The optical reflectance and transmittance spectra in the wavelength range of 300-2500 nm are used to compute the absorption coefficient of zinc oxide films annealed at different post-annealing temperatures 400, 500 an...The optical reflectance and transmittance spectra in the wavelength range of 300-2500 nm are used to compute the absorption coefficient of zinc oxide films annealed at different post-annealing temperatures 400, 500 and 600°C.The values of the cross point between the curves of the real and imaginary parts of the optical conductivity ɑ_1 and ɑ_1 with energy axis of films exhibit values that correspond to optical gaps and are about 3.25-3.3 eV. The maxima of peaks in plots dR/dλ and dT/dλ versus wavelength of films exhibit optical gaps at about 3.12-3.25 eV.The values of the fundamental indirect band gap obtained from the Tauc model are at about 3.14-3.2 eV. It can be seen that films annealed at 600°C have the minimum indirect optical band gap at about 3.15 eV. The films annealed at 600°C have Urbach＇s energy minimum of 1.38 eV and hence have minimum disorder. The dispersion energy d of films annealed at 500°C has the minimum value of 43 eV.展开更多
Electrical properties of C/Ni films are studied using four mosaic targets made of pure graphite and stripes of nickel with the surface areas of 1.78,3.21,3.92 and 4.64%.The conductivity data in the temperature range o...Electrical properties of C/Ni films are studied using four mosaic targets made of pure graphite and stripes of nickel with the surface areas of 1.78,3.21,3.92 and 4.64%.The conductivity data in the temperature range of400-500 K shows the extended state conduction.The conductivity data in the temperature range of 150-300 K shows the multi-phonon hopping conduction.The Berthelot-type conduction dominates in the temperature range of 50-150 K.The conductivity of the films in the temperature range about 〈 50 K is described in terms of variable-range hopping conduction.In low temperatures,the localized density of state around Fermi level（F）for the film deposition with 3.92% nickel has a maximum value of about 56.2×10^（17）cm^（-3）eV^（-1） with the minimum average hopping distance of about 3.43 × 10^（-6） cm.展开更多
文摘The optical reflectance and transmittance spectra in the wavelength range of 300-2500 nm are used to compute the absorption coefficient of zinc oxide films annealed at different post-annealing temperatures 400, 500 and 600°C.The values of the cross point between the curves of the real and imaginary parts of the optical conductivity ɑ_1 and ɑ_1 with energy axis of films exhibit values that correspond to optical gaps and are about 3.25-3.3 eV. The maxima of peaks in plots dR/dλ and dT/dλ versus wavelength of films exhibit optical gaps at about 3.12-3.25 eV.The values of the fundamental indirect band gap obtained from the Tauc model are at about 3.14-3.2 eV. It can be seen that films annealed at 600°C have the minimum indirect optical band gap at about 3.15 eV. The films annealed at 600°C have Urbach＇s energy minimum of 1.38 eV and hence have minimum disorder. The dispersion energy d of films annealed at 500°C has the minimum value of 43 eV.
文摘Electrical properties of C/Ni films are studied using four mosaic targets made of pure graphite and stripes of nickel with the surface areas of 1.78,3.21,3.92 and 4.64%.The conductivity data in the temperature range of400-500 K shows the extended state conduction.The conductivity data in the temperature range of 150-300 K shows the multi-phonon hopping conduction.The Berthelot-type conduction dominates in the temperature range of 50-150 K.The conductivity of the films in the temperature range about 〈 50 K is described in terms of variable-range hopping conduction.In low temperatures,the localized density of state around Fermi level（F）for the film deposition with 3.92% nickel has a maximum value of about 56.2×10^（17）cm^（-3）eV^（-1） with the minimum average hopping distance of about 3.43 × 10^（-6） cm.
