Increasing usage of foams in various industry sectors had causing serious disposal problems once it reaches the end of its life-cycle.Herein,PVA-MFC foam was prepared by freeze-drying using polyvinyl alcohol(PVA)and m...Increasing usage of foams in various industry sectors had causing serious disposal problems once it reaches the end of its life-cycle.Herein,PVA-MFC foam was prepared by freeze-drying using polyvinyl alcohol(PVA)and microfibrillated cellulose(MFC)as a reinforced material from sugarcane bagasse(SCB).In this study,the PVA-MFC foam was chemically silylated with Y-methacryloxypropyltrimethoxysilane(MPS)and tetraethoxysilane(TEOS).The wetting ability and mechanical strength of the silylated_(2,20)PVA-MFC foam was greatly enhanced compared with unmodified_(2,20)PVA-MFC foam.The silane chemicals(MPS and TEOS)had been confirmed grafted on_(2,20)PVA-MFC foam due to the presence of Si-C and Si-O-C stretching vibration as showed in Fourier Transform Infrared(FTIR)spectra and cloud-like coating of porous pore was observed in scanning electron microscopy(SEM)images.The silylated_(2,20)PVA-MFC foam(MPS and TEOS)exhibited a series of desirable properties such as lower swelling ratio and high absorption capacity of solvents and oils but had low thermal stability in thermogravimetric(TGA)analysis.The characterization of_(2,20)PVA-MFC foam using TEOS was further investigated.A significant difference in morphology was clearly observed between the unmodified and silylated_(2,20)PVA-MFC-TEOS foam through field emission scanning electron microscopy(FESEM)images.The X-ray photoelectron(XPS)analysis of silylated_(2,20)PVA-MFC-TEOS foam confirmed the presence of C,O and trace amount of Si elements.These synthesized_(2,20)PVA-MFC foam could be a promising material for broad range of polymer foam applications.展开更多
基金support provided by the Ministry of Education of Malaysia under grant FRGS 16-044-0543 and FRGS19-091-0700.
文摘Increasing usage of foams in various industry sectors had causing serious disposal problems once it reaches the end of its life-cycle.Herein,PVA-MFC foam was prepared by freeze-drying using polyvinyl alcohol(PVA)and microfibrillated cellulose(MFC)as a reinforced material from sugarcane bagasse(SCB).In this study,the PVA-MFC foam was chemically silylated with Y-methacryloxypropyltrimethoxysilane(MPS)and tetraethoxysilane(TEOS).The wetting ability and mechanical strength of the silylated_(2,20)PVA-MFC foam was greatly enhanced compared with unmodified_(2,20)PVA-MFC foam.The silane chemicals(MPS and TEOS)had been confirmed grafted on_(2,20)PVA-MFC foam due to the presence of Si-C and Si-O-C stretching vibration as showed in Fourier Transform Infrared(FTIR)spectra and cloud-like coating of porous pore was observed in scanning electron microscopy(SEM)images.The silylated_(2,20)PVA-MFC foam(MPS and TEOS)exhibited a series of desirable properties such as lower swelling ratio and high absorption capacity of solvents and oils but had low thermal stability in thermogravimetric(TGA)analysis.The characterization of_(2,20)PVA-MFC foam using TEOS was further investigated.A significant difference in morphology was clearly observed between the unmodified and silylated_(2,20)PVA-MFC-TEOS foam through field emission scanning electron microscopy(FESEM)images.The X-ray photoelectron(XPS)analysis of silylated_(2,20)PVA-MFC-TEOS foam confirmed the presence of C,O and trace amount of Si elements.These synthesized_(2,20)PVA-MFC foam could be a promising material for broad range of polymer foam applications.
