By means of the microstructure observation and creep properties measurement, an investigation has been made into the influence of the salt quenching temperatures on the microstructure and creep property of FGH95 super...By means of the microstructure observation and creep properties measurement, an investigation has been made into the influence of the salt quenching temperatures on the microstructure and creep property of FGH95 superalloy. The results shown that, after full heat treatment, a high volume of g￠ phase and some granular carbide dispersedly precipitate in the matrix. Thereinto, as the molten salt temperature decreases from 650℃to520℃, the size of fine g￠ phase in the alloy decrease gradually and the amount of carbides increase in the alloy. And the alloy quenched in molten salt at520℃possesses better creep resistance due to the fact that there are more granular carbides precipitating in the alloy to enhance the grain strength. During creep, the deformation features of the alloy are that the configurations of stacking fault and slipping dislocations are activated in the alloy.展开更多
The influence of temperatures on the stacking fault energies and deformation mechanism of a Re- containing single crystal nickel-based superalloy during creep at elevated temperatures was investigated by means of calc...The influence of temperatures on the stacking fault energies and deformation mechanism of a Re- containing single crystal nickel-based superalloy during creep at elevated temperatures was investigated by means of calculating the stacking fault energy of alloy, measuring creep properties and performing contrast analysis of dislocation configuration. The results show that the alloy at 760 ℃ possesses lower stacking fault energy, and the stacking fault of alloy increases with increasing temperature. The defor- mation mechanism of alloy during creep at 760 ℃ is 7＇ phase sheared by 〈110〉 super-dislocations, which may be decomposed to form the configuration of Shockley partials plus super-lattice intrinsic stacking fault, while the deformation mechanism of alloy during creep at 1070 ℃ is the screw or edge super- dislocations shearing into the rafted 7＇ phase. But during creep at 7（50 and 980 ℃, some super- dislocations shearing into 7＇ phase may cross-slip from the {111} to {100} planes to form the K-W locks with non-plane core structure, which may restrain the dislocations slipping to enhance the creep resis- tance of alloy at high temperature. The interaction between the Re and other elements may decrease the diffusion rate of atoms to improve the microstructure stability, which is thought to be the main reason why the K-W locks are to be kept in the Re-containing superalloy during creep at 980 ℃.展开更多
文摘By means of the microstructure observation and creep properties measurement, an investigation has been made into the influence of the salt quenching temperatures on the microstructure and creep property of FGH95 superalloy. The results shown that, after full heat treatment, a high volume of g￠ phase and some granular carbide dispersedly precipitate in the matrix. Thereinto, as the molten salt temperature decreases from 650℃to520℃, the size of fine g￠ phase in the alloy decrease gradually and the amount of carbides increase in the alloy. And the alloy quenched in molten salt at520℃possesses better creep resistance due to the fact that there are more granular carbides precipitating in the alloy to enhance the grain strength. During creep, the deformation features of the alloy are that the configurations of stacking fault and slipping dislocations are activated in the alloy.
基金supported by the National Natural Science Foundation of China (Grant No. 51271125)
文摘The influence of temperatures on the stacking fault energies and deformation mechanism of a Re- containing single crystal nickel-based superalloy during creep at elevated temperatures was investigated by means of calculating the stacking fault energy of alloy, measuring creep properties and performing contrast analysis of dislocation configuration. The results show that the alloy at 760 ℃ possesses lower stacking fault energy, and the stacking fault of alloy increases with increasing temperature. The defor- mation mechanism of alloy during creep at 760 ℃ is 7＇ phase sheared by 〈110〉 super-dislocations, which may be decomposed to form the configuration of Shockley partials plus super-lattice intrinsic stacking fault, while the deformation mechanism of alloy during creep at 1070 ℃ is the screw or edge super- dislocations shearing into the rafted 7＇ phase. But during creep at 7（50 and 980 ℃, some super- dislocations shearing into 7＇ phase may cross-slip from the {111} to {100} planes to form the K-W locks with non-plane core structure, which may restrain the dislocations slipping to enhance the creep resis- tance of alloy at high temperature. The interaction between the Re and other elements may decrease the diffusion rate of atoms to improve the microstructure stability, which is thought to be the main reason why the K-W locks are to be kept in the Re-containing superalloy during creep at 980 ℃.