The present paper reports the effective utilization of marble sludge powder(MSP)for the recovery of potash values from waste mica scrap using chlorination roasting-water leaching method.Characterization studies indica...The present paper reports the effective utilization of marble sludge powder(MSP)for the recovery of potash values from waste mica scrap using chlorination roasting-water leaching method.Characterization studies indicated the presence of dolomite as the major mineral phase in MSP,whereas muscovite and quartz were observed in the mica sample.The acid leaching studies suggest a maximum of 22%potash recovery under conditions:4 M H2SO4 acid,particle size of^100μm,stirring speed of 600 r/min,leaching temperature of 75℃,and leaching time of 90 min.The chlorination roasting-water leaching process was adopted to achieve the lowest level of 80%-90%potash recovery.The optimum conditions for the recovery of^93%potash from mica(~8.6wt%K2O)requires 900℃ roasting temperature,30 min roasting time,and 1:1:0.75 mass ratio of mica:MSP:NaCl.The roasting temperature and amount of NaCl are found to be the most important factors for the recovery process.The reaction mechanism suggests the formation of different mineral phases,including sylvite(KCl),wollastonite,kyanite,and enstatite,during roasting,which were confirmed by X-ray diffraction(XRD)analyses and scanning electron microscopy(SEM)morphologies.The MSP-blended NaCl additive is more effective for potash recovery compared with the other reported commercial roasting additives.展开更多
The removal of iron from an Indian diaspore sample was studied using magnetic separation and leaching techniques aided by an in-depth mineralogical characterization study involving quantitative mineralogical evaluatio...The removal of iron from an Indian diaspore sample was studied using magnetic separation and leaching techniques aided by an in-depth mineralogical characterization study involving quantitative mineralogical evaluation by scanning electron microscope（QEMSCAN）, electron probe micro-analyzer（EPMA） and X-ray diffraction（XRD）. The characterization studies indicate that extremely fine-sized hematite grains are associated with several other mineral phases in a complex manner with around 60% of the hematite not liberated even below the size of 38 μm limiting the scope of physical separation processes to remove the iron. Wet high intensity magnetic separation（WHIMS） studies reveal that only 49% of iron can be removed. Further, leaching studies using oxalic acid suggest that around 76% of the iron can be removed under conditions such as a solid to liquid ratio of 0.05：1, a temperature of 90 ℃ a time period of 120 min and an acid concentration of 1 mol/L. The dissolution of iron in oxalic acid is found to be controlled by chemical reaction and the activation energy is calculated as 35.15 k J/mol.展开更多
文摘The present paper reports the effective utilization of marble sludge powder(MSP)for the recovery of potash values from waste mica scrap using chlorination roasting-water leaching method.Characterization studies indicated the presence of dolomite as the major mineral phase in MSP,whereas muscovite and quartz were observed in the mica sample.The acid leaching studies suggest a maximum of 22%potash recovery under conditions:4 M H2SO4 acid,particle size of^100μm,stirring speed of 600 r/min,leaching temperature of 75℃,and leaching time of 90 min.The chlorination roasting-water leaching process was adopted to achieve the lowest level of 80%-90%potash recovery.The optimum conditions for the recovery of^93%potash from mica(~8.6wt%K2O)requires 900℃ roasting temperature,30 min roasting time,and 1:1:0.75 mass ratio of mica:MSP:NaCl.The roasting temperature and amount of NaCl are found to be the most important factors for the recovery process.The reaction mechanism suggests the formation of different mineral phases,including sylvite(KCl),wollastonite,kyanite,and enstatite,during roasting,which were confirmed by X-ray diffraction(XRD)analyses and scanning electron microscopy(SEM)morphologies.The MSP-blended NaCl additive is more effective for potash recovery compared with the other reported commercial roasting additives.
文摘The removal of iron from an Indian diaspore sample was studied using magnetic separation and leaching techniques aided by an in-depth mineralogical characterization study involving quantitative mineralogical evaluation by scanning electron microscope（QEMSCAN）, electron probe micro-analyzer（EPMA） and X-ray diffraction（XRD）. The characterization studies indicate that extremely fine-sized hematite grains are associated with several other mineral phases in a complex manner with around 60% of the hematite not liberated even below the size of 38 μm limiting the scope of physical separation processes to remove the iron. Wet high intensity magnetic separation（WHIMS） studies reveal that only 49% of iron can be removed. Further, leaching studies using oxalic acid suggest that around 76% of the iron can be removed under conditions such as a solid to liquid ratio of 0.05：1, a temperature of 90 ℃ a time period of 120 min and an acid concentration of 1 mol/L. The dissolution of iron in oxalic acid is found to be controlled by chemical reaction and the activation energy is calculated as 35.15 k J/mol.
