The growing environmental concerns have led to attention on bio-based composite materials, such as the natural fibres, recycled carbon fibres and bio-based resins. Herein, the bio-based epoxy composites were reinforce...The growing environmental concerns have led to attention on bio-based composite materials, such as the natural fibres, recycled carbon fibres and bio-based resins. Herein, the bio-based epoxy composites were reinforced with ramie fibre (RF) and recycled carbon fibre (rCF) via inter-layer hybridisation. The dynamic mechanical analysis, tensile, flexural and impact properties characterisation were conducted to analyse the mechanical behaviour of the specimens. Also, the morphology of fractured surface after mechanical tests was studied under a scanning electron microscope. When the volume ratio between RF and rCF was varied from 100/0 to 0/100, the flexural and tensile strength of composites was significantly increased, while the impact strength was reduced. Thus the maximum values of flexural strength (182 MPa) and tensile strength (165 MPa) were observed for rCF reinforced composite, whilst impact strength of 24 kJ/m</span><sup><span style="font-family:Verdana;">2</span></sup><span style="font-family:Verdana;"> was found for RF reinforced composite. Furthermore, the values of storage and loss modulus were increased with the rCF incorporation due to a greater degree of restriction with the addition of rCF into the matrix. The hybridisation was able to combine the specific properties of RF and rCF and optimise the mechanical performance of composites. Therefore, the alternative low-cost green composites are prepared which can replace synthetic materials for semi-structural applications.展开更多
Currently, phosphate based glasses have been potential future biomaterial for medical application due to excellent cytocompatibility and fully bioresorbability. In this study, phosphate based glass system with composi...Currently, phosphate based glasses have been potential future biomaterial for medical application due to excellent cytocompatibility and fully bioresorbability. In this study, phosphate based glass system with composition of 48P2O5-12B2O3-(25-X)MgO-14CaO-1Na2O-(X)Fe2O3 (X = 6, 8, 10) and 45P2O5-(Y)B2O3-(32-Y)MgO-14CaO-1Na2O-8Fe2O3 (Y = 12, 15, 20), was prepared via a melting quenching process. The effect of replacing MgO with Fe2O3 and B2O3 on the structural, thermal, degradation properties of phosphate based glass was investigated. Fourier Transform Infrared (FTIR) spectroscopy and Raman spectroscopy analysis confirmed the polymerisation of phosphate based glass network with addition of Fe2O3, thus the processing window was observed to increase whilst the dissolution rate was reduced, attributed to the formation of Fe-O-P cross-link. As the effect on the glass structure stability was demonstrated by both B2O3 and MgO, the nonlinear variation of thermal stability and degradation behaviour was observed for glass system with substitution of MgO by B2O3. However, due to the lower dissolution rate of glass system when compared to the biocompatible phosphate based glass in preliminary study, the expected cytocompatibility could be confirmed in the downstream activities.展开更多
文摘The growing environmental concerns have led to attention on bio-based composite materials, such as the natural fibres, recycled carbon fibres and bio-based resins. Herein, the bio-based epoxy composites were reinforced with ramie fibre (RF) and recycled carbon fibre (rCF) via inter-layer hybridisation. The dynamic mechanical analysis, tensile, flexural and impact properties characterisation were conducted to analyse the mechanical behaviour of the specimens. Also, the morphology of fractured surface after mechanical tests was studied under a scanning electron microscope. When the volume ratio between RF and rCF was varied from 100/0 to 0/100, the flexural and tensile strength of composites was significantly increased, while the impact strength was reduced. Thus the maximum values of flexural strength (182 MPa) and tensile strength (165 MPa) were observed for rCF reinforced composite, whilst impact strength of 24 kJ/m</span><sup><span style="font-family:Verdana;">2</span></sup><span style="font-family:Verdana;"> was found for RF reinforced composite. Furthermore, the values of storage and loss modulus were increased with the rCF incorporation due to a greater degree of restriction with the addition of rCF into the matrix. The hybridisation was able to combine the specific properties of RF and rCF and optimise the mechanical performance of composites. Therefore, the alternative low-cost green composites are prepared which can replace synthetic materials for semi-structural applications.
文摘Currently, phosphate based glasses have been potential future biomaterial for medical application due to excellent cytocompatibility and fully bioresorbability. In this study, phosphate based glass system with composition of 48P2O5-12B2O3-(25-X)MgO-14CaO-1Na2O-(X)Fe2O3 (X = 6, 8, 10) and 45P2O5-(Y)B2O3-(32-Y)MgO-14CaO-1Na2O-8Fe2O3 (Y = 12, 15, 20), was prepared via a melting quenching process. The effect of replacing MgO with Fe2O3 and B2O3 on the structural, thermal, degradation properties of phosphate based glass was investigated. Fourier Transform Infrared (FTIR) spectroscopy and Raman spectroscopy analysis confirmed the polymerisation of phosphate based glass network with addition of Fe2O3, thus the processing window was observed to increase whilst the dissolution rate was reduced, attributed to the formation of Fe-O-P cross-link. As the effect on the glass structure stability was demonstrated by both B2O3 and MgO, the nonlinear variation of thermal stability and degradation behaviour was observed for glass system with substitution of MgO by B2O3. However, due to the lower dissolution rate of glass system when compared to the biocompatible phosphate based glass in preliminary study, the expected cytocompatibility could be confirmed in the downstream activities.