Changing the N content in the Ti_(3)AlC_(2−y)N_(y) MAX phase solid solutions allows for the fine-tuning of their properties.However,systematic studies on the synthesis and properties of Ti_(3)AlC_(2−y)N_(y) solid solu...Changing the N content in the Ti_(3)AlC_(2−y)N_(y) MAX phase solid solutions allows for the fine-tuning of their properties.However,systematic studies on the synthesis and properties of Ti_(3)AlC_(2−y)N_(y) solid solution bulks have not been reported thus far.Here,previously reported Ti_(3)AlC_(2−y)N_(y) solid solution bulks(y=0.3,0.5,0.8,and 1.0)were synthesized via hot pressing of their powder counterparts under optimized conditions.The prepared Ti_(3)AlC_(2−y)N_(y) bulks are dense and have a fine microstructure with grain sizes of 6–8μm.The influence of the N content on the mechanical properties,electrical conductivities,and coefficients of thermal expansion(CTEs)of the prepared Ti_(3)AlC_(2−y)N_(y) bulk materials was clarified.The flexural strength and Vickers hardness values increased with increasing N content,suggesting that solid solution strengthening effectively improved the mechanical properties of Ti_(3)AlC_(2−y)N_(y).Ti_(3)AlCN(y=1)had the highest Vickers hardness and flexural strength among the studied samples,reaching 5.54 GPa and 550 MPa,respectively.However,the electrical conductivity and CTEs of the Ti_(3)AlC_(2−y)N_(y) solid solutions decreased with increasing N content,from 8.93×10^(−6) to 7.69×10^(−6) K^(−1) and from 1.33×10^(6) to 0.95×10^(6) S/m,respectively.This work demonstrated the tunable properties of Ti_(3)AlC_(2−y)N_(y) solid solutions with varying N contents and widened the MAX phase family for fundamental studies and applications.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
基金supported by the Fundamental Research Funds for the Central Universities(Nos.2023YJS061 and 2023JBZY019).
文摘Changing the N content in the Ti_(3)AlC_(2−y)N_(y) MAX phase solid solutions allows for the fine-tuning of their properties.However,systematic studies on the synthesis and properties of Ti_(3)AlC_(2−y)N_(y) solid solution bulks have not been reported thus far.Here,previously reported Ti_(3)AlC_(2−y)N_(y) solid solution bulks(y=0.3,0.5,0.8,and 1.0)were synthesized via hot pressing of their powder counterparts under optimized conditions.The prepared Ti_(3)AlC_(2−y)N_(y) bulks are dense and have a fine microstructure with grain sizes of 6–8μm.The influence of the N content on the mechanical properties,electrical conductivities,and coefficients of thermal expansion(CTEs)of the prepared Ti_(3)AlC_(2−y)N_(y) bulk materials was clarified.The flexural strength and Vickers hardness values increased with increasing N content,suggesting that solid solution strengthening effectively improved the mechanical properties of Ti_(3)AlC_(2−y)N_(y).Ti_(3)AlCN(y=1)had the highest Vickers hardness and flexural strength among the studied samples,reaching 5.54 GPa and 550 MPa,respectively.However,the electrical conductivity and CTEs of the Ti_(3)AlC_(2−y)N_(y) solid solutions decreased with increasing N content,from 8.93×10^(−6) to 7.69×10^(−6) K^(−1) and from 1.33×10^(6) to 0.95×10^(6) S/m,respectively.This work demonstrated the tunable properties of Ti_(3)AlC_(2−y)N_(y) solid solutions with varying N contents and widened the MAX phase family for fundamental studies and applications.
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.