adsorption was found to increase with the increase of temperature during the adsorption process. Langmuir adsorption isotherm model was found to match the experimental adsorption isotherm better. The kinetics of adsorption was modeled using a pseudo second order kinetic model and the model parameters were estimated.

Removing chlorine of CuCl residue from zinc hydrometallurgy by microwave roasting

Most Zn hydrometallurgy factories adopt Cu2SO4 as a dechlorination reagent from zinc solution nowadays, thus much CuCl residue is produced. The existing process of treating this residue is washing with water or sodium carbonate solution, which would cause a lot of troubles to water treatment and waste discharge. A method of microwave roasting was adopted for dechlorination of CuCl residue. A 1.5 kW microwave roasting equipment with dust collection and tail gas adsorption systems was set up and applied during the experiment. By investigating the effect of temperature, heat preservation time, moisture content of raw material and grain size of samples on the dechlorination, the optimal experimental condition is obtained. When the samples with 2% moisture and <150 μm grain size are microwave roasted at 400 °C for 2 h, the Cl content turns from 14.27% to 1.35% and the dechlorination rate is as high as 90%, while that with conventional heating is only 60%-80%. The phase change of the roasting process investigated with X-ray diffraction verifies that CuCl in CuCl residue is removed by being transformed into CuO.

Process optimization for treatment of methyltin mercaptide effluents using modified semi-coke

The central composite process optimization was performed by response surface methodology technique using a design for the treatment of methyltin mercaptide with modified semi-coke. The semi-coke from the coal industry was suitably modified by treating it with phosphoric acid, with a thermal activation process. The objective of the process optimization is to reduce the chemical oxygen demand （COD） and NH4＋-N in the methyltin mercaptide industrial effluent. The process variables considered for process optimization are the semi-coke dosage, adsorption time and effluent pH. The optimized process conditions are identified to be a semi-coke dosage of 80 g/L, adsorption time of 90 min and a pH value of 8.34. The ANOVA results indicate that the adsorbent dosage and pH are the significant parameters, while the adsorption time is insignificant, possibly owing to the large range of adsorption time chosen. The textural characteristics of modified semi-coke were analyzed using scanning electron microscopy and nitrogen adsorption isotherm. The average BET surface area of modified semi-coke is estimated to be 915 mE/g, with the average pore volume of 0.71 cm3/g and a average pore diameter of 3.09 nm, with micropore volume contributing to 52.36%.

LaF_3-LiF-La_2O_3系熔盐密度的研究

根据阿基米德定律,测定了La F3-Li F-La2O3熔盐电解质体系的密度,研究了温度、La F3的含量、La2O3加入量对体系密度的影响。结果表明：密度随着温度的升高呈明显线性降低的趋势,而随着La F3含量的增加而增大。在温度为1050℃时,La F3摩尔含量为20%~35%的该熔盐电解质体系的密度随着La2O3加入量的增加先增加后降低,在La2O3的饱和溶解度（1.5%~3%）附近达到最大值。