Macro Meso Response and Stress Wave Propagation Characteristics of MCT High-Voltage Switch Under Shock load

In order to study the dynamic and electrical coupling response characteristics of Metal Oxide Semiconductor Controlled Thyristor(MCT)high-voltage switch under the synergic action of mechanical load and high voltage,the separated Hopkinson pressure bar(SHPB)test system was used to simulate different impact load environments,and combined with the multi-layer high-voltage ceramic capacitor charging and discharging system,the instantaneous electrical signals of MCT high-voltage switch were collected.Combined with numerical simulation and theoretical analysis,the failure mode and stress wave propagation characteristics of MCT high voltage switch were determined.The mechanical and electrical coupling response characteristics and failure mechanism of MCT high voltage switch under dynamic load were revealed from macroscopic and microscopic levels.The results show that the damage modes of MCT high-voltage switches can be divided into non-functional damage,recoverable functional damage,non-recoverable damage and structural damage.Due to the gap between the metal gate and the oxide layer,the insulating oxide layer was charged.After placing for a period of time,the elastic deformation of the metal gate partially recovered and the accumulated charge disappeared,which induced the recoverable functional damage failure of the device.In addition,obvious cracks appeared on both sides of the monocrystalline silicon inside the MCT high-voltage switch,leading to unrecoverable damage of the device.

Effect of the interval between two shocks on ejecta formation from the grooved aluminum surface

This work focuses on the effect of the interval between two shocks on the ejecta formation from the grooved aluminum(Al_(1100))surface by using smoothed particle hydrodynamics numerical simulation.Two unsupported shocks are obtained by the plate-impact between sample and two flyers at interval,with a peak pressure of approximately 30 GPa for each shock.When the shock interval varies from 2.11 to 7.67 times the groove depth,the bubble velocity reduces to a constant,and the micro jetting factor R_(J) from spike to bubble exhibits a non-monotonic change that decreases initially and then increases.At a shock interval of 3.6 times the groove depth,micro jetting factor R_(J) from spike to bubble reaches its minimum value of approximately 0.6.While,the micro jetting factor R_(F) from spike to free surface decreases linearly at first,and stabilizes around 0.25 once the shock interval surpasses 4.18 times the groove depth.When the shock interval is less than 4.18 times the groove depth,the unloading wave generated by the breakout of the first shock wave is superimpose with the unloading part of the second shock wave to form a large tensile area.

Bioinspired fish-scale-like magnesium composites strengthened by contextures of continuous titanium fibers:Lessons from nature

Natural fish scales demonstrate outstanding mechanical efficiency owing to their elaborate architectures and thereby may serve as ideal prototypes for the architectural design of man-made materials.Here bioinspired magnesium composites with fish-scale-like orthogonal plywood and double-Bouligand architectures were developed by pressureless infiltration of a magnesium melt into the woven contextures of continuous titanium fibers.The composites exhibit enhanced strength and work-hardening ability compared to those estimated from a simple mixture of their constituents at ambient to elevated temperatures.In particular,the double-Bouligand architecture can effectively deflect cracking paths,alleviate strain localization,and adaptively reorient titanium fibers within the magnesium matrix during the deformation of the composite,representing a successful implementation of the property-optimizing mechanisms in fish scales.The strength of the composites,specifically the effect of their bioinspired architectures,was interpreted based on the adaptation of classical laminate theory.This study may offer a feasible approach for developing new bioinspired metal-matrix composites with improved performance and provide theoretical guidance for their architectural designs.