Two-mm thick A1050 pure aluminum plates were successfully joined by conventional and rapid cooling friction stir welding(FSW), respectively. The microstructure and mechanical properties of the welded joints were inves...Two-mm thick A1050 pure aluminum plates were successfully joined by conventional and rapid cooling friction stir welding(FSW), respectively. The microstructure and mechanical properties of the welded joints were investigated by electron backscatter diffraction characterization, Vickers hardness measurements, and tensile testing. The results showed that liquid CO_(2) coolant significantly reduced the peak temperature and increased the cooling rate, so the rapidly cooled FSW joint exhibited fine grains with a large number of dislocations. The grain refinement mechanism of the FSW A1050 pure aluminum joint was primarily attributed to the combined effects of continuous dynamic recrystallization, grain subdivision, and geometric dynamic recrystallization. Compared with conventional FSW, the yield strength, ultimate tensile strength, and fracture elongation of rapidly cooled FSW joint were significantly enhanced, and the welding efficiency was increased from 80% to 93%. The enhanced mechanical properties and improved synergy of strength and ductility were obtained due to the increased dislocation density and remarkable grain refinement. The wear of the tool can produce several WC particles retained in the joint, and the contribution of second phase strengthening to the enhanced strength should not be ignored.展开更多
To improve the wear resistance of the FeCoCrNiB_(0.2)high entropy alloy(HEA),the FeCoCrNiB_(0.2)(WC_(0))and FeCoCrNiB_(0.2)+20wt%WC(WC_(20))HEA coatings were prepared on Q235 steel by laser cladding(LC).The microstruc...To improve the wear resistance of the FeCoCrNiB_(0.2)high entropy alloy(HEA),the FeCoCrNiB_(0.2)(WC_(0))and FeCoCrNiB_(0.2)+20wt%WC(WC_(20))HEA coatings were prepared on Q235 steel by laser cladding(LC).The microstructure,hardness,and tribometer of the HEA coatings were investigated using scanning electron microscopy with spectroscopy(SEM/EDS),X-ray diffraction(XRD),vickers microhardness tester,and pin-on-disc tribometer,respectively.The experimental results show that the WC0HEA coating comprises a simple BCC phase mixed with an M_(2)B phase.Adding 20wt%WC,the WC_(20)HEA coating is composed of a simple BCC phase mixed with the Cr_(23)C_(6)carbide phase.The microstructure of the WC_(20)HEA coating is simple,which consists of equiaxed grain and dendritic.The microhardness also increases from 625.5HV to 806.0HV,and the wear mass loss correspondingly decreases from 30.9 to 14.9 mg.W and C atoms formed by WC dissolution are mainly dissolved in the BCC phase,which leads to the solution strengthening effect.Besides,Cr_(23)C_(6)carbides inhibit the growth of the grains,play the role of fine-grain strengthening,and further improve the hardness and wear resistance of the HEA coating.展开更多
To improve the wear resistance of Fe_(4)CoCrNiB_(0.2) high-entropy alloy(HEA),the Fe_(4)CoCrNiB_(0.2)Mo_(x)(where,x in Fe_(4)CoCrNiB_(0.2)Mo_(x) is a molar content,and the value is 0,0.5,1,respectively)HEAs were prepa...To improve the wear resistance of Fe_(4)CoCrNiB_(0.2) high-entropy alloy(HEA),the Fe_(4)CoCrNiB_(0.2)Mo_(x)(where,x in Fe_(4)CoCrNiB_(0.2)Mo_(x) is a molar content,and the value is 0,0.5,1,respectively)HEAs were prepared on the Q235 substrate by laser cladding.The structure,hardness,and wear resistance of Fe_(4)CoCrNiB_(0.2)Mo_(x) HEAs were investigated using scanning electron microscopy with spectroscopy(SEM/EDS),X-ray diffraction(XRD),Vickers microhardness tester,and pin-on-disc tribometer.The influences of Mo content on the phase structures and mechanical properties of Fe_(4)CoCrNiB_(0.2)Mo_(x) HEAs are studied.The experimental results show that the Fe_(4)CoCrNiB_(0.2)Mo_(x) HEA cladding layers are composed of a simple BCC phase mixed with M_(2)B phase,BCC phase,and BCC+FCC dual-phase,respectively.The wear resistance and hardness of the Fe_(4)CoCrNiB_(0.2)Mo HEA sample are 2 and 1.35 times those of the Fe_(4)CoCrNiB_(0.2) HEA sample,respectively.The microhardness and wear resistance of the Fe_(4)CoCrNiB_(0.2)Mo_(x) HEAs increase with the increase of Mo content.It is found that the Fe_(4)CoCrNiB_(0.2)Mo_(x) HEA cladding layers are mainly strengthened by the solid solution strengthening and fine-grained strengthening.展开更多
基金Funded by the Natural Science Foundation of Jiangsu Province(No.BK20211067)“Qing Lan” Project of Jiangsu Province。
文摘Two-mm thick A1050 pure aluminum plates were successfully joined by conventional and rapid cooling friction stir welding(FSW), respectively. The microstructure and mechanical properties of the welded joints were investigated by electron backscatter diffraction characterization, Vickers hardness measurements, and tensile testing. The results showed that liquid CO_(2) coolant significantly reduced the peak temperature and increased the cooling rate, so the rapidly cooled FSW joint exhibited fine grains with a large number of dislocations. The grain refinement mechanism of the FSW A1050 pure aluminum joint was primarily attributed to the combined effects of continuous dynamic recrystallization, grain subdivision, and geometric dynamic recrystallization. Compared with conventional FSW, the yield strength, ultimate tensile strength, and fracture elongation of rapidly cooled FSW joint were significantly enhanced, and the welding efficiency was increased from 80% to 93%. The enhanced mechanical properties and improved synergy of strength and ductility were obtained due to the increased dislocation density and remarkable grain refinement. The wear of the tool can produce several WC particles retained in the joint, and the contribution of second phase strengthening to the enhanced strength should not be ignored.
基金Funded by the National Natural Science Foundation of China (No.51879089)。
文摘To improve the wear resistance of the FeCoCrNiB_(0.2)high entropy alloy(HEA),the FeCoCrNiB_(0.2)(WC_(0))and FeCoCrNiB_(0.2)+20wt%WC(WC_(20))HEA coatings were prepared on Q235 steel by laser cladding(LC).The microstructure,hardness,and tribometer of the HEA coatings were investigated using scanning electron microscopy with spectroscopy(SEM/EDS),X-ray diffraction(XRD),vickers microhardness tester,and pin-on-disc tribometer,respectively.The experimental results show that the WC0HEA coating comprises a simple BCC phase mixed with an M_(2)B phase.Adding 20wt%WC,the WC_(20)HEA coating is composed of a simple BCC phase mixed with the Cr_(23)C_(6)carbide phase.The microstructure of the WC_(20)HEA coating is simple,which consists of equiaxed grain and dendritic.The microhardness also increases from 625.5HV to 806.0HV,and the wear mass loss correspondingly decreases from 30.9 to 14.9 mg.W and C atoms formed by WC dissolution are mainly dissolved in the BCC phase,which leads to the solution strengthening effect.Besides,Cr_(23)C_(6)carbides inhibit the growth of the grains,play the role of fine-grain strengthening,and further improve the hardness and wear resistance of the HEA coating.
基金Funded by the National Natural Science Foundation of China(No.51879089)。
文摘To improve the wear resistance of Fe_(4)CoCrNiB_(0.2) high-entropy alloy(HEA),the Fe_(4)CoCrNiB_(0.2)Mo_(x)(where,x in Fe_(4)CoCrNiB_(0.2)Mo_(x) is a molar content,and the value is 0,0.5,1,respectively)HEAs were prepared on the Q235 substrate by laser cladding.The structure,hardness,and wear resistance of Fe_(4)CoCrNiB_(0.2)Mo_(x) HEAs were investigated using scanning electron microscopy with spectroscopy(SEM/EDS),X-ray diffraction(XRD),Vickers microhardness tester,and pin-on-disc tribometer.The influences of Mo content on the phase structures and mechanical properties of Fe_(4)CoCrNiB_(0.2)Mo_(x) HEAs are studied.The experimental results show that the Fe_(4)CoCrNiB_(0.2)Mo_(x) HEA cladding layers are composed of a simple BCC phase mixed with M_(2)B phase,BCC phase,and BCC+FCC dual-phase,respectively.The wear resistance and hardness of the Fe_(4)CoCrNiB_(0.2)Mo HEA sample are 2 and 1.35 times those of the Fe_(4)CoCrNiB_(0.2) HEA sample,respectively.The microhardness and wear resistance of the Fe_(4)CoCrNiB_(0.2)Mo_(x) HEAs increase with the increase of Mo content.It is found that the Fe_(4)CoCrNiB_(0.2)Mo_(x) HEA cladding layers are mainly strengthened by the solid solution strengthening and fine-grained strengthening.