In this study,a facile and environmentally friendly method with low energy consumption for preparing nanoscale AgCl and BaSO4 co-precipitates(AgCl@BaSO_(4) co-precipitates)was developed based on the metathetical react...In this study,a facile and environmentally friendly method with low energy consumption for preparing nanoscale AgCl and BaSO4 co-precipitates(AgCl@BaSO_(4) co-precipitates)was developed based on the metathetical reaction.Then,the dried co-precipitates were melt-compounded with polyamide 6(PA6)resins at a specified mass ratio in a twin-screw extruder.The results demonstrated that in the absence of any coating agent or carrier,the nanoparticles of AgCl@BaSO_(4) co-precipitates were homogeneously dispersed in the PA6 matrix.Further analysis showed that after the addition of AgCl@BaSO_(4) co-precipitates,the antibacterial performance,along with the flame-retardance and anti-dripping characteristics of PA6,was enhanced significantly.In addition,the PA6 composites possessed high spinnability in producing pre-oriented yarn.展开更多
基金This project was financially supported by the National Key Research Program of China(Grant No.2016YFB0302702)the Open Foundation of National&Local Joint Engineering Laboratory for New Petrochemical Materials and Fine Utilization of Resources(Grant No.KF201804).
文摘In this study,a facile and environmentally friendly method with low energy consumption for preparing nanoscale AgCl and BaSO4 co-precipitates(AgCl@BaSO_(4) co-precipitates)was developed based on the metathetical reaction.Then,the dried co-precipitates were melt-compounded with polyamide 6(PA6)resins at a specified mass ratio in a twin-screw extruder.The results demonstrated that in the absence of any coating agent or carrier,the nanoparticles of AgCl@BaSO_(4) co-precipitates were homogeneously dispersed in the PA6 matrix.Further analysis showed that after the addition of AgCl@BaSO_(4) co-precipitates,the antibacterial performance,along with the flame-retardance and anti-dripping characteristics of PA6,was enhanced significantly.In addition,the PA6 composites possessed high spinnability in producing pre-oriented yarn.