A method to upgrade the iron grade in copper slag was proposed using lime to decompose Al_(2)O_(3)-containing fayalite melt(AFMT).Thermodynamic calculations indicated that adjusting the CaO/AFMT ratio can yield a resi...A method to upgrade the iron grade in copper slag was proposed using lime to decompose Al_(2)O_(3)-containing fayalite melt(AFMT).Thermodynamic calculations indicated that adjusting the CaO/AFMT ratio can yield a residual melt with a FeO concentration of 75−88 wt.%and produce Ca_(2)SiO_(4).In-situ observations suggested that the reaction was impeded in some way.Quenching experiments revealed that the initial reaction products consisted of calcium ferrite compounds and FeO−CaO melt.At the FeO−CaO melt/AFMT interface,Ca_(2)SiO_(4) particles precipitated,forming a dense Ca_(2)SiO_(4) film that significantly impeded mass transfer.Although trace amounts of Al_(2)O_(3) in AFMT temporarily enhanced mass transfer,they were insufficient to overcome this retardation effect.The decomposition reaction was far from achieving equilibrium,demonstrating a self-retardation effect.Measures must be implemented to eliminate this self-retardation effect and enhance the efficiency of reaction kinetics.展开更多
An innovative and effective method of separating chicken meat and bone from chicken skeleton was developed in this study. Different heating approaches to chicken skeleton were compared to optimize cooking conditions i...An innovative and effective method of separating chicken meat and bone from chicken skeleton was developed in this study. Different heating approaches to chicken skeleton were compared to optimize cooking conditions including cooking temperature and cooking time. The separation efficiency of chicken meat and bone in different conditions, including flow direction, impeller speed and the liquid level rising velocity were also studied. Experimental results demonstrated high temperature cooking and assisted mechanical stirring could improve separating rate of chicken skeleton. Liquid flow entering at tangent entrance direction of the kettle could maintain the stability of the liquid level and smoothness of the separation process. The outflow rate of chicken meat increased as the liquid level rising velocity raised, and approached to the maximum value at 0.80 cm/s. The practical application test showed that the best conditions for separation of chicken skeleton were: 45 min cooking time at 114°C;tangent flow direction;stir speed of 200 r/min;the liquid level rising velocity of water is 0.8 cm/s. Using this approach, the value of chicken bone was increased, product specialization was enhanced, and the results could be used in future high value chicken product development.展开更多
The joining of DP780 steel to Al5052 was conducted by laser lap welding,in which the metal vapor and spatters were monitored by a high-speed camera.A universal testing machine was used to test the mechanical propertie...The joining of DP780 steel to Al5052 was conducted by laser lap welding,in which the metal vapor and spatters were monitored by a high-speed camera.A universal testing machine was used to test the mechanical properties of the welded joints,and the changing law of lap tensile resistance with the laser welding parameters was analyzed.Optical microscope and scanning electron microscope were used to observe the macro-structure and micro-structure,respectively.Three different intermetallic compounds(IMCs)phases,i.e.banded Fe2Al5,FeAl2 and needle-like FeAl3 were generated at the steel/Al interface on microscopic observation.The aim of this research is to investigate the relationship among the lap tensile resistance,the welding parameters and the failure mode under different energy densities.Experimental results showed that the steel/Al joints have two different fracture modes at low heat input and high heat input.The failures happened along the heat-affected zone of the weld and along the steel/Al joint interface,respectively.And both of the two failure modes are brittle fractures.Additionally,cracks appeared at the fracture interface,and needle-like particle clusters were found in the fracture microstructure.展开更多
基金supported by the National Natural Science Foundation of China (No.52121004)the National Science Fund for Distinguished Young Scholars (No.51825403)+2 种基金the Science and Technology Innovation Program of Hunan Province,China (No.2021RC3013)National Key R&D Program of China (No.2022YFC3901602)the Major Science and Technology Project of Gansu Province,China (No.21ZD4GD033)。
文摘A method to upgrade the iron grade in copper slag was proposed using lime to decompose Al_(2)O_(3)-containing fayalite melt(AFMT).Thermodynamic calculations indicated that adjusting the CaO/AFMT ratio can yield a residual melt with a FeO concentration of 75−88 wt.%and produce Ca_(2)SiO_(4).In-situ observations suggested that the reaction was impeded in some way.Quenching experiments revealed that the initial reaction products consisted of calcium ferrite compounds and FeO−CaO melt.At the FeO−CaO melt/AFMT interface,Ca_(2)SiO_(4) particles precipitated,forming a dense Ca_(2)SiO_(4) film that significantly impeded mass transfer.Although trace amounts of Al_(2)O_(3) in AFMT temporarily enhanced mass transfer,they were insufficient to overcome this retardation effect.The decomposition reaction was far from achieving equilibrium,demonstrating a self-retardation effect.Measures must be implemented to eliminate this self-retardation effect and enhance the efficiency of reaction kinetics.
文摘An innovative and effective method of separating chicken meat and bone from chicken skeleton was developed in this study. Different heating approaches to chicken skeleton were compared to optimize cooking conditions including cooking temperature and cooking time. The separation efficiency of chicken meat and bone in different conditions, including flow direction, impeller speed and the liquid level rising velocity were also studied. Experimental results demonstrated high temperature cooking and assisted mechanical stirring could improve separating rate of chicken skeleton. Liquid flow entering at tangent entrance direction of the kettle could maintain the stability of the liquid level and smoothness of the separation process. The outflow rate of chicken meat increased as the liquid level rising velocity raised, and approached to the maximum value at 0.80 cm/s. The practical application test showed that the best conditions for separation of chicken skeleton were: 45 min cooking time at 114°C;tangent flow direction;stir speed of 200 r/min;the liquid level rising velocity of water is 0.8 cm/s. Using this approach, the value of chicken bone was increased, product specialization was enhanced, and the results could be used in future high value chicken product development.
基金Project(51675104)supported by the National Natural Science Foundation of ChinaProject(202002020068)supported by the Guangzhou Municipal Special Fund Project for Scientific and Technological Innovation and Development,ChinaProject(2017KCXTD010)supported by the Innovation Team Project,Department of Education of Guangdong Province,China。
文摘The joining of DP780 steel to Al5052 was conducted by laser lap welding,in which the metal vapor and spatters were monitored by a high-speed camera.A universal testing machine was used to test the mechanical properties of the welded joints,and the changing law of lap tensile resistance with the laser welding parameters was analyzed.Optical microscope and scanning electron microscope were used to observe the macro-structure and micro-structure,respectively.Three different intermetallic compounds(IMCs)phases,i.e.banded Fe2Al5,FeAl2 and needle-like FeAl3 were generated at the steel/Al interface on microscopic observation.The aim of this research is to investigate the relationship among the lap tensile resistance,the welding parameters and the failure mode under different energy densities.Experimental results showed that the steel/Al joints have two different fracture modes at low heat input and high heat input.The failures happened along the heat-affected zone of the weld and along the steel/Al joint interface,respectively.And both of the two failure modes are brittle fractures.Additionally,cracks appeared at the fracture interface,and needle-like particle clusters were found in the fracture microstructure.