Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners a...Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.展开更多
In order to improve the through-thickness homogeneity and properties of aviation aluminum alloy thick plate.The effect of heating-cooling retrogression and re-ageing on the performance of Al-8Zn-2Mg-2Cu alloy thick pl...In order to improve the through-thickness homogeneity and properties of aviation aluminum alloy thick plate.The effect of heating-cooling retrogression and re-ageing on the performance of Al-8Zn-2Mg-2Cu alloy thick plate was investigated by hardness tests, electrical conductivity tests and transmission electron microscopy(TEM) observation.Results revealed that, during retrogression heating, the fine pre-precipitates in surface layer dissolve more and the undissolved η′ or η phases are more coarsened than that of center layer. During slow cooling after retrogression,precipitates continue coarsening but with a lower rate and the secondary precipitation occurs in both layers. Finer precipitates resulting from the secondary precipitation are more in surface. However, the coarsening and secondary precipitation behaviors are restrained in both layers under quick cooling condition. The electrical conductivity and through-thickness homogeneity of precipitates increases while the hardness decreases with cooling rate decreasing. After the optimized non-isothermal retrogression and re-ageing(NRRA) including air-cooling retrogression, the throughthickness homogeneity which is evaluated by integrated retrogression effects has been improved to 94%. The tensile strength, fracture toughness and exfoliation corrosion grade of Al-8Zn-2Mg-2Cu alloy plate is 619 MPa, 24.7 MPa·m^(1/2)and EB, respectively, which indicates that the non-isothermal retrogression and re-aging(NRRA) could improve the mechanical properties and corrosion resistance with higher through-thickness homogeneity.展开更多
ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12%Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the ...A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12%Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the coatings were analyzed by SEM and XRD, and the heat insulation performance and the thermal shock resistance of the coatings were investigated. With ZrO2 nanoparticles addition, the cathode plasma discharge on the coating surface is more obvious than that without ZrO2 nanoparticles addition, the coating is more uniform and compact, and the thickness of the coating increases. Furthermore, the content of Zr and Y elements increases and the degree of crystallization of the coating is more complete. The formation of the solid solution of yttrium stabilized zirconia is promoted by cathode plasma discharge. In addition, the thermal insulation temperature increases as ZrO2 nano-particles are added to the electrolyte. After 1 000 cycles of thermal shock, there was no cracking in the coating surface layer, which indicated that the CPED coating with ZrO2 nanoparticles addition possessed a good thermal shock resistance.展开更多
In this work, AI-7.5Si-4Cu alloy melt modified by AI-10Sr, RE and AI-5-13-B master alloys was poured into multi-step moulds made from three moulding sands, including quartz, alumina and chromite, to investigate compar...In this work, AI-7.5Si-4Cu alloy melt modified by AI-10Sr, RE and AI-5-13-B master alloys was poured into multi-step moulds made from three moulding sands, including quartz, alumina and chromite, to investigate comparatively the effects of different cooling rates of the casting mould on the alloy＇s microstructures and mechanical properties. The results show that with an increase in wall thickness, the cooling rate decreases, the dendrite arm spacing （DAS） increases significantly and the mechanical properties decrease steadily. The elongation is more sensitive to the cooling rate than the tensile strength. No obvious trend of the effect of wall thickness on hardness of the alloy was found. When the cooling rate is at its greatest, the microstructures and mechanical properties are the best when using chromite sand. The improvement of the properties is mainly attributed to the decrease of the DAS, the grain refinement and the metamorphic effect. Each of the three has a strong impact on the microstructures. Furthermore, a series of fitting models was established based on the data of the DAS to predict the mechanical properties of the multivariate sand-cast AI-7.5Si-4Cu alloy,展开更多
Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resista...Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resistance ofthe as-welded Cu12Mn8Al3Fe2Ni alloy is much more superior to that of the as-cast one. The cumulative mass lossand the mass loss rate of the as-welded Cu12Mn8Al3Fe2Ni alloy are almost 1/4 that of the as-cast one. SEM analysisof eroded specimens reveals that the as-cast Cu12Mn8Al3Fe2Ni alloy is attacked more severely than the as-weldedone. Microcracks causing cavitation damage initiate at the phase boundaries.展开更多
In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0～14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher th...In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0～14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.展开更多
The corrosion resistance of the micro-arc oxidation(MAO) ceramic coating on a cast Al-13Si-5Cu alloy was investigated using various electrochemical methods including electrochemical impedance spectroscopy(EIS) and pol...The corrosion resistance of the micro-arc oxidation(MAO) ceramic coating on a cast Al-13Si-5Cu alloy was investigated using various electrochemical methods including electrochemical impedance spectroscopy(EIS) and polarization curves.Microstructures of MAO ceramic coating were studied by SEM,and the influence of microscopic patterns on corrosion resistance was analyzed.The corrosion resistance of the aluminum alloy can be improved significantly by MAO process owing to increasing impedance and corrosion potential and decreasing corrosion current,and the ceramic coatings are composed of loose layer,compact layer and transition layer,which improve the corrosion resistance.The corrosin resistance is determined by the thickness of the compact layer and is not proportional to the total thickness of MAO,though the latter is one of the important factors influencing the corrosin resistance.展开更多
基金Project (09C26279200863) supported by Technology Innovation Fund Project of High-tech Small and Medium Enterprises,Ministry of Science and Technology of ChinaProject (BA2011084) supported by Special Fund Project on Science and Technology Achievement Transformation of Jiangsu Province,China
文摘Al-7.5Si-4Cu cast alloy melt modified by Al-5Ti-B, RE and Al-10Sr master alloys were poured in the chromite sand moulds, to investigate comparatively the effects of individual or combined additions of grain refiners and modifiers on the mechanical properties, microstructures, grain refining and modification, and intermetallic compounds of the alloy. The results show that the mechanical properties and the microstructures of Al-7.5Si-4Cu cast alloys are improved immensely by combining addition of 0.8%Al-5Ti-B, 0.1%RE and 0.1%Al-10Sr grain refiners and modifiers compared with the individual addition and cast conditions. For individual addition condition, addition of 0.8%Al-5Ti-B master alloy can obtain superior tensile strength, Brinell hardness and finer equiaxedα（Al） dendrites. The alloy with 0.1%RE master alloy shows the highest improvement in ductility because the rare earth can purify the molten metal and change the shape of intermetallic compounds. While the alloy with 0.1%Al-10Sr modifier shows only good improvement in yield strength, and the improvement of other performance is unsatisfactory. The Al-10Sr modifier has a significant metamorphism for the eutectic silicon, but will make the gas content in the aluminum alloy melt increase to form serious columnar grain structures. The effects of grain refining and modification on mean area and aspect ratio have the same conclusions obtained in the mechanical properties and the microstructures analyses.
基金Project(51801082) supported by National Natural Science Foundation of ChinaProjects(GY2021003, GY2021020)supported by the Key Research and Development Program of Zhenjiang City,China+1 种基金Project(KYCX21_3453) supported by Graduate Research and Innovation Projects in Jiangsu Province,ChinaProject(202110289002Z) supported by Undergraduate Innovation and Entrepreneurship Training Program of Jiangsu Province,China。
文摘In order to improve the through-thickness homogeneity and properties of aviation aluminum alloy thick plate.The effect of heating-cooling retrogression and re-ageing on the performance of Al-8Zn-2Mg-2Cu alloy thick plate was investigated by hardness tests, electrical conductivity tests and transmission electron microscopy(TEM) observation.Results revealed that, during retrogression heating, the fine pre-precipitates in surface layer dissolve more and the undissolved η′ or η phases are more coarsened than that of center layer. During slow cooling after retrogression,precipitates continue coarsening but with a lower rate and the secondary precipitation occurs in both layers. Finer precipitates resulting from the secondary precipitation are more in surface. However, the coarsening and secondary precipitation behaviors are restrained in both layers under quick cooling condition. The electrical conductivity and through-thickness homogeneity of precipitates increases while the hardness decreases with cooling rate decreasing. After the optimized non-isothermal retrogression and re-ageing(NRRA) including air-cooling retrogression, the throughthickness homogeneity which is evaluated by integrated retrogression effects has been improved to 94%. The tensile strength, fracture toughness and exfoliation corrosion grade of Al-8Zn-2Mg-2Cu alloy plate is 619 MPa, 24.7 MPa·m^(1/2)and EB, respectively, which indicates that the non-isothermal retrogression and re-aging(NRRA) could improve the mechanical properties and corrosion resistance with higher through-thickness homogeneity.
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
基金Funded by the Youth Innovation Team of Shaanxi Universities,Shaanxi Key Research and Development Program(No.2018GY-111)Shaanxi Provincial Department of Education Industrialization Cultivation Project(No.17JF009)Yulin Science and Technology Project(Nos.2016-16-4 and 2018-2-30)
文摘A novel thermal-protective coating has been successfully prepared by CPED process on a cast Al-12%Si alloy with the addition of ZrO2 nano-particles in the electrolyte. The microstructures and phase composition of the coatings were analyzed by SEM and XRD, and the heat insulation performance and the thermal shock resistance of the coatings were investigated. With ZrO2 nanoparticles addition, the cathode plasma discharge on the coating surface is more obvious than that without ZrO2 nanoparticles addition, the coating is more uniform and compact, and the thickness of the coating increases. Furthermore, the content of Zr and Y elements increases and the degree of crystallization of the coating is more complete. The formation of the solid solution of yttrium stabilized zirconia is promoted by cathode plasma discharge. In addition, the thermal insulation temperature increases as ZrO2 nano-particles are added to the electrolyte. After 1 000 cycles of thermal shock, there was no cracking in the coating surface layer, which indicated that the CPED coating with ZrO2 nanoparticles addition possessed a good thermal shock resistance.
基金financially supported by the Technology Innovation Fund Project of High-tech Small and Medium Enterprises,Ministry of Science and Technology of China(No:09C26279200863)the Special Fund Project on Science and Technology Achievement Transformation of Jiangsu Province(No:BA201184)
文摘In this work, AI-7.5Si-4Cu alloy melt modified by AI-10Sr, RE and AI-5-13-B master alloys was poured into multi-step moulds made from three moulding sands, including quartz, alumina and chromite, to investigate comparatively the effects of different cooling rates of the casting mould on the alloy＇s microstructures and mechanical properties. The results show that with an increase in wall thickness, the cooling rate decreases, the dendrite arm spacing （DAS） increases significantly and the mechanical properties decrease steadily. The elongation is more sensitive to the cooling rate than the tensile strength. No obvious trend of the effect of wall thickness on hardness of the alloy was found. When the cooling rate is at its greatest, the microstructures and mechanical properties are the best when using chromite sand. The improvement of the properties is mainly attributed to the decrease of the DAS, the grain refinement and the metamorphic effect. Each of the three has a strong impact on the microstructures. Furthermore, a series of fitting models was established based on the data of the DAS to predict the mechanical properties of the multivariate sand-cast AI-7.5Si-4Cu alloy,
文摘Cavitation erosion behavior of as-welded Cu12Mn8Al3Fe2Ni alloy in 3.5% NaCl aqueous solution was studied bymagnetostrictive vibratory device for cavitation erosion. The results show that the cavitation erosion resistance ofthe as-welded Cu12Mn8Al3Fe2Ni alloy is much more superior to that of the as-cast one. The cumulative mass lossand the mass loss rate of the as-welded Cu12Mn8Al3Fe2Ni alloy are almost 1/4 that of the as-cast one. SEM analysisof eroded specimens reveals that the as-cast Cu12Mn8Al3Fe2Ni alloy is attacked more severely than the as-weldedone. Microcracks causing cavitation damage initiate at the phase boundaries.
文摘In the as-cast Ti-55 alloy, the intragranular rare earth-rich phase particles are about 1. 0～14 μm in diameter, elliptical, and rich in Nd, Sn, and O. The contents of Nd and Sn on the grain boundaries are higher than those at other sites. The intragranular phases grow preferably at the region on the grain boundaries, which causes the formation of the elliptical morphology of the intragranular phases.
基金Project(09JK481) supported by the Special Research Plan Project of the Education Department of Shaanxi Provincethe Open Fund Item of Thin-film Technology and Optical Detection Key Laboratory of Shaanxi Province,China
文摘The corrosion resistance of the micro-arc oxidation(MAO) ceramic coating on a cast Al-13Si-5Cu alloy was investigated using various electrochemical methods including electrochemical impedance spectroscopy(EIS) and polarization curves.Microstructures of MAO ceramic coating were studied by SEM,and the influence of microscopic patterns on corrosion resistance was analyzed.The corrosion resistance of the aluminum alloy can be improved significantly by MAO process owing to increasing impedance and corrosion potential and decreasing corrosion current,and the ceramic coatings are composed of loose layer,compact layer and transition layer,which improve the corrosion resistance.The corrosin resistance is determined by the thickness of the compact layer and is not proportional to the total thickness of MAO,though the latter is one of the important factors influencing the corrosin resistance.