Electrochemical and localized corrosion behavior of a 4045/7072/3003 M/4045 Al alloy composite in 3.5 wt.%NaCl solution was investigated from cross-sectional and plane directions by electrochemical impedance spectrosc...Electrochemical and localized corrosion behavior of a 4045/7072/3003 M/4045 Al alloy composite in 3.5 wt.%NaCl solution was investigated from cross-sectional and plane directions by electrochemical impedance spectroscopy,polarization curves,and high-resolution microscopic examination.Plane directions showed higher corrosion resistance than the cross-sectional surface,with almost all localized corrosion initiated from Si-containing inclusions.The cross-section showed a complex galvanic effect among the four layers,the galvanic coupling between 4045/7072 accelerated the dissolution of 7072 because 7072 served as the anode,however,the galvanic coupling between 3003 M/4045 protected 4045 from corrosion,indicating that 3003 M served as the anode.展开更多
Embedded aluminum-steel composite sheets used in heat exchanger were produced by cold roll bonding(CRB). The influences of annealing temperature and annealing time on the microstructure and the bonding strength of the...Embedded aluminum-steel composite sheets used in heat exchanger were produced by cold roll bonding(CRB). The influences of annealing temperature and annealing time on the microstructure and the bonding strength of the composite sheet were investigated. The recrystallization of the steel layer began at 525℃ and finished at 600℃. With the increase of the annealing temperature, the peel strength of the composite sheet whose original steel sheet surface was treated by scratch brush initially increased and then decreased, which was resulted from the competition of the mechanical locking and metallurgical bonding. After annealing, the cracks which formed between the broken work-hardened steel surface layer and its matrix during cold roll bonding remained. The composite sheet produced by CRB with the steel surface treatment of flap disc had less interfacial defects, higher bonding quality, higher diffusion rate of Al and Fe atoms at the interface and larger metallurgical bonding extent than the composite sheet produced by CRB with the steel surface treatment of scratch brush under the same conditions of annealing,which was helpful to shorten annealing time, reduce energy consumption and improve production efficiency.展开更多
基金financed by the National Key Research and Development Program(No.2022YFB3705801)the National Natural Science Foundation of China(Nos.52031007 and 52171077).
文摘Electrochemical and localized corrosion behavior of a 4045/7072/3003 M/4045 Al alloy composite in 3.5 wt.%NaCl solution was investigated from cross-sectional and plane directions by electrochemical impedance spectroscopy,polarization curves,and high-resolution microscopic examination.Plane directions showed higher corrosion resistance than the cross-sectional surface,with almost all localized corrosion initiated from Si-containing inclusions.The cross-section showed a complex galvanic effect among the four layers,the galvanic coupling between 4045/7072 accelerated the dissolution of 7072 because 7072 served as the anode,however,the galvanic coupling between 3003 M/4045 protected 4045 from corrosion,indicating that 3003 M served as the anode.
基金supported by the National High Technology Research and Development Program of China (2013AA031301)the National Natural Science Foundation of China (51104016)the Natural Science Foundation of Jiangsu Province (BK20161151)
文摘Embedded aluminum-steel composite sheets used in heat exchanger were produced by cold roll bonding(CRB). The influences of annealing temperature and annealing time on the microstructure and the bonding strength of the composite sheet were investigated. The recrystallization of the steel layer began at 525℃ and finished at 600℃. With the increase of the annealing temperature, the peel strength of the composite sheet whose original steel sheet surface was treated by scratch brush initially increased and then decreased, which was resulted from the competition of the mechanical locking and metallurgical bonding. After annealing, the cracks which formed between the broken work-hardened steel surface layer and its matrix during cold roll bonding remained. The composite sheet produced by CRB with the steel surface treatment of flap disc had less interfacial defects, higher bonding quality, higher diffusion rate of Al and Fe atoms at the interface and larger metallurgical bonding extent than the composite sheet produced by CRB with the steel surface treatment of scratch brush under the same conditions of annealing,which was helpful to shorten annealing time, reduce energy consumption and improve production efficiency.