以硅橡胶为基体,添加无机填料制备的耐热涂层在耐热防腐方面有重要应用前景。采用自制改性硅橡胶作基体,添加不同配比的高岭土、二氧化硅和氧化铝,制备了复合涂层。采用扫描电子显微镜(scanning electron microscopy,SEM)观察了硅橡胶...以硅橡胶为基体,添加无机填料制备的耐热涂层在耐热防腐方面有重要应用前景。采用自制改性硅橡胶作基体,添加不同配比的高岭土、二氧化硅和氧化铝,制备了复合涂层。采用扫描电子显微镜(scanning electron microscopy,SEM)观察了硅橡胶基体中无机填料的分散状况,采用热重分析仪(thermogravimetric analyzer,TGA)对复合涂层的热解温度和失重率进行了分析。结果表明:在复合体系中,无机填料与基体的相容性较好,分散均匀;与基体材料相比,无机填料的添加可有效提高复合材料的耐热性。填料质量分数为20%的复合涂层,其在800℃时质量残留率比自制改性硅橡胶的基体提高了10%以上。展开更多
The critical points and time-temperature-transformation(TTT)curves of the isothermal transformation diagrams for a high-speed steel casting on a horizontal centrifugal casting machine had been determined experimentall...The critical points and time-temperature-transformation(TTT)curves of the isothermal transformation diagrams for a high-speed steel casting on a horizontal centrifugal casting machine had been determined experimentally in the study.The effects of quenching temperature on the microstructures and properties of centrifugal casting high speed steel(HSS)roll has been investigated using scanning electron microscopy(SEM), light optical microscopy(LOM)and X-ray diffraction(XRD)as well as using tensile,impact,and hardness tests. The results show that the HSS roll has excellent hardenability and its matrix structure can be transformed into the martensite after being quenched in the sodium silicate solution.The retained austenite in the quenching structure increases and the hardness decreases when the quenching temperature exceeds 1,040℃.The tensile strength and impact toughness of HSS roll increase once the quenching temperature is raised from 980℃to 1,040℃. However,the tensile strength and impact toughness have no significant change when the quenching temperature exceeds 1,040℃.The HSS roll quenched at 1,040℃exhibits excellent comprehensive mechanical properties.展开更多
The as-cast microstructures of high carbon high speed steels （HC-HSS） made by sand casting, centrifugal casting and electromagnetic centrifugal casting, respectively, were studied by using of optical microscopy （OM...The as-cast microstructures of high carbon high speed steels （HC-HSS） made by sand casting, centrifugal casting and electromagnetic centrifugal casting, respectively, were studied by using of optical microscopy （OM） and D/max2200pc X-ray diffraction. The results show that the microstructure of as-cast HC- HSS is dominated by alloy carbides （W2C, VC, Cr7C3）, martensite and austenite. The centrifugal casting and electromagnetic centrifugal casting apparently improve the solidification structure of HCoHSS. With the increase of magnetic intensity （B）, the volume fraction of austenite in the HC-HSS solidification structure increases significantly while the eutectic ledeburite decreases. Moreover, the secondary carbides precipitated from the austenite are finer with more homogeneous distribution in the electromagnetic centrifugal castings. It has also been found that the lath of eutectic carbide in ledeburite becomes finer and carbide phase spacing in eutectic ledeburite increases along with the higher magnetic field strength.展开更多
文摘以硅橡胶为基体,添加无机填料制备的耐热涂层在耐热防腐方面有重要应用前景。采用自制改性硅橡胶作基体,添加不同配比的高岭土、二氧化硅和氧化铝,制备了复合涂层。采用扫描电子显微镜(scanning electron microscopy,SEM)观察了硅橡胶基体中无机填料的分散状况,采用热重分析仪(thermogravimetric analyzer,TGA)对复合涂层的热解温度和失重率进行了分析。结果表明:在复合体系中,无机填料与基体的相容性较好,分散均匀;与基体材料相比,无机填料的添加可有效提高复合材料的耐热性。填料质量分数为20%的复合涂层,其在800℃时质量残留率比自制改性硅橡胶的基体提高了10%以上。
基金supported by the innovation fund of small and medium-sized enterprise of Science&Technology Ministry of China under grant(07C26215110842).
文摘The critical points and time-temperature-transformation(TTT)curves of the isothermal transformation diagrams for a high-speed steel casting on a horizontal centrifugal casting machine had been determined experimentally in the study.The effects of quenching temperature on the microstructures and properties of centrifugal casting high speed steel(HSS)roll has been investigated using scanning electron microscopy(SEM), light optical microscopy(LOM)and X-ray diffraction(XRD)as well as using tensile,impact,and hardness tests. The results show that the HSS roll has excellent hardenability and its matrix structure can be transformed into the martensite after being quenched in the sodium silicate solution.The retained austenite in the quenching structure increases and the hardness decreases when the quenching temperature exceeds 1,040℃.The tensile strength and impact toughness of HSS roll increase once the quenching temperature is raised from 980℃to 1,040℃. However,the tensile strength and impact toughness have no significant change when the quenching temperature exceeds 1,040℃.The HSS roll quenched at 1,040℃exhibits excellent comprehensive mechanical properties.
基金supported by the special fund for basic scientifi c research of central colleges,Chang’an University (CHD2010JC015)the innovation fund of small and medium-sized enterprise of Science & Technology Ministry of China under grant no. 10C26213201139Beijing Education Committee patent outcome conversion item
文摘The as-cast microstructures of high carbon high speed steels （HC-HSS） made by sand casting, centrifugal casting and electromagnetic centrifugal casting, respectively, were studied by using of optical microscopy （OM） and D/max2200pc X-ray diffraction. The results show that the microstructure of as-cast HC- HSS is dominated by alloy carbides （W2C, VC, Cr7C3）, martensite and austenite. The centrifugal casting and electromagnetic centrifugal casting apparently improve the solidification structure of HCoHSS. With the increase of magnetic intensity （B）, the volume fraction of austenite in the HC-HSS solidification structure increases significantly while the eutectic ledeburite decreases. Moreover, the secondary carbides precipitated from the austenite are finer with more homogeneous distribution in the electromagnetic centrifugal castings. It has also been found that the lath of eutectic carbide in ledeburite becomes finer and carbide phase spacing in eutectic ledeburite increases along with the higher magnetic field strength.