In this study, the influence of hot isostatic pressing（HIP） process on the 418 alloy produced by metal injection molding（MIM） technique（named as MIM 418）was investigated based on the characteristic analysis of 4...In this study, the influence of hot isostatic pressing（HIP） process on the 418 alloy produced by metal injection molding（MIM） technique（named as MIM 418）was investigated based on the characteristic analysis of 418 alloy powder. And comparison analysis of the microstructure and mechanical property between the MIM 418 and as-cast 418 alloys was performed by scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS）,and X-ray diffraction（XRD）. The results show that MIM418 alloy exhibits fine grain（~30 μm） and uniform microstructure. The defects existing in MIM 418 alloy formed during sintering process can be eliminated through HIP treatment, and the relative density increases from97.0 % to 99.5 %. The mechanical property can be improved significantly because of the elimination of defects, and the tensile strength and elongation are1,271 MPa and 16.8 %, respectively, which are increased by 34.5 % and 180 % compared with K418 alloy after solution heat treatment.展开更多
基金financially supported by the National High Technology Research and Development Program of China (No. 2012AA03AA514)
文摘In this study, the influence of hot isostatic pressing（HIP） process on the 418 alloy produced by metal injection molding（MIM） technique（named as MIM 418）was investigated based on the characteristic analysis of 418 alloy powder. And comparison analysis of the microstructure and mechanical property between the MIM 418 and as-cast 418 alloys was performed by scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS）,and X-ray diffraction（XRD）. The results show that MIM418 alloy exhibits fine grain（~30 μm） and uniform microstructure. The defects existing in MIM 418 alloy formed during sintering process can be eliminated through HIP treatment, and the relative density increases from97.0 % to 99.5 %. The mechanical property can be improved significantly because of the elimination of defects, and the tensile strength and elongation are1,271 MPa and 16.8 %, respectively, which are increased by 34.5 % and 180 % compared with K418 alloy after solution heat treatment.