Structure and electrochemical performance of delafossite AgFeO_(2)nanoparticles for supercapacitor electrodes

Delafossite AgFeO_(2)nanoparticles with a mixture of 2H and 3R phases were successfully fabricated by using a simple co-precipitation method.The resulting precursor was calcined at temperatures of 100,200,300,400,and 500℃to obtain the delafossite AgFe0_(2)phase.The morphology and microstructure of the prepared AgFeO_(2)samples were characterized by using field emission scanning electron microscopy(FESEM),transmission electron microscopy(TEM),N_(2) adsorption/desorption,X-ray absorption spectroscopy(XAS),and Xray photoelectron spectroscopy(XPS)techniques.A three-electrode system was employed to investigate the electrochemical properties of the delafossite AgFeO_(2)nanoparticles in a 3 M KOH electrolyte.The delafossite AgFeO_(2)nanoparticles calcined at 100℃(AFO100)exhibited the highest surface area of 28.02 m^(2)·g^(-1)and outstanding electrochemical performance with specific capacitances of 229.71 F·g^(-1)at a current density of 1 A·g^(-1)and 358.32 F·g^(-1)at a scan rate of 2 mV·s^(-1).This sample also demonstrated the capacitance retention of 82.99% after 1000 charge/discharge cycles,along with superior specific power and specific energy values of 797.46 W·kg^(-1)and 72.74Wh·kg^(-1),respectively.These findings indicate that delafossite AgFeO_(2)has great potential as an electrode material for supercapacitor applications.

Comparative structural and electrochemical properties of mixed P2/O′3-layered sodium nickel manganese oxide prepared by sol-gel and electrospinning methods:Effect of Na-excess content

The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X-ray diffraction results of the prepared NNMO without adding Na-excess content indicate sodium loss,while the mixed phase of P2/O′3-type layered NNMO presented after adding Na-excess content.Compared with the sol-gel method,the secondary phase of NiO is more suppressed by using the electrospinning method,which is further confirmed by field emission scanning electron microscope images.N_(2) adsorption-desorption isotherms show no remarkably difference in specific surface areas between different preparation methods and Na-excess contents.The analysis of X-ray absorption near edge structure indicates that the oxidation states of Ni and Mn are+2 and+4,respectively.For the electrochemical properties,superior electrochemical performance is observed in the NNMO electrode with a low Na-excess content of 5wt%.The highest specific capacitance is 36.07 F·g^(-1)at0.1 A·g^(-1)in the NNMO electrode prepared by using the sol-gel method.By contrast,the NNMO electrode prepared using the electrospinning method with decreased Na-excess content shows excellent cycling stability of 100%after charge-discharge measurements for 300 cycles.Therefore,controlling the Na excess in the precursor together with the preparation method is important for improving the electrochemical performance of Na-based electrode materials in supercapacitors.

Synthesis, characterization and magnetic properties of KFeO_(2) nanoparticles prepared by a simple egg white solution route

Nanoparticles of potassium ferrite(KFeO_(2))in this work were synthesized by a simple egg white solution method upon calcination in air at 773,873,and 973 K for 2 h.The effects of calcination temperature on the structural and magnetic properties of the synthesized KFeO_(2) nanoparticles were investigated.By varying the calcination temperature,X-ray diffraction and transmission electron microscopy results indicated the changes in crystallinity and morphology including particle size,respectively.Notably,the reduction in particle size of the synthesized KFeO_(2) was found to have a remarkable influence on the magnetic properties.At room temperature,the synthesized KFeO_(2) nanoparticles prepared at 873 K exhibited the highest saturation magnetization(M_(S))of 2.07×10^(4) A·m^(−1).In addition,the coercivity(H_(C))increased from 3.51 to 16.89 kA·m^(−1) as the calcination temperature increased to 973 K.The zero-field cooled(ZFC)results showed that the blocking temperatures(T_(B))of about 125 and 85 K were observed in the samples calcined at 773 and 873 K,respectively.Therefore,this work showed that the egg white solution method is simple,cost effective,and environmentally friendly for the preparation of KFeO_(2) nanoparticles.

Influence of polymer solution on the morphology and local structure of NH_(4)ZnPO_(4)powders synthesized by a simple precipitation method at room temperature

NH_(4)Zn PO_(4)powders were synthesized using a simple precipitation method at room temperature.The effects of polyvinyl pyrrolidone(PVP),polyvinyl alcohol(PVA),glucose,and hexadecyltrimethylammonium bromide(CTAB)solutions on the morphology and structure of the prepared samples were investigated.The phase composition and morphology of the prepared samples were characterized using X-ray diffraction and scanning electron microscopy,respectively.Depending on the polymer sources,the hexagonal structure prepared using non-surfactant of water completely changed to monoclinic structure when CTAB was added.X-ray absorption near-edge structure(XANES)and X-ray photoelectron spectroscopy(XPS)were performed to study the local structure and surface electronic structure of the prepared samples,confirming that the oxidation states of P and Zn ions are^(5+)and^(2+),respectively.On the basis of the results of inductively coupled plasma atomic emission spectroscopy(ICP-OES),the NH_(4)Zn PO_(4)powders can be classified as a slow-release fertilizer where less than 15%of the ions were released in 24 h.A simple precipitation method using water,PVP,PVA,sucrose,and CTAB as a template can be used to synthesize NH4 Zn PO4 powders.In addition,this method may be extended for the preparation of other oxide materials.

Influence of gas-diffusion-layer current collector on electrochemical performance of Ni(OH)_(2) nanostructures

We report the electrochemical performance of Ni(OH)_(2) on a gas diffusion layer(GDL).The Ni(OH)_(2) working electrode was successfully prepared via a simple method,and its electrochemical performance in 1 M NaOH electrolyte was investigated.The electrochemical results showed that the Ni(OH)_(2)/GDL provided the maximum specific capacitance value(418.11 F·g^(−1))at 1 A·g^(−1).Furthermore,the Ni(OH)_(2) electrode delivered a high specific energy of 17.25 Wh·kg^(−1) at a specific power of 272.5 W·kg^(−1) and retained about 81%of the capacitance after 1000 cycles of galvanostatic charge–discharge(GCD)measurements.The results of scanning electron microscopy(SEM)coupled with energy-dispersive X-ray spectroscopy(EDS)revealed the occurrence of sodium deposition after long-time cycling,which caused the reduction in the specific capacitance.This study results suggest that the light-weight GDL,which can help overcome the problem of the oxide layer on metal–foam substrates,is a promising current collector to be used with Ni-based electroactive materials for energy storage applications.