Li4Ti5O12 powders were prepared by so-gel method using tetrabutyl titanate,lithium acetate and absolute alcohol as starting materials.Li4Ti5O12-polyaniline(Li4Ti5O12-PAn)composite was prepared by in situ polymerizatio...Li4Ti5O12 powders were prepared by so-gel method using tetrabutyl titanate,lithium acetate and absolute alcohol as starting materials.Li4Ti5O12-polyaniline(Li4Ti5O12-PAn)composite was prepared by in situ polymerization method using aniline, ammonium persulfate and hydrochloricarried as starting materials.Li4Ti5O12-PAn composite was characterized by X-ray diffractometry(XRD),infrared spectrum(IR)combined with electrochemical tests.The results show that the electrical conductivity is enhanced obviously due to the introduction of PAn to Li4Ti5O12.Li4Ti5O12-PAn composite exhibits better high-rate capability and cyclability than Li4Ti5O12.The composite can deliver a specific capacity of 191.3 and 148.9 mA·h/g,only 0.13%and 0.61%of the capacity is lose after being discharged 80 times at 0.1C and 2.0C,respectively.展开更多
基金Project(20376086)supported by the National Natural Science Foundation of ChinaProject(2005037700)supported by Postdoctora Science Foundation of China+2 种基金Project(07JJ3014)supported by Hunan Provincial Natural Science Foundation of ChinaProject(07A058)supported by Scientific Research Fund of Hunan Provincial Education DepartmentProject(2004107)supported by Postdoctoral Science Foundation of Central South University,China
文摘Li4Ti5O12 powders were prepared by so-gel method using tetrabutyl titanate,lithium acetate and absolute alcohol as starting materials.Li4Ti5O12-polyaniline(Li4Ti5O12-PAn)composite was prepared by in situ polymerization method using aniline, ammonium persulfate and hydrochloricarried as starting materials.Li4Ti5O12-PAn composite was characterized by X-ray diffractometry(XRD),infrared spectrum(IR)combined with electrochemical tests.The results show that the electrical conductivity is enhanced obviously due to the introduction of PAn to Li4Ti5O12.Li4Ti5O12-PAn composite exhibits better high-rate capability and cyclability than Li4Ti5O12.The composite can deliver a specific capacity of 191.3 and 148.9 mA·h/g,only 0.13%and 0.61%of the capacity is lose after being discharged 80 times at 0.1C and 2.0C,respectively.