The optical reflectance and transmittance spectra in the wavelength range of 300-2500 nm are used to compute the absorption coefficient of zinc oxide films annealed at different post-annealing temperatures 400, 500 an...The optical reflectance and transmittance spectra in the wavelength range of 300-2500 nm are used to compute the absorption coefficient of zinc oxide films annealed at different post-annealing temperatures 400, 500 and 600°C.The values of the cross point between the curves of the real and imaginary parts of the optical conductivity ɑ_1 and ɑ_1 with energy axis of films exhibit values that correspond to optical gaps and are about 3.25-3.3 eV. The maxima of peaks in plots dR/dλ and dT/dλ versus wavelength of films exhibit optical gaps at about 3.12-3.25 eV.The values of the fundamental indirect band gap obtained from the Tauc model are at about 3.14-3.2 eV. It can be seen that films annealed at 600°C have the minimum indirect optical band gap at about 3.15 eV. The films annealed at 600°C have Urbach＇s energy minimum of 1.38 eV and hence have minimum disorder. The dispersion energy d of films annealed at 500°C has the minimum value of 43 eV.展开更多
ZnS/graphene nanocomposites with different graphene concentrations （5, 10 and 15 wt.%） were synthesized using L-cysteine as surfactant and graphene oxide （GO） powders as graphene source. Excellent performance for ...ZnS/graphene nanocomposites with different graphene concentrations （5, 10 and 15 wt.%） were synthesized using L-cysteine as surfactant and graphene oxide （GO） powders as graphene source. Excellent performance for nanocomposites to remove methylene blue （MB） dye and hexavalent chromium （Cr（VI）） under visible-light illumina- tion was revealed. TEM images showed that ZnS NPs were decorated on GO sheets and the GO caused a significant decrease in the ZnS diameter size. XRD patterns, XPS and FTIR spectroscopy results indicated that GO sheets changed into reduced graphene oxide （rGO） during the synthesis process. Photocurrent measurements under a visible- light source indicated a good chemical reaction between ZnS NPs and rGO sheets.展开更多
文摘The optical reflectance and transmittance spectra in the wavelength range of 300-2500 nm are used to compute the absorption coefficient of zinc oxide films annealed at different post-annealing temperatures 400, 500 and 600°C.The values of the cross point between the curves of the real and imaginary parts of the optical conductivity ɑ_1 and ɑ_1 with energy axis of films exhibit values that correspond to optical gaps and are about 3.25-3.3 eV. The maxima of peaks in plots dR/dλ and dT/dλ versus wavelength of films exhibit optical gaps at about 3.12-3.25 eV.The values of the fundamental indirect band gap obtained from the Tauc model are at about 3.14-3.2 eV. It can be seen that films annealed at 600°C have the minimum indirect optical band gap at about 3.15 eV. The films annealed at 600°C have Urbach＇s energy minimum of 1.38 eV and hence have minimum disorder. The dispersion energy d of films annealed at 500°C has the minimum value of 43 eV.
文摘ZnS/graphene nanocomposites with different graphene concentrations （5, 10 and 15 wt.%） were synthesized using L-cysteine as surfactant and graphene oxide （GO） powders as graphene source. Excellent performance for nanocomposites to remove methylene blue （MB） dye and hexavalent chromium （Cr（VI）） under visible-light illumina- tion was revealed. TEM images showed that ZnS NPs were decorated on GO sheets and the GO caused a significant decrease in the ZnS diameter size. XRD patterns, XPS and FTIR spectroscopy results indicated that GO sheets changed into reduced graphene oxide （rGO） during the synthesis process. Photocurrent measurements under a visible- light source indicated a good chemical reaction between ZnS NPs and rGO sheets.