High pressure die casting copper is used to produce rotors for induction motors to improve efficiency.Experiments were carried out for a special"step-shape"casting with different step thicknesses.Based on th...High pressure die casting copper is used to produce rotors for induction motors to improve efficiency.Experiments were carried out for a special"step-shape"casting with different step thicknesses.Based on the measured temperature inside the die,the interfacial heat transfer coefficient(IHTC)at the metal/die interface during vacuum die casting was evaluated by solving the inverse problem.The IHTC peak value was 4.5×10^3-11×10^3 W·m^-2·K^-1 under the basic operation condition.The influences of casting pressure,fast shot speed,pouring temperature and initial die surface temperature on the IHTC peak values were investigated.Results show that a greater casting pressure and faster shot speed could only increase the IHTC peak values at the location close to the ingate.An increase of pouring temperature and/or initial die surface temperature significantly increases the IHTC peak values.展开更多
Pure copper tensile bars were produced by conventional die casting(HPDC) and vacuum-assist die casting(VADC) processes. Porosity and mechanical properties were investigated by using optical microscopy(OM), scanning el...Pure copper tensile bars were produced by conventional die casting(HPDC) and vacuum-assist die casting(VADC) processes. Porosity and mechanical properties were investigated by using optical microscopy(OM), scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS), X-ray computed tomography(XCT) and tensile tester. Results show that porosities including gas porosity and shrinkage porosity could be observed in copper castings. Since the application of vacuum could reduce filling related gas entrapment and facilitate solidification due to the increased heat transfer between metal and die, both number and size of the entrapped gases, as well as shrinkage porosities were significantly reduced in vacuum-assist die castings of pure copper. The porosity fraction decreased from 2.243% to 0.875% compared with that of the conventional die casting. Besides, mechanical properties were improved significantly, i.e., by 15% for ultimate tensile strength and three times for elongation.展开更多
文摘High pressure die casting copper is used to produce rotors for induction motors to improve efficiency.Experiments were carried out for a special"step-shape"casting with different step thicknesses.Based on the measured temperature inside the die,the interfacial heat transfer coefficient(IHTC)at the metal/die interface during vacuum die casting was evaluated by solving the inverse problem.The IHTC peak value was 4.5×10^3-11×10^3 W·m^-2·K^-1 under the basic operation condition.The influences of casting pressure,fast shot speed,pouring temperature and initial die surface temperature on the IHTC peak values were investigated.Results show that a greater casting pressure and faster shot speed could only increase the IHTC peak values at the location close to the ingate.An increase of pouring temperature and/or initial die surface temperature significantly increases the IHTC peak values.
文摘Pure copper tensile bars were produced by conventional die casting(HPDC) and vacuum-assist die casting(VADC) processes. Porosity and mechanical properties were investigated by using optical microscopy(OM), scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS), X-ray computed tomography(XCT) and tensile tester. Results show that porosities including gas porosity and shrinkage porosity could be observed in copper castings. Since the application of vacuum could reduce filling related gas entrapment and facilitate solidification due to the increased heat transfer between metal and die, both number and size of the entrapped gases, as well as shrinkage porosities were significantly reduced in vacuum-assist die castings of pure copper. The porosity fraction decreased from 2.243% to 0.875% compared with that of the conventional die casting. Besides, mechanical properties were improved significantly, i.e., by 15% for ultimate tensile strength and three times for elongation.
