To promote the scale-up production and industrial application of magnesium oxide （MgO） whiskers, MgO whiskers were prepared by the calcination method of the precursor. The precursor MgSO4·5Mg（OH）2·2H2O ...To promote the scale-up production and industrial application of magnesium oxide （MgO） whiskers, MgO whiskers were prepared by the calcination method of the precursor. The precursor MgSO4·5Mg（OH）2·2H2O （152 MOS） single component was prepared by hydrothermal synthesis reaction in MgSO4 solution and NaOH solution. MgO whisker was prepared by heating treatment of the precursor at low heating speed to keep the structure of the precursor not be destroyed. The composition, the morphology and the structure of these whiskers were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results indicate that the MgO whisker was about 0.5-1.2 μm in diameter and 20-80 μm in length, with an aspect ratio no less than 100.展开更多
Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
文摘To promote the scale-up production and industrial application of magnesium oxide （MgO） whiskers, MgO whiskers were prepared by the calcination method of the precursor. The precursor MgSO4·5Mg（OH）2·2H2O （152 MOS） single component was prepared by hydrothermal synthesis reaction in MgSO4 solution and NaOH solution. MgO whisker was prepared by heating treatment of the precursor at low heating speed to keep the structure of the precursor not be destroyed. The composition, the morphology and the structure of these whiskers were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results indicate that the MgO whisker was about 0.5-1.2 μm in diameter and 20-80 μm in length, with an aspect ratio no less than 100.
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.