Two types of spinel cathode powders, LiMn2O4 and LiAl0.1Mn1.9O3.9F0.1, were synthesized by solid-state reaction, X-ray diffraction （XRD） patterns of the prepared samples were identified as the spinel structure with ...Two types of spinel cathode powders, LiMn2O4 and LiAl0.1Mn1.9O3.9F0.1, were synthesized by solid-state reaction, X-ray diffraction （XRD） patterns of the prepared samples were identified as the spinel structure with a space group of Fd 3^- m. The cubic lattice parameter was determined from least-squares fitting of the XRD data. The LiAl0.1Mn1.9O3.9F0.1 sample showed a little lower initial capacity, but better cycling performance than the LiMn2O4 sample at both room temperature and an elevated temperature. The Vanderbilt method was used to test the electrochemical conductivity of the LiMn2O4 samples. The electrochemical impedance spectroscopy （EIS） method was employed to investigate the electrochemical properties of these spinel LiMn2O4 samples.展开更多
To study the electrochemical kinetic properties of the Li/Graphite system, cycle voltammerty (CV), ac-impedance and chro- noamperometry (CA) techniques have been used. The results showed that the diffusion of lithium ...To study the electrochemical kinetic properties of the Li/Graphite system, cycle voltammerty (CV), ac-impedance and chro- noamperometry (CA) techniques have been used. The results showed that the diffusion of lithium ions in Li_xC_6 is the rate-determining step. The chemical diffusion coefficients of lithium (D_Li) have been estimated for different x values. As for the same material, the value of D_Li was calculated in order to compare the differences among the three techniques.展开更多
LiMn2O4 powder as a cathode materials for rechargeable lithium-ion batteries was prepared by solid-state reaction from LitCO3 and electrolytic MnOz at different sintering periods （2, 6, 18, and 32 h）. X-ray diffract...LiMn2O4 powder as a cathode materials for rechargeable lithium-ion batteries was prepared by solid-state reaction from LitCO3 and electrolytic MnOz at different sintering periods （2, 6, 18, and 32 h）. X-ray diffraction （XRD） patterns of the prepared samples are identified as the spinel structure with a space group of Fd3 m. The lattice parameters almost remain the same as the sintering periods increase. The sample with a sintering period of 32 h shows good cycling performance at both low and nigh current densities, and also elevated temperature. It is believed that the excellent electrochemical behavior of this sample results from its good crystallinity and large grain size compared with other samples. Different electrochemical measurements were conducted to investigate the electrochemical properties of spinel LiMn204. 2008 University of Science and Technology Beijing. All rights reserved.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No.50272012).
文摘Two types of spinel cathode powders, LiMn2O4 and LiAl0.1Mn1.9O3.9F0.1, were synthesized by solid-state reaction, X-ray diffraction （XRD） patterns of the prepared samples were identified as the spinel structure with a space group of Fd 3^- m. The cubic lattice parameter was determined from least-squares fitting of the XRD data. The LiAl0.1Mn1.9O3.9F0.1 sample showed a little lower initial capacity, but better cycling performance than the LiMn2O4 sample at both room temperature and an elevated temperature. The Vanderbilt method was used to test the electrochemical conductivity of the LiMn2O4 samples. The electrochemical impedance spectroscopy （EIS） method was employed to investigate the electrochemical properties of these spinel LiMn2O4 samples.
文摘To study the electrochemical kinetic properties of the Li/Graphite system, cycle voltammerty (CV), ac-impedance and chro- noamperometry (CA) techniques have been used. The results showed that the diffusion of lithium ions in Li_xC_6 is the rate-determining step. The chemical diffusion coefficients of lithium (D_Li) have been estimated for different x values. As for the same material, the value of D_Li was calculated in order to compare the differences among the three techniques.
基金the National Natural Science Foundation of China(No.50272012).
文摘LiMn2O4 powder as a cathode materials for rechargeable lithium-ion batteries was prepared by solid-state reaction from LitCO3 and electrolytic MnOz at different sintering periods （2, 6, 18, and 32 h）. X-ray diffraction （XRD） patterns of the prepared samples are identified as the spinel structure with a space group of Fd3 m. The lattice parameters almost remain the same as the sintering periods increase. The sample with a sintering period of 32 h shows good cycling performance at both low and nigh current densities, and also elevated temperature. It is believed that the excellent electrochemical behavior of this sample results from its good crystallinity and large grain size compared with other samples. Different electrochemical measurements were conducted to investigate the electrochemical properties of spinel LiMn204. 2008 University of Science and Technology Beijing. All rights reserved.