Polymer bonded explosive(PBX)formulations were successfully prepared in the laboratory scale containing 1,1-diamino-2,2-dinitroethene(FOX-7)and hexogen(RDX)as brisant high explosives and different binder types of poly...Polymer bonded explosive(PBX)formulations were successfully prepared in the laboratory scale containing 1,1-diamino-2,2-dinitroethene(FOX-7)and hexogen(RDX)as brisant high explosives and different binder types of polyurethane(PU)based on glycidyl azide polymer(GAP) and hydroxyl-terminated polybutadiene(HTPB) as an energetic and inert polymeric binder respectively.Casting technique was used for the preparation of different PBX formulations based on FOX-7/RDX and PU(GAP/HTPB)with 14% binder.The sensitivity to different initial impulses and performance characteristics of the explosive and lethal zone of the tested controlled fragmentation warhead by the fragmentation warhead assessment test(arena test)were studied,in which the arena test was carried out with a controlled fragmentation warhead made from Ck45 steel,with dimensions(100 mm length,30 mm outer diameter and 3 mm thickness).Results show that PBXGF4 has lower sensitivity to impact and heat than those of PBXGR4 by 188.4% and 3.2% respectively.Its friction sensitivity is the same as that of PBXGR4.It has better performance,in which detonation velocity increases by 2.1% and brisance increases by 0.5% when compared with those of PBXGR4.It was concluded that PBXGF4 which based on FOX-7 bonded with PU/GAP matrix has good characteristics as PBX,specially in the sensitivity to impact and can be applied for replacing PBXs based on RDX in the advanced PBXs for low sensitive fragmentation warheads.展开更多
The effects of plasticizers,antioxidants and burning rate modifiers on the aging performance of the composite solid propellant based on hydroxyl-terminated polybutadiene(HTPB)/hexamethylene diisocyanate(HMDI)were expl...The effects of plasticizers,antioxidants and burning rate modifiers on the aging performance of the composite solid propellant based on hydroxyl-terminated polybutadiene(HTPB)/hexamethylene diisocyanate(HMDI)were explored by apply-ing an accelerated aging program for 90 day at 70 ℃. The HTPB propellant matrix with the diisooctyl sebacate(DOS)as plasti-cizers and diisooctyl azelate(DOZ), antioxidants as N,N ′-Diphenyl-p-phenylenediamine(AO) and 2,2′-methylenebis(4-methyl-6-tert-butylphenol)(cyanox 2246)and burning rate modifiers as barium ferrite(BF),copper chromites(CC)and fer-ric oxide(FO)were varied. Results show that sample(S1)which based on DOS decreases the stress value and increases the strain value which considered to be an excellent start for aging program. Sample(S3)containing AO presents the higher resis-tance to oxidation showing the better performance that reflects on increasing the shelf life of the composite solid propellant mo-tor. Sample(S5)which based on BF enhances the ballistic performance among over the other tested two samples. The accelerat-ed aging program allowed us to estimate the motor in-service lifetime.展开更多
文摘Polymer bonded explosive(PBX)formulations were successfully prepared in the laboratory scale containing 1,1-diamino-2,2-dinitroethene(FOX-7)and hexogen(RDX)as brisant high explosives and different binder types of polyurethane(PU)based on glycidyl azide polymer(GAP) and hydroxyl-terminated polybutadiene(HTPB) as an energetic and inert polymeric binder respectively.Casting technique was used for the preparation of different PBX formulations based on FOX-7/RDX and PU(GAP/HTPB)with 14% binder.The sensitivity to different initial impulses and performance characteristics of the explosive and lethal zone of the tested controlled fragmentation warhead by the fragmentation warhead assessment test(arena test)were studied,in which the arena test was carried out with a controlled fragmentation warhead made from Ck45 steel,with dimensions(100 mm length,30 mm outer diameter and 3 mm thickness).Results show that PBXGF4 has lower sensitivity to impact and heat than those of PBXGR4 by 188.4% and 3.2% respectively.Its friction sensitivity is the same as that of PBXGR4.It has better performance,in which detonation velocity increases by 2.1% and brisance increases by 0.5% when compared with those of PBXGR4.It was concluded that PBXGF4 which based on FOX-7 bonded with PU/GAP matrix has good characteristics as PBX,specially in the sensitivity to impact and can be applied for replacing PBXs based on RDX in the advanced PBXs for low sensitive fragmentation warheads.
文摘The effects of plasticizers,antioxidants and burning rate modifiers on the aging performance of the composite solid propellant based on hydroxyl-terminated polybutadiene(HTPB)/hexamethylene diisocyanate(HMDI)were explored by apply-ing an accelerated aging program for 90 day at 70 ℃. The HTPB propellant matrix with the diisooctyl sebacate(DOS)as plasti-cizers and diisooctyl azelate(DOZ), antioxidants as N,N ′-Diphenyl-p-phenylenediamine(AO) and 2,2′-methylenebis(4-methyl-6-tert-butylphenol)(cyanox 2246)and burning rate modifiers as barium ferrite(BF),copper chromites(CC)and fer-ric oxide(FO)were varied. Results show that sample(S1)which based on DOS decreases the stress value and increases the strain value which considered to be an excellent start for aging program. Sample(S3)containing AO presents the higher resis-tance to oxidation showing the better performance that reflects on increasing the shelf life of the composite solid propellant mo-tor. Sample(S5)which based on BF enhances the ballistic performance among over the other tested two samples. The accelerat-ed aging program allowed us to estimate the motor in-service lifetime.