Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coati...Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition(CVD)technique.Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces.Additionally,the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test.The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2%(volume fraction)and 11.1%,and 40.7%(volume fraction)and 7.5%,respectively.And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa,and 180.2 MPa and 97.2 GPa,respectively.With a proper thickness,the coating can effectively adjust the fiber/matrix interface,thus causing a dramatic increase in the mechanical properties of the composites.展开更多
基金Project(NCET-07-0228)support by the New Century Excellent Talents in University
文摘Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide(2D-SiC/SiC)composites were molded by stacking method and densified through precursor infiltration and pyrolysis(PIP)process.SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition(CVD)technique.Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces.Additionally,the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test.The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2%(volume fraction)and 11.1%,and 40.7%(volume fraction)and 7.5%,respectively.And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa,and 180.2 MPa and 97.2 GPa,respectively.With a proper thickness,the coating can effectively adjust the fiber/matrix interface,thus causing a dramatic increase in the mechanical properties of the composites.