The effect of diboron trioxide(B_2O_3) on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets was investigated in this work. The main characterization methods were X-ray ...The effect of diboron trioxide(B_2O_3) on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets was investigated in this work. The main characterization methods were X-ray fluorescence, inductively coupled plasma–atomic emission spectroscopy, mercury injection porosimetry, X-ray diffraction, metallographic microscopy, and scanning electron microscopy–energy-dispersive X-ray spectroscopy. The results showed that the crushing strength increased greatly with increasing B_2O_3 content and that the increase in crushing strength was strongly correlated with a decrease in porosity, the formation of liquid phases, and the growth and recrystallization consolidation of hematite crystalline grains. The smelting properties were measured under simulated blast furnace conditions; the results showed that the smelting properties within a certain B_2O_3 content range were improved and optimized except in the softening stage. The valuable element B was easily transformed to the slag, and this phenomenon became increasingly evident with increasing B_2O_3 content. The formation of Ti(C,N) was mostly avoided, and the slag and melted iron were separated well during smelting with the addition of B_2O_3. The size increase of the melted iron was consistent with the gradual optimization of the dripping characteristics with increasing B_2O_3 content.展开更多
The effect of nickel oxide additive on the smelting behaviors of chromium-bearing vanadium titanomagnetite pellets(CVTP)was investigated while analyzing the transfer behavior of nickel in iron and slag.The results sho...The effect of nickel oxide additive on the smelting behaviors of chromium-bearing vanadium titanomagnetite pellets(CVTP)was investigated while analyzing the transfer behavior of nickel in iron and slag.The results show that when NiO added to CVTP increases from 0 to 6 wt.%,softening start temperature increases from 1148 to 1212℃,and the softening end temperature increases from 1280 to 1334℃;the melting start temperature increases from 1318 to 1377℃,and the dripping temperature decreases from 1558 to 1521℃.The pig iron comprises a compound of Fe-Ni-C.The slag structure depolymerizes with increasing nickel addition.The softening-melting behaviors of CVTP,the reduction of nickel into pig iron,and the depolymerization of slag structure indicate the feasibility of producing nickel-iron alloy through the blast furnace process.展开更多
In order to clarify the oxidation mechanisms and make better use of the low-grade vanadiferous titanomagnetite concentrate with high titanium(LVTC),the oxidation behavior of LVTC was investigated.The results showed th...In order to clarify the oxidation mechanisms and make better use of the low-grade vanadiferous titanomagnetite concentrate with high titanium(LVTC),the oxidation behavior of LVTC was investigated.The results showed that oxidation degree was achieved within 90 min when temperature was not lower than 700°C,and the main phases of the oxidized LVTC consisted of Fe9TiO15,Fe2O3,CaSiTiO5 and a small amount of Fe2.75Ti0.25O4.Increasing temperature is favorable to the formation of Fe2TiO5.The surface of LVTC gradually becomes rough,with fine particles of needle-like and granular shape appearing on the surface,which finally turn from laminar to creamy,spread out,and are interspersed with many tiny holes.The phase oxidation paths in LVTC were as follows:(1)Fe2.75Ti0.25O4→Fe9TiO15+Fe2O3;(2)Fe2.75Ti0.25O4→Fe2O3+FeTiO3→Fe2TiO5;(3)FeTiO3→Fe2O3+Fe2Ti3O9→Fe2TiO5.LVTC is predominantly mesoporous whether oxidized or not,with the pores mainly distributed in the range of 2–40 nm,and the specific surface area of LVTC decreases significantly with increasing temperature.展开更多
基金financially supported by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China (No. 2015BAB19B02)the National Program on Key Basic Research Project of China (No. 2013CB632603)
文摘The effect of diboron trioxide(B_2O_3) on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets was investigated in this work. The main characterization methods were X-ray fluorescence, inductively coupled plasma–atomic emission spectroscopy, mercury injection porosimetry, X-ray diffraction, metallographic microscopy, and scanning electron microscopy–energy-dispersive X-ray spectroscopy. The results showed that the crushing strength increased greatly with increasing B_2O_3 content and that the increase in crushing strength was strongly correlated with a decrease in porosity, the formation of liquid phases, and the growth and recrystallization consolidation of hematite crystalline grains. The smelting properties were measured under simulated blast furnace conditions; the results showed that the smelting properties within a certain B_2O_3 content range were improved and optimized except in the softening stage. The valuable element B was easily transformed to the slag, and this phenomenon became increasingly evident with increasing B_2O_3 content. The formation of Ti(C,N) was mostly avoided, and the slag and melted iron were separated well during smelting with the addition of B_2O_3. The size increase of the melted iron was consistent with the gradual optimization of the dripping characteristics with increasing B_2O_3 content.
基金financial supports from the National Natural Science Foundation of China(Nos.21908020,U1908226)。
文摘The effect of nickel oxide additive on the smelting behaviors of chromium-bearing vanadium titanomagnetite pellets(CVTP)was investigated while analyzing the transfer behavior of nickel in iron and slag.The results show that when NiO added to CVTP increases from 0 to 6 wt.%,softening start temperature increases from 1148 to 1212℃,and the softening end temperature increases from 1280 to 1334℃;the melting start temperature increases from 1318 to 1377℃,and the dripping temperature decreases from 1558 to 1521℃.The pig iron comprises a compound of Fe-Ni-C.The slag structure depolymerizes with increasing nickel addition.The softening-melting behaviors of CVTP,the reduction of nickel into pig iron,and the depolymerization of slag structure indicate the feasibility of producing nickel-iron alloy through the blast furnace process.
基金supported by the National Natural Science Foundation of China(Grant Nos.51674084,21908020 and U1908226)the National Key R&D Program of China(No.2017YFB0603801).
文摘In order to clarify the oxidation mechanisms and make better use of the low-grade vanadiferous titanomagnetite concentrate with high titanium(LVTC),the oxidation behavior of LVTC was investigated.The results showed that oxidation degree was achieved within 90 min when temperature was not lower than 700°C,and the main phases of the oxidized LVTC consisted of Fe9TiO15,Fe2O3,CaSiTiO5 and a small amount of Fe2.75Ti0.25O4.Increasing temperature is favorable to the formation of Fe2TiO5.The surface of LVTC gradually becomes rough,with fine particles of needle-like and granular shape appearing on the surface,which finally turn from laminar to creamy,spread out,and are interspersed with many tiny holes.The phase oxidation paths in LVTC were as follows:(1)Fe2.75Ti0.25O4→Fe9TiO15+Fe2O3;(2)Fe2.75Ti0.25O4→Fe2O3+FeTiO3→Fe2TiO5;(3)FeTiO3→Fe2O3+Fe2Ti3O9→Fe2TiO5.LVTC is predominantly mesoporous whether oxidized or not,with the pores mainly distributed in the range of 2–40 nm,and the specific surface area of LVTC decreases significantly with increasing temperature.