The mechanical and wear properties of CFRP laminate were investigated using a method of cycling low velocity impact, to study the trend and mechanism of impact resistance of the CFRP laminate under repeated impact dur...The mechanical and wear properties of CFRP laminate were investigated using a method of cycling low velocity impact, to study the trend and mechanism of impact resistance of the CFRP laminate under repeated impact during its service process. The interface responses of CFRP laminate under di erent impact kinetic energy during the cycling impact process were studied were studied experimentally, such as impact contact duration, deformation and energy absorption. The worn surface morphologies were observed through optical microscopy and a 3?D surface profiler and the cross?sectional morphologies were observed through SEM to investigate the mechanism of impact material dam?age. Based on a single?degree?of?freedom damping vibration model, the normal contact sti ness and contact damp?ing of the material in di erent wear stages were calculated. It shows the failure process of CFRP laminate damaged by accumulated absorption energy under the cycling impact of di erent initial kinetic energy. The results indicate that the sti ness and damping coe cients will change at di erent impact velocities or cycle numbers. The damage mechanism of CFRP laminates under cycling low kinetic energy is delamination. After repeated experiments, it was found that there was a threshold value for the accumulated absorption energy before the failure of the CFRP laminate.展开更多
基金National Natural Science Foundation of China(Grant Nos.U1530136,51627806)Young Scientific Innovation Team of Science and Technology of Sichuan Province of China(Grant No.2017TD0017)Opening Project of Key Laboratory of Testing Technology for Manufacturing Process of China(Grant Nos.2016-01,Southwest University of Science and Technology)
文摘The mechanical and wear properties of CFRP laminate were investigated using a method of cycling low velocity impact, to study the trend and mechanism of impact resistance of the CFRP laminate under repeated impact during its service process. The interface responses of CFRP laminate under di erent impact kinetic energy during the cycling impact process were studied were studied experimentally, such as impact contact duration, deformation and energy absorption. The worn surface morphologies were observed through optical microscopy and a 3?D surface profiler and the cross?sectional morphologies were observed through SEM to investigate the mechanism of impact material dam?age. Based on a single?degree?of?freedom damping vibration model, the normal contact sti ness and contact damp?ing of the material in di erent wear stages were calculated. It shows the failure process of CFRP laminate damaged by accumulated absorption energy under the cycling impact of di erent initial kinetic energy. The results indicate that the sti ness and damping coe cients will change at di erent impact velocities or cycle numbers. The damage mechanism of CFRP laminates under cycling low kinetic energy is delamination. After repeated experiments, it was found that there was a threshold value for the accumulated absorption energy before the failure of the CFRP laminate.