The research used industrial by-products original phosphogypsum(PG)as the main raw material,slag(SG)and Portland cement(PC)as auxiliary materials,and the optimal additive amount was determined according to the compres...The research used industrial by-products original phosphogypsum(PG)as the main raw material,slag(SG)and Portland cement(PC)as auxiliary materials,and the optimal additive amount was determined according to the compressive strength value of the sample.Comprehensively evaluate the water resistance and volume stability of the samples,and determine the best formula for new roadbed stabilized materials.The results showed that when the weight ratio of PG,slag and cement was OPG:SG:PC=6:3:1,and mixed with 5%micro silica fume(MSF)and 3‰hydroxypropyl methyl cellulose(HPMC),the sample’s comprehensive performance was the best,specifically,the sample’s compressive strength in 60 days reached 28.8 MPa,the softening coefficient reached 0.9,and the expansion rate was stable at about−0.2%.In addition,the mechanism of action of enhancers MSF and HPMC was analyzed according to use Vicat device,X-ray diffractometer and scanning electron microscope.The best formula SP3GH3 has the best curing effect on soil.The 28-day unconfined compressive strength(UCS)of the sample reached 2.4 MPa,the expansion rate was less than 0.09%,and the water stability coefficient was above 0.79,which was higher than that of the samples cured by traditional cement and lime during the same period.展开更多
A phosphogypsum-based subgrade stabilizer(PBSS)was formulated using industrial by-product phosphogypsum(PG),mixed with slag and calcium-silicon-rich active material(GSR).The active powder(AP)was used to modify PBSS,an...A phosphogypsum-based subgrade stabilizer(PBSS)was formulated using industrial by-product phosphogypsum(PG),mixed with slag and calcium-silicon-rich active material(GSR).The active powder(AP)was used to modify PBSS,and PBSS-AP was obtained.PBSS and PBSS-AP were each mixed with 10%silty soil,and cement and lime(CAL:5%lime+2%cement)were used as the traditional material for comparative experiments.Samples were cured under standard conditions,and tested for unconfined compressive strength(UCS),water stability,volume expansion,and leachate,to explore the stabilization effect of the three solidified materials on silty soil.The results showed that the comprehensive performance of sility soil mixed with 12%PBSS-AP was the best.The CaO,SiO_(2)and Al_(2)O_(3)provided by PG,Slag and GSR will react with water to form a stable C-S-H gel,which is conducive to stabilizing the soil.Field application results showed that the compaction exceeded 95%,the deflection was 144.9 mm,and UCS was 2.5 MPa after 28 days.These findings indicated that PBSS-AP is an effective stabilizer for subgrade soils.展开更多
基金This work was supported by the Jiangsu Provincial Science and Technology Department’s Social Development-Major Science and Technology Demonstration Project(Grant No.BE2018697)the Jiangsu Provincial Science and Technology Department Social Development Project(Grant No.BE2017704)the Scientific Research Project of the Suqian Municipal Transportation Bureau.
文摘The research used industrial by-products original phosphogypsum(PG)as the main raw material,slag(SG)and Portland cement(PC)as auxiliary materials,and the optimal additive amount was determined according to the compressive strength value of the sample.Comprehensively evaluate the water resistance and volume stability of the samples,and determine the best formula for new roadbed stabilized materials.The results showed that when the weight ratio of PG,slag and cement was OPG:SG:PC=6:3:1,and mixed with 5%micro silica fume(MSF)and 3‰hydroxypropyl methyl cellulose(HPMC),the sample’s comprehensive performance was the best,specifically,the sample’s compressive strength in 60 days reached 28.8 MPa,the softening coefficient reached 0.9,and the expansion rate was stable at about−0.2%.In addition,the mechanism of action of enhancers MSF and HPMC was analyzed according to use Vicat device,X-ray diffractometer and scanning electron microscope.The best formula SP3GH3 has the best curing effect on soil.The 28-day unconfined compressive strength(UCS)of the sample reached 2.4 MPa,the expansion rate was less than 0.09%,and the water stability coefficient was above 0.79,which was higher than that of the samples cured by traditional cement and lime during the same period.
基金the Jiangsu Provincial Science and Technology Department’s Social Development-Major Science and Technology Demonstration Project(Grant No.BE2018697)the Jiangsu Provincial Science and Technology Department Social Development Project(Grant No.BE2017704)the Scientific Research Project of the Suqian Municipal Transportation Bureau.
文摘A phosphogypsum-based subgrade stabilizer(PBSS)was formulated using industrial by-product phosphogypsum(PG),mixed with slag and calcium-silicon-rich active material(GSR).The active powder(AP)was used to modify PBSS,and PBSS-AP was obtained.PBSS and PBSS-AP were each mixed with 10%silty soil,and cement and lime(CAL:5%lime+2%cement)were used as the traditional material for comparative experiments.Samples were cured under standard conditions,and tested for unconfined compressive strength(UCS),water stability,volume expansion,and leachate,to explore the stabilization effect of the three solidified materials on silty soil.The results showed that the comprehensive performance of sility soil mixed with 12%PBSS-AP was the best.The CaO,SiO_(2)and Al_(2)O_(3)provided by PG,Slag and GSR will react with water to form a stable C-S-H gel,which is conducive to stabilizing the soil.Field application results showed that the compaction exceeded 95%,the deflection was 144.9 mm,and UCS was 2.5 MPa after 28 days.These findings indicated that PBSS-AP is an effective stabilizer for subgrade soils.