Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_...Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.展开更多
The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of th...The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of the film to 1.36 T at 300 K and remains 0.938 T at 380 K.As the thickness of the Y spacer layer increases,Y participates in the formation of the main phase in the film,and further regulates the formation of La-B phases.The results of the first-order reversal curve(FORC)and micromagnetic fitting show that the coercivity of all the films is dominated by nucleation mechanism.The c-axis preferred orientation,good magnetic microstructure parameters and the largest dipole interaction enhance the coercivity.Therefore,the introduction of the Y spacer layer can be an effective way to improve the coercivity of La-Nd-Fe-B film over a wide temperature range of 150 K-380 K.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.52371203 and 52271192)the Ministry of Science and Technology of China(Grant No.2021YFB3501201)。
文摘Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.
基金Project supported by the National Key Research and Development Program of China(Grant No.2021YFB3500303)the National Natural Science Foundation of China(Grant Nos.52031014 and 51971219).
文摘The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of the film to 1.36 T at 300 K and remains 0.938 T at 380 K.As the thickness of the Y spacer layer increases,Y participates in the formation of the main phase in the film,and further regulates the formation of La-B phases.The results of the first-order reversal curve(FORC)and micromagnetic fitting show that the coercivity of all the films is dominated by nucleation mechanism.The c-axis preferred orientation,good magnetic microstructure parameters and the largest dipole interaction enhance the coercivity.Therefore,the introduction of the Y spacer layer can be an effective way to improve the coercivity of La-Nd-Fe-B film over a wide temperature range of 150 K-380 K.