High-strength and thermally stable TiB_(2)-modified Al-Mn-Mg-Er-Zr alloy fabricated via selective laser melting

To increase the processability and plasticity of the selective laser melting(SLM)fabricated Al-Mn-Mg-Er-Zr alloys,a novel TiB_(2)-modified Al-Mn-Mg-Er-Zr alloy with a mixture of Al-Mn-Mg-Er-Zr and nano-TiB_(2) powders was fabricated by SLM.The pro-cessability,microstructure,and mechanical properties of the alloy were systematically investigated by density measurement,microstruc-ture characterization,and mechanical properties testing.The alloys fabricated at 250 W displayed higher relative densities due to a uni-formly smooth top surface and appropriate laser energy input.The maximum relative density value of the alloy reached(99.7±0.1)%,demonstrating good processability.The alloy exhibited a duplex grain microstructure consisting of columnar regions primarily and equiaxed regions with TiB_(2),Al6Mn,and Al3Er phases distributed along the grain boundaries.After directly aging treatment at a high tem-perature of 400℃,the strength of the SLM-fabricated TiB_(2)/Al-Mn-Mg-Er-Zr alloy increased due to the precipitation of the secondary Al6Mn phases.The maximum yield strength and ultimate tensile strength of the aging alloy were measured to be(374±1)and(512±13)MPa,respectively.The SLM-fabricated TiB_(2)/Al-Mn-Mg-Er-Zr alloy demonstrates exceptional strength and thermal stability due to the synergistic effects of the inhibition of grain growth,the incorporation of TiB_(2) nanoparticles,and the precipitation of secondary Al6Mn nanoparticles.

Fabrication and Excellent Properties of Polyvinylidene fluoride/Graphene Composite Films as Thermal Interface Materials

The growing concern about thermal conductivityand electromagnetic shielding inelectronic equipment has promoted the development of interfacial film materials.In this work,polyvinylidene fluoride(PVDF)/graphene composite films with different graphene contents were fabricated by high-energy ball milling,cold isostatic pressing,scraping and coating,successively.High-energy ball milling is beneficial to the dispersion of graphene powder,while cold isostatic pressing can greatly enhance thermal conductivity and mechanical strength by reducing the voids in the film and increasing the contact area of graphene sheets.The thermal conductivity,tensile strength and electromagnetic shielding properties of the films were carefully investigated and compared.It was demonstrated that the thermal conductivity increased from 0.19 Wm-1.K-1 for pure PVDF to 103.9 W-m-1.K-1 for the composite film with PVDF:graphene=1:3.Meanwhile the electromagnetic shielding efficiency can reach 36.55 dB.The prepared PVDF/graphene composite films exhibit outstanding overall performance and have the potential for practical applications.

Influence of process parameters and aging treatment on the microstructure and mechanical properties of Al Si8Mg3 alloy fabricated by selective laser melting

Many studies have investigated the selective laser melting(SLM)of AlSi10Mg and AlSi7Mg alloys,but there are still lack of researches focused on Al-Si-Mg alloys specifically tailored for SLM.In this work,a novel high Mg-content AlSi8Mg3 alloy was specifically designed for SLM.The results showed that this new alloy exhibited excellent SLM processability with a lowest porosity of 0.07%.Massive lattice distortion led to a high Vickers hardness in samples fabricated at a high laser power due to the precipitation of Mg_(2)Si nanoparticles from theα-Al matrix induced by high-intensity intrinsic heat treatment during SLM.The maximum microhardness and compressive yield strength of the alloy reached HV(211±4)and(526±12)MPa,respectively.After aging treatment at 150℃,the maximum microhardness and compressive yield strength of the samples were further improved to HV(221±4)and(577±5)MPa,respectively.These values are higher than those of most known aluminum alloys fabricated by SLM.This paper provides a new idea for optimizing the mechanical properties of Al-Si-Mg alloys fabricated using SLM.

Insights into the oxidation resistance mechanism and tribological behaviors of multilayered TiSiN/CrVxN hard coatings

In the last decades,vanadium alloyed coatings have been introduced as potential candidates for self-lubrication due to their perfect tribological properties.In this work,the influence of V incorporation on the wear performance and oxidation resistance of TiSiN/CrN film coatings deposited by direct current(DC)reactive magnetron sputtering is investigated.The results show that vanadium incorporation significantly decreases the oxidation resistance of the coatings.In general,two layers are formed during the oxidation process:i)Ti(V)O_(2) on top,followed by a protective layer,which is subdivided into two layers,Cr_(2)O_(3) and Si-O.ii)The diffusion of V controls the oxidation of V-containing coatings.The addition of vanadium improves the wear resistance of coatings,and the wear rate decreases with increasing V content in the coatings;however,the friction coefficient is independent of the chemical composition of the coatings.The wear of the V-containing coatings is driven by polishing wear.

Tribological performance under different environments of Ti-C-N composite films for marine wear-resistant parts

The need for reducing the wear in mechanical parts used in the industry makes self-lubricant films one of the sustainable solutions to achieve long-term protection under different environmental conditions.The purpose of this work is to study the influence of C additions on the tribological behavior of a magnetron-sputtered TiN film in air,water,and seawater.The results show that the addition of C into the TiN binary film induced a new amorphous phase,and the films exhibited a dual phase of fcc(face-centered cubic)-TiN and amorphous carbon.The antifriction and wear-resistance properties were enhanced in air and water by adding 19.1at%C.However,a further increase in the C concentration improved anti-frictional properties but also led to higher wear rates.Although the amorphous phase induced microbatteries and accelerated the corrosion of TiN phases in seawater,the negative abrasion state was detected for all Ti-C-N films due to the adhesion of the tribocorrosion debris on the wear track.

Erratum to:Influence of process parameters and aging treatment on the microstructure and mechanical properties of AlSi8Mg3 alloy fabricated by selective laser melting

Erratum to:International Journal of Minerals, Metallurgy and MaterialsVolume 29, Number 9, September 2022, Page 1770https://doi.org/10.1007/s12613-021-2287-1The original version of this article unfortunately contained a mistake due to the PDF file conversion through different softwares. The presentation of Fig. 13 in original version was incorrect.

Nano-multilayered ZrN‒Ag/Mo‒S‒N film design for stable anti-frictional performance at a wide range of temperatures

A multilayer film,composed by ZrN‒Ag(20 nm)and Mo‒S‒N(10 nm)layers,combining the intrinsic lubricant characteristics of each layer was deposited using DC magnetron sputtering system,to promote lubrication in a wide-range of temperatures.The results showed that the ZrN‒Ag/Mo‒S‒N multilayer film exhibited a sharp interface between the different layers.A face-centered cubic(fcc)dual-phases of ZrN and Ag co-existed in the ZrN‒Ag layers,whilst the Mo‒S‒N layers displayed a mixture of hexagonal close-packed MoS_(2)(hcp-MoS_(2))nano-particles and an amorphous phase.The multilayer film exhibited excellent room temperature(RT)triblogical behavior,as compared to the individual monolayer film,due to the combination of a relative high hardness with the low friction properties of both layers.The reorientation of MoS_(2)parallel to the sliding direction also contributed to the enhanced anti-frictional performance at RT.At 400℃,the reorientation of MoS_(2)as well as the formation of MoO_(3)phase were responsible for the lubrication,whilst the hard t-ZrO_(2)phase promoted abrasion and,consequently,led to increasing wear rate.At 600℃,the Ag_(2)MoO_(4)double-metal oxide was the responsible for the low friction and wear-resistance;furthermore,the observed transformation from t-ZrO_(2)to m-ZrO_(2),could also have contributed to the better tribological performance.