The influence of the precipitating reagents and dispersants on the formation of nano-aluminum hydroxide from sodium aluminate solution by chemical precipitation was investigated. The influence of the dispersed seeds o...The influence of the precipitating reagents and dispersants on the formation of nano-aluminum hydroxide from sodium aluminate solution by chemical precipitation was investigated. The influence of the dispersed seeds on the decomposi-tion process was investigated too. The alkaline aluminate solutions were used as original solutions with a concentration of Al2O3 having 14.78 g/dm3, αk—1.6 and127 g/dm3, αk—1.6. For the precipitation processes there were used follow-ing precipitating reagents—solutions HCl, NaHCO3 and NH4HCO3 with a concentration of 80 g/dm3, dispersants—PEG 6000, (NaPO3)6 and Tween 20. For the decomposition process the dispersed seeds and factories seeds were used. Structural studies of the aluminum hydroxide particles were carried out by means of the electron-probe microanalysis and scanning electron microscopy, and phase composition of products was determined by means of X-ray diffraction analysis. Ammonium bicarbonate and Tween 20 were determined as the optimal precipitating reagent and dispersant, correspondingly, resulting in dispersed aluminum hydroxide, which is used as a seed in the decomposition process. It was established that this product in form of dispersed seed considerably reduces the duration of the decomposition process;the maximal decomposition of solution (73.9%) was observed after injection of dispersеd aluminum hydroxide into solution. The final aluminum hydroxide having 90% of particles less than 100 nanometers was obtained within 7 hours of steady decreasing temperature from 70°C to 48°C.展开更多
objects of the research are Kazakhstan’s Turgay clay, studied of method for alumina and potassium metasilicate obtaining from Turgay sub-standard aluminum raw materials. Concluded that optimal conditions for the proc...objects of the research are Kazakhstan’s Turgay clay, studied of method for alumina and potassium metasilicate obtaining from Turgay sub-standard aluminum raw materials. Concluded that optimal conditions for the process of Turgay clay: reaction temperature 100°C, original solution K2O concentration to 300 g/dm3, reaction time 120 min, liquid-solid ratio of 3:1;optimized the conditions of digestion alumina concentrate: original Na2O solution concentration of 400 g/dm3, temperature 280°C, molar ratio CaO : SiO2 = 1. Recovery is 99.6 % of alumina digestion under this condition;crystallized solid phase components as Na2O·Al2O3·6H2O sodium hydroaluminate crystals. Extracted of alumina from solution of sodium展开更多
文摘The influence of the precipitating reagents and dispersants on the formation of nano-aluminum hydroxide from sodium aluminate solution by chemical precipitation was investigated. The influence of the dispersed seeds on the decomposi-tion process was investigated too. The alkaline aluminate solutions were used as original solutions with a concentration of Al2O3 having 14.78 g/dm3, αk—1.6 and127 g/dm3, αk—1.6. For the precipitation processes there were used follow-ing precipitating reagents—solutions HCl, NaHCO3 and NH4HCO3 with a concentration of 80 g/dm3, dispersants—PEG 6000, (NaPO3)6 and Tween 20. For the decomposition process the dispersed seeds and factories seeds were used. Structural studies of the aluminum hydroxide particles were carried out by means of the electron-probe microanalysis and scanning electron microscopy, and phase composition of products was determined by means of X-ray diffraction analysis. Ammonium bicarbonate and Tween 20 were determined as the optimal precipitating reagent and dispersant, correspondingly, resulting in dispersed aluminum hydroxide, which is used as a seed in the decomposition process. It was established that this product in form of dispersed seed considerably reduces the duration of the decomposition process;the maximal decomposition of solution (73.9%) was observed after injection of dispersеd aluminum hydroxide into solution. The final aluminum hydroxide having 90% of particles less than 100 nanometers was obtained within 7 hours of steady decreasing temperature from 70°C to 48°C.
文摘objects of the research are Kazakhstan’s Turgay clay, studied of method for alumina and potassium metasilicate obtaining from Turgay sub-standard aluminum raw materials. Concluded that optimal conditions for the process of Turgay clay: reaction temperature 100°C, original solution K2O concentration to 300 g/dm3, reaction time 120 min, liquid-solid ratio of 3:1;optimized the conditions of digestion alumina concentrate: original Na2O solution concentration of 400 g/dm3, temperature 280°C, molar ratio CaO : SiO2 = 1. Recovery is 99.6 % of alumina digestion under this condition;crystallized solid phase components as Na2O·Al2O3·6H2O sodium hydroaluminate crystals. Extracted of alumina from solution of sodium
