In this work,a two-step metal organic chemical vapor deposition(MOCVD)method was applied for growingβ-Ga_(2)O_(3) film on c-plane sapphire.Optimized buffer layer growth temperature(T_(B))was found at 700℃ and theβ-...In this work,a two-step metal organic chemical vapor deposition(MOCVD)method was applied for growingβ-Ga_(2)O_(3) film on c-plane sapphire.Optimized buffer layer growth temperature(T_(B))was found at 700℃ and theβ-Ga_(2)O_(3) film with full width at half maximum(FWHM)of 0.66°was achieved.A metal−semiconductor−metal(MSM)solar-blind photodetector(PD)was fabricated based on theβ-Ga_(2)O_(3) film.Ultrahigh responsivity of 1422 A/W@254 nm and photo-to-dark current ratio(PDCR)of 10^(6) at 10 V bias were obtained.The detectivity of 2.5×10^(15) Jones proved that the photodetector has outstanding performance in detecting weak signals.Moreover,the photodetector exhibited superior wavelength selectivity with rejection ratio(R_(250 nm)/R_(400 nm))of 105.These results indicate that the two-step method is a promising approach for preparation of high-qualityβ-Ga_(2)O_(3)films for high-performance solar-blind photodetectors.展开更多
对实验室用 MOCVD方法生长的未掺杂 Ga N单晶膜的发光性能进行了研究。结果表明 :在室温时未掺杂 Ga N单晶出现的能量为 2 .9e V左右蓝带发光与补偿度有较强的依赖关系。高补偿 Ga N的蓝带发射强 ,低补偿 Ga N的蓝带发射弱。对蓝带发光...对实验室用 MOCVD方法生长的未掺杂 Ga N单晶膜的发光性能进行了研究。结果表明 :在室温时未掺杂 Ga N单晶出现的能量为 2 .9e V左右蓝带发光与补偿度有较强的依赖关系。高补偿 Ga N的蓝带发射强 ,低补偿 Ga N的蓝带发射弱。对蓝带发光机理进行了探讨 ,认为蓝带为导带电子跃迁至受主能级的发光 ( e A发光 )。观察到降低 Ga N补偿度能提高 Ga N带边发射强度。展开更多
基金the National Natural Science Foundation of China(62304252)the Youth Innovation Promotion Association of Chinese Academy Sciences(CAS)and IMECAS-HKUST-Joint Laboratory of Microelectronics。
基金This work was supported by the National Key Research and Development Program of China(Grant No.2020YFB2206103)。
文摘In this work,a two-step metal organic chemical vapor deposition(MOCVD)method was applied for growingβ-Ga_(2)O_(3) film on c-plane sapphire.Optimized buffer layer growth temperature(T_(B))was found at 700℃ and theβ-Ga_(2)O_(3) film with full width at half maximum(FWHM)of 0.66°was achieved.A metal−semiconductor−metal(MSM)solar-blind photodetector(PD)was fabricated based on theβ-Ga_(2)O_(3) film.Ultrahigh responsivity of 1422 A/W@254 nm and photo-to-dark current ratio(PDCR)of 10^(6) at 10 V bias were obtained.The detectivity of 2.5×10^(15) Jones proved that the photodetector has outstanding performance in detecting weak signals.Moreover,the photodetector exhibited superior wavelength selectivity with rejection ratio(R_(250 nm)/R_(400 nm))of 105.These results indicate that the two-step method is a promising approach for preparation of high-qualityβ-Ga_(2)O_(3)films for high-performance solar-blind photodetectors.
文摘对实验室用 MOCVD方法生长的未掺杂 Ga N单晶膜的发光性能进行了研究。结果表明 :在室温时未掺杂 Ga N单晶出现的能量为 2 .9e V左右蓝带发光与补偿度有较强的依赖关系。高补偿 Ga N的蓝带发射强 ,低补偿 Ga N的蓝带发射弱。对蓝带发光机理进行了探讨 ,认为蓝带为导带电子跃迁至受主能级的发光 ( e A发光 )。观察到降低 Ga N补偿度能提高 Ga N带边发射强度。