We present a simple hot press-based method for processing La(Fe,Si)13-based compounds consisting of La–Fe–Co–Si–C particles and phenolic resin. The magnetic entropy change △S per unit mass for the La Fe_(10.87)Co...We present a simple hot press-based method for processing La(Fe,Si)13-based compounds consisting of La–Fe–Co–Si–C particles and phenolic resin. The magnetic entropy change △S per unit mass for the La Fe_(10.87)Co_(0.63)Si_(1.5)C_(0.2)/phenolic resin compounds have nearly the same magnitude with the base materials. With the content of phenolic resin of 5.0 wt%, the compound conductivity is 3.13 W·m^(-1)·K^(-1). In order to measure the cooling performance of La(Fe,Si)13-based compounds,the La(Fe_(11.6-x)Co_(x))Si_(1.4)C_(0.15)(x =0.60, 0.65, 0.75, 0.80, 0.85)/phenolic resin compounds were pressed into thin plates and tested in a hybrid refrigerator that combines the active magnetic refrigeration effect with the Stirling cycle refrigeration effect. The test results showed that a maximum cooling power of 41 W was achieved over a temperature span of 30 K.展开更多
基金supported by the National Natural Science Foundation of China (Grant Nos. 52171054 and 52171195)the National Natural Science Foundation for Distinguished Young Scholars (Grant No. 51925605)。
文摘We present a simple hot press-based method for processing La(Fe,Si)13-based compounds consisting of La–Fe–Co–Si–C particles and phenolic resin. The magnetic entropy change △S per unit mass for the La Fe_(10.87)Co_(0.63)Si_(1.5)C_(0.2)/phenolic resin compounds have nearly the same magnitude with the base materials. With the content of phenolic resin of 5.0 wt%, the compound conductivity is 3.13 W·m^(-1)·K^(-1). In order to measure the cooling performance of La(Fe,Si)13-based compounds,the La(Fe_(11.6-x)Co_(x))Si_(1.4)C_(0.15)(x =0.60, 0.65, 0.75, 0.80, 0.85)/phenolic resin compounds were pressed into thin plates and tested in a hybrid refrigerator that combines the active magnetic refrigeration effect with the Stirling cycle refrigeration effect. The test results showed that a maximum cooling power of 41 W was achieved over a temperature span of 30 K.
文摘采用传统固相烧结法制备了K0.5Na0.5Nb O3-x Al(Fe0.9Mn0.1)O3(KNN-AF9M1)无铅压电陶瓷,着重研究了AF9M1的不同掺杂量(x分别为0,0.02,0.04,0.06,0.08)对陶瓷显微结构和压电性能的影响。结果表明,室温下,少量AF9M1的掺杂并未改变KNN基陶瓷正交相钙钛矿结构,但有助于陶瓷晶粒的生长及致密化。随着AF9M1含量的增加,陶瓷的压电常数(d33)、机电耦合系数(kp)、机械品质因数(Qm)和居里点(Tc)均先增大后减小,当x=0.04时,均达到最大值,分别为121 p C/N、0.35、179和392℃。