MORPHOLOGY EVOLUTION IN PTFE AS A FUNCTION OF MELT TIME AND TEMPERATURE——Ⅰ.HIGH MOLECULAR WEIGHT SINGLE-AND MULTI-MOLECULE FOLDED CHAIN SINGLE CRYSTALS AND BAND STRUCTURES

The effect of sintering dispersed dispersion and nano-emulsion particles of high molecular weightpolytetrafluoroethylene(PTFE)on a substrate as a function of“melt”time and temperature is described.Folded chain singlecrystals parallel to the substrate and as ribbons on-edge(with double striations),as well as bands,are produced for longersintering times;particle merger and diffusion of individual molecules,crystallizing as folded chain,single(or few)molecule,single crystals when“trapped”on the substrate by cooling occur for shorter sintering times.It is suggested the observedstructures develop with sintering time,in a mesomorphic melt.The structure of the nascent particles is also discussed.

CRYSTAL STRUCTURE AND MORPHOLOGY OF NASCENT SAMPLES OF SYMMETRIC AROMATIC POLYESTERS——Ⅰ.POLY(P-PHENYLENE TEREPHTHALATE)

The morphology and crytal structure of poly(p-phenylene terephthalate) (PPT), prepared by confined thin filmmelt (CTFMP) and solution (CTFSP) and bulk solution polymerization, were characterized by transmission electronmicroscopy, electron dimaction and molecular modeling. The unit cell is monoclinic (P2_1/a space group) with parameters a =7.89, b = 5.49, c = 12.65 A, α=γ= 90°, β=100.33°, density = 1.48 g/cm^3, the a, b and β values differing slightly from thosereported previously in the literature. A degree of variation in relative intensities of hk0 reflections in, apparently, untilted[001] ED patterns was observed from a given sample, suggesting some variation in molecular packing. ED evidence wasfound for a second phase, with [001] appearing the same as for phase Ⅱ of the related poly(p-oxybenzoate) (PpOBA)polymer. CTFMP crystals polymerized above 220℃ (up to 370℃) and CTFSP crystals polymerized at 300℃ consisted oflamellae 100-200 A thick.

CRYSTAL STRUCTURE AND MORPHOLOGY OF NASCENT SAMPLES OF SYMMETRIC AROMATIC POLYESTERS——Ⅱ. POLY(p-PHENYLENE 2,6-NAPHTHALATE)

Confined thin film melt polymerization (CTFMP) of naphthalene chloride/hydroquinone (NCMQ, 1/1, molar)mixtures at polymerization temperatures (T_p) below ca. 300℃ resulted in relatively thick, elongated crystals. Polymerizationof NC/HQ above 300℃ between glass yielded well-formed lamellar crystals ca. 100 A thick. Phase Ⅰ and Ⅱ [001] EDpatterns were obtained for all T_p, the relative amount of phase Ⅰ increasing with T_p. Polymerization of naphthalenedicarboxylic acid/hydroquinione diacetate 1/1 mixtures at high T_p also yielded lamellar crystals that "curled up" off of thesubstrate. When the high temperature CTFMP polymerization was conducted between mica, aggregates of lamellae on-edgedeveloped but epitaxial growth did not occur. Epitaxial growth of lamellae between mica could be obtained, however, byconfined thin film solution polymerization, with both of the latter samples yielding apparently related ED patterns from adifferent unit cell than phase Ⅰ or Ⅱ. Fiber patterns, obtained from sheared samples, indicated considerably greater crystaldisorder than in the nascent crystals. Refinement of the phase Ⅰ unit cell parameters, based on the [001] and [01 1] EDpatterns, with modeling based on Cerius^2, suggests a monoclinic phase Ⅰ unit cell with a = 7.76, b = 5.71, c = 14.99 A, α = γ= 90°, β= 99.7°, ρ = 1.47 g/cm^3, space group P12_1/al.