To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K...To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K with strain rates of 0.01, 0.1, and 1 s-1. The results show that the measured flow stress should be revised by friction and the calculated values of friction coefficient m are in the range of 0.45-0.56. Arrhenius-type constitutive equation was developed by regression analysis. The comparison between the experimental and predicted flow stress shows that the R~ and the average absolute relative error （AARE） are 0.948 and 5.44%, respectively. The measured apparent activation energy Qa is in the range of 540-890 kJ/mol. Both dis-continuous dynamic recrystallization （DDRX） and continuous dynamic recrystallization （CDRX） mechanisms are observed in the deformed alloy, but dynamic recovery （DRV） is the dominant softening mechanism up to a true strain of 1.5.展开更多
In order to well understand the elementary mechanisms that govern the hot working process of a V？5Cr？5Ti alloy （mass fraction, %）, thermal activation parameters under compression were measured in a temperature ran...In order to well understand the elementary mechanisms that govern the hot working process of a V？5Cr？5Ti alloy （mass fraction, %）, thermal activation parameters under compression were measured in a temperature range of 1373？1673 K by a Gleeble？3800 system. The results show that the stress exponentn is 4.87 and the activation energyQis 375.89 kJ/mol for the power law equation. The activation energy is determined as 288.34 kJ/mol, which is close to the self-diffusion energy of alloy （270？300 kJ/mol） by introducing a threshold stress（σ0） variable. The typical values of physical activation volume （Vp） and strain rate sensitivity （m） are measured as （120？700）b3 and 0.075？0.122, respectively, by the repeated stress relaxation tests. These activation parameters indicate that the rate controlling mechanism for V？5Cr？5Ti alloy compressed in ranges of 1373？1673 K and 0.001？1.0 s？1 is the dislocation climb by overcoming of forest dislocations.展开更多
基金Project(11105127) supported by the National Natural Science Foundation of China
文摘To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K with strain rates of 0.01, 0.1, and 1 s-1. The results show that the measured flow stress should be revised by friction and the calculated values of friction coefficient m are in the range of 0.45-0.56. Arrhenius-type constitutive equation was developed by regression analysis. The comparison between the experimental and predicted flow stress shows that the R~ and the average absolute relative error （AARE） are 0.948 and 5.44%, respectively. The measured apparent activation energy Qa is in the range of 540-890 kJ/mol. Both dis-continuous dynamic recrystallization （DDRX） and continuous dynamic recrystallization （CDRX） mechanisms are observed in the deformed alloy, but dynamic recovery （DRV） is the dominant softening mechanism up to a true strain of 1.5.
基金Project(11105127)supported by the National Natural Science Foundation of China
文摘In order to well understand the elementary mechanisms that govern the hot working process of a V？5Cr？5Ti alloy （mass fraction, %）, thermal activation parameters under compression were measured in a temperature range of 1373？1673 K by a Gleeble？3800 system. The results show that the stress exponentn is 4.87 and the activation energyQis 375.89 kJ/mol for the power law equation. The activation energy is determined as 288.34 kJ/mol, which is close to the self-diffusion energy of alloy （270？300 kJ/mol） by introducing a threshold stress（σ0） variable. The typical values of physical activation volume （Vp） and strain rate sensitivity （m） are measured as （120？700）b3 and 0.075？0.122, respectively, by the repeated stress relaxation tests. These activation parameters indicate that the rate controlling mechanism for V？5Cr？5Ti alloy compressed in ranges of 1373？1673 K and 0.001？1.0 s？1 is the dislocation climb by overcoming of forest dislocations.