Assisted Compatibility, and Balanced Regulation of the Mechanical, Thermal, and Antioxidant Activity of Polyvinyl Alcohol-Chinese Bayberry Tannin Extract Films Using Different Di-Aldehydes as Cross-Linkers

Polyvinyl alcohol(PVA)-based films containing Chinese bayberry tannin(BT)were prepared by cross-linking using glyoxal,glutaraldehyde and dialdehyde starch,individually.The presence of cross-linkers was evident to promote the transparency and decrease the moisture content of PVA/BT films,while the water solubility stayed almost unchanged in the cross-linked PVA/BTfilms.All cross-linkers provided promotion of the water vapor per-meability,mechanical property and thermal stability of PVA/BT films.The best water vapor barrier capacity was found in case of glutaraldehyde cross-linked PVA/BT film,while the highest tensile strength was encountered in case of glyoxal cross-linked PVA/BT films,compared with the uncross-linked films.The scavenging action of the films towards DPPH radical activity was influenced by the nature of each cross-linker.Namely,the PVA/AT film cross-linked by glutaraldehyde acquired the lowest radical scavenging activity in a certain time,suggesting that glutaraldehyde decreased the release rate of BT from PVA.Based on the experimental data,glutaraldehyde and dialdehyde starch could be more suitable for PVA/BT film preparation since they can promote the intermo-lecular interaction of PVA and BT to a reasonable extent.

Preparation and Characterization of Sandwich Structured Materials with Interesting Insulation and Fire Resistance

A cellular material in the form of 3-layered sandwich structure material was prepared via sole use of mechanical stirring without any use of a foaming agent,while Tween-80 was employed as a foam stabilizer via a developed in-situ mold casting.The resulting structure displayed a good appearance with no visual defects.The 3-layered composition of the sandwish structure,“nonporous resin layer-porous foam layer-nonporous resin layer”,was examined in terms of the microstructure,density&density distribution,pulverization ratio,mechanical strength,insulation and flame retardant performance.It was indicated from the results that the bonding between the resin layer and foam layer was tight,while the tensile rupture always occurred in the porous layer.Also,the density of the sandwich structure material was symmetrical with“saddle”distribution,and a uniform density for any given layer.The increase in the density at the interface layer provided a good interpretation for the tensile rupture never occurred at the interface.The brittleness resistance of the developed material was significantly improved,and the pulverization ratio was sharply decreased from 9.93%to 0.31%.The material acquired a thermal conductivity and limiting oxygen index(LOI)of 0.0241 W/m⋅K and 29.92%,respectively,indicating potential use of such materials broadly in fields of insulation and flame retardancy.