The phase equilibria and compositions in Mg-rich comer at 300℃ were determined in the Mg-Zn-A1 ternary system through the equilibrated alloy method by using X-ray diffraction （XRD） and scanning electron microscopy ...The phase equilibria and compositions in Mg-rich comer at 300℃ were determined in the Mg-Zn-A1 ternary system through the equilibrated alloy method by using X-ray diffraction （XRD） and scanning electron microscopy （SEM） assisted with energy dispersive spectroscopy of X-ray （EDS）. The results show that there exist three three-phase regions consisted of a-Mg＋Mg17A112（7）＋A15Mg11Zn4（φ）, a-Mg＋Mga2（Al, Zn）49（r）＋A15MgllZn4（φ） and a-Mg＋MgZn＋Mg32（A1, Zn）49（r）, respectively. The intermetallic compounds in equilibrium with a-Mg phase all have large composition ranges, not appear to be linear. At the same time, both zinc and aluminum are soluble in the a-Mg solid solution, with which the compounds are in equilibrium.展开更多
基金Projects (50901017,50731002) supported by the National Natural Science Foundation of ChinaProject (20090042120008) supported by Doctoral Program Foundation of Institutions of Higher Education of ChinaProjects (N100702001,N090502002) supported by the Fundamental Research Funds of the Central Universities,China
文摘The phase equilibria and compositions in Mg-rich comer at 300℃ were determined in the Mg-Zn-A1 ternary system through the equilibrated alloy method by using X-ray diffraction （XRD） and scanning electron microscopy （SEM） assisted with energy dispersive spectroscopy of X-ray （EDS）. The results show that there exist three three-phase regions consisted of a-Mg＋Mg17A112（7）＋A15Mg11Zn4（φ）, a-Mg＋Mga2（Al, Zn）49（r）＋A15MgllZn4（φ） and a-Mg＋MgZn＋Mg32（A1, Zn）49（r）, respectively. The intermetallic compounds in equilibrium with a-Mg phase all have large composition ranges, not appear to be linear. At the same time, both zinc and aluminum are soluble in the a-Mg solid solution, with which the compounds are in equilibrium.