Oxidizing roasting of molybdenite with lime can significantly reduce SO2pollution compared with the traditional roastingwithout lime.However,the calcine is subsequently leached by sulfuric acid,resulting in serious eq...Oxidizing roasting of molybdenite with lime can significantly reduce SO2pollution compared with the traditional roastingwithout lime.However,the calcine is subsequently leached by sulfuric acid,resulting in serious equipment corrosion and abundantnon-recyclable CaSO4slag.In this work,a novel process,in which the molybdenite was roasted with CaCO3followed by(NH4)2CO3solution leaching,was proposed to improve the art of lime roasting-sulfuric acid leaching.Oxidizing roasting of molybdenite withCaCO3was investigated through thermodynamic calculation,thermogravimetric analysis and roasting experiments.The results showthat the products of the oxidizing reaction of MoS2in the presence of CaCO3and O2are CaSO4,CaMoO4and CO2at573-1000K.The MoS2conversion rate achieves approximately99%and the sulfur-retained rate attains approximately95%with aCaCO3-to-MoS2molar ratio of3.6at500°C for1h by adding5%mineralizer A(mass fraction).The leaching results show that theleaching rate of Mo reaches98.2%at85°C for7h with a(NH4)2CO3concentration of600g/L and a liquid-solid ratio of10mL/g.The results presented are potential to develop a novel cleaner technique for ammonium molybdate production.展开更多
基金Project(51274243)supported by the National Natural Science Foundation of ChinaProject(2015CX001)supported by the Innovation-driven Plan in Central South University,China
文摘Oxidizing roasting of molybdenite with lime can significantly reduce SO2pollution compared with the traditional roastingwithout lime.However,the calcine is subsequently leached by sulfuric acid,resulting in serious equipment corrosion and abundantnon-recyclable CaSO4slag.In this work,a novel process,in which the molybdenite was roasted with CaCO3followed by(NH4)2CO3solution leaching,was proposed to improve the art of lime roasting-sulfuric acid leaching.Oxidizing roasting of molybdenite withCaCO3was investigated through thermodynamic calculation,thermogravimetric analysis and roasting experiments.The results showthat the products of the oxidizing reaction of MoS2in the presence of CaCO3and O2are CaSO4,CaMoO4and CO2at573-1000K.The MoS2conversion rate achieves approximately99%and the sulfur-retained rate attains approximately95%with aCaCO3-to-MoS2molar ratio of3.6at500°C for1h by adding5%mineralizer A(mass fraction).The leaching results show that theleaching rate of Mo reaches98.2%at85°C for7h with a(NH4)2CO3concentration of600g/L and a liquid-solid ratio of10mL/g.The results presented are potential to develop a novel cleaner technique for ammonium molybdate production.