In this study, jute woven fabrics (1 × 1 plain, twill, zigzag and diamond weave) were manufactured from 100% raw jute yarn. The fabric specimens were treated by 5%, 10%, 15%, 20% and 25% unsaturated polyester res...In this study, jute woven fabrics (1 × 1 plain, twill, zigzag and diamond weave) were manufactured from 100% raw jute yarn. The fabric specimens were treated by 5%, 10%, 15%, 20% and 25% unsaturated polyester resin where styrene monomer used as a solvent and 1% methyl ethyl ketone peroxide (MEKP) was used as initiator. Two bar pressure was applied for complete wetting of the fabric by a Padder and curing was done at 130?C for 10 minutes. The physico-mechanical characteristics of untreated and treated samples were examined and evaluated. It was revealed that moisture content (MC) and water absorbency of the treated specimens were decreased with the increase of resin percentage (%) in the fabrics. MC and water absorbency were maximum decreased up to 50.23% and 60.14% respectively by 25% resin treatment. On the other hand, bending length (BL), flexural rigidity (FR), flexural modulus (FM) and tensile strength (TS) were enhanced with the increase of resin percentage in the fabrics which resulted higher fabric stiffness. The maximum improvement of BL, FR, FM and TS were found to be 6.67%, 56.04%, 10.57% and 18.75% respectively in comparison to untreated sample. Soil degradation tests exhibited that 33.59% TS loss occurred for untreated specimens where only 8.04% loss of TS found for 25% resin treated one. Furthermore, jute based twill, zigzag and diamond fabrics were also treated by 10%, 15%, 20% and 25% resin, then measured their TS and compared with plain fabrics. It was revealed that plain fabrics have superior TS over other fabrics. It was also evident that TS enhanced for all the fabrics after resin treatment and maximum increase found for all the fabrics up to 25% resin treatment.展开更多
Jute fiber (woven fabric, 1 × 1 plain weave) reinforced polypropylene matrix composites were prepared by compression molding with various fiber loading such as 30%, 40%, 46%, 50%, 55% by weight. The mechanical pr...Jute fiber (woven fabric, 1 × 1 plain weave) reinforced polypropylene matrix composites were prepared by compression molding with various fiber loading such as 30%, 40%, 46%, 50%, 55% by weight. The mechanical properties such as tensile strength (TS), bending strength (BS), tensile modulus (TM), bending modulus (BM) and impact strength (IS) of the composite were assessed and analyzed. The highest value of TS, BS, TM, BM and IS were 68.1 MPa, 94.1 MPa, 2936 MPa, 4831 MPa and 14.5 kJ/m2 respectively with 50% fiber loading by weight. It was found that the mechanical properties of the composites were increased with the increase in jute fiber content up to 50% by weight;however, further increase in fiber loading the value decreased. On the basis of fiber content, 50% fiber reinforced composites had the optimum set of mechanical properties. Initially the water absorption rate was higher and then it became slower and static with time. Chemical ageing test with various chemical media such as H2O2, NaOH, HCl and NaCl were performed up to 168 hours. After first 24 hours the composite samples showed gradual weight gain (%) and then the weight gain was become slow and steady in the chemical solution.展开更多
The effect of alkali concentrations has been studied on the color strength （K/S） and color fastness properties of single jersey cotton knitted fabrics dyed with 1% Novacron Red S-B reactive dye. Same bath scouring a...The effect of alkali concentrations has been studied on the color strength （K/S） and color fastness properties of single jersey cotton knitted fabrics dyed with 1% Novacron Red S-B reactive dye. Same bath scouring and bleaching are performed and conventional exhaust dyeing method employed by IR laboratory sample dyeing machine. Various alkali concentrations such as 6, 7, 8, 9 and 10 g/L are employed and other parameters are kept fixed. The color strength （K/S） and color fastness to wash and rubbing are examined and evaluated. It is revealed that with the increase in alkali concentration from 6 g/L to 8 g/L the value of K/S increases and then up to 10 g/L the value decreases. The overall color fastness properties to washing and rubbing for the dyed samples range from good to excellent.展开更多
文摘In this study, jute woven fabrics (1 × 1 plain, twill, zigzag and diamond weave) were manufactured from 100% raw jute yarn. The fabric specimens were treated by 5%, 10%, 15%, 20% and 25% unsaturated polyester resin where styrene monomer used as a solvent and 1% methyl ethyl ketone peroxide (MEKP) was used as initiator. Two bar pressure was applied for complete wetting of the fabric by a Padder and curing was done at 130?C for 10 minutes. The physico-mechanical characteristics of untreated and treated samples were examined and evaluated. It was revealed that moisture content (MC) and water absorbency of the treated specimens were decreased with the increase of resin percentage (%) in the fabrics. MC and water absorbency were maximum decreased up to 50.23% and 60.14% respectively by 25% resin treatment. On the other hand, bending length (BL), flexural rigidity (FR), flexural modulus (FM) and tensile strength (TS) were enhanced with the increase of resin percentage in the fabrics which resulted higher fabric stiffness. The maximum improvement of BL, FR, FM and TS were found to be 6.67%, 56.04%, 10.57% and 18.75% respectively in comparison to untreated sample. Soil degradation tests exhibited that 33.59% TS loss occurred for untreated specimens where only 8.04% loss of TS found for 25% resin treated one. Furthermore, jute based twill, zigzag and diamond fabrics were also treated by 10%, 15%, 20% and 25% resin, then measured their TS and compared with plain fabrics. It was revealed that plain fabrics have superior TS over other fabrics. It was also evident that TS enhanced for all the fabrics after resin treatment and maximum increase found for all the fabrics up to 25% resin treatment.
文摘Jute fiber (woven fabric, 1 × 1 plain weave) reinforced polypropylene matrix composites were prepared by compression molding with various fiber loading such as 30%, 40%, 46%, 50%, 55% by weight. The mechanical properties such as tensile strength (TS), bending strength (BS), tensile modulus (TM), bending modulus (BM) and impact strength (IS) of the composite were assessed and analyzed. The highest value of TS, BS, TM, BM and IS were 68.1 MPa, 94.1 MPa, 2936 MPa, 4831 MPa and 14.5 kJ/m2 respectively with 50% fiber loading by weight. It was found that the mechanical properties of the composites were increased with the increase in jute fiber content up to 50% by weight;however, further increase in fiber loading the value decreased. On the basis of fiber content, 50% fiber reinforced composites had the optimum set of mechanical properties. Initially the water absorption rate was higher and then it became slower and static with time. Chemical ageing test with various chemical media such as H2O2, NaOH, HCl and NaCl were performed up to 168 hours. After first 24 hours the composite samples showed gradual weight gain (%) and then the weight gain was become slow and steady in the chemical solution.
文摘The effect of alkali concentrations has been studied on the color strength （K/S） and color fastness properties of single jersey cotton knitted fabrics dyed with 1% Novacron Red S-B reactive dye. Same bath scouring and bleaching are performed and conventional exhaust dyeing method employed by IR laboratory sample dyeing machine. Various alkali concentrations such as 6, 7, 8, 9 and 10 g/L are employed and other parameters are kept fixed. The color strength （K/S） and color fastness to wash and rubbing are examined and evaluated. It is revealed that with the increase in alkali concentration from 6 g/L to 8 g/L the value of K/S increases and then up to 10 g/L the value decreases. The overall color fastness properties to washing and rubbing for the dyed samples range from good to excellent.