Supercritical-hydrothermal accelerated solid state reaction route for synthesis of LiMn_2O_4 cathode material for high-power Li-ion batteries

Synthesis of the spinel structure lithium manganese oxide （LiMn2O4） by supercritical hydrothermal （SH） accelerated solid state reaction （SSR） route was studied. The impacts of the reaction pressure, reaction temperature and reaction time of SH route, and the calcination temperature of SSR route on the purity, particle morphology and electrochemical properties of the prepared LiMn2O4 materials were studied. The experimental results show that after 15 min reaction in SH route at 400 ℃ and 30 MPa, the reaction time of SSR could be significantly decreased, e.g. down to 3 h with the formation temperature of 800 ℃, compared with the conventional solid state reaction method. The prepared LiMn2O4 material exhibits good crystallinity, uniform size distribution and good electrochemical performance, and has an initial specific capacity of 120 mA.h/g at a rate of 0.1C （1C=148 mA/g） and a good rate capability at high rates, even up to 50C.

Solid State Reaction Yielding a Mineral Utilizing Silica Obtained from an Agricultural Waste

Wollastonite, a mineral of wide industrial applications was synthesised from rice husk ash silica and limestone. A number of raw batches consisting of these starting materials, in 1:1 molar ratio, were heat treated to produce it through solid state reaction from 900℃ to 1300℃. The conducted reaction was monitored by XRD step by step. Amount of Wollastonite formed at every temperature was also studied to some extent. Analyses of the obtained data indicated that the target mineral formation was quite effective and almost proportional to a rise in temperature up to 1200℃. The results from both, XRD and chemical analysis were found in fair agreement with one another

Reaction mechanisms for 0.5Li_2MnO_3 ·0.5LiMn_(0.5)Ni_(0.5)O_2 precursor prepared by low-heating solid state reaction

Lithium-excess manganese layered oxides, which are commonly described in chemical formula 0.5Li2MnO3·0.5LiMn0.5Ni0.5O2, were prepared by low-heating solid state reaction. The reaction mechanisms of synthesizing precursors, the decomposition mechanism, and intermediate materials in calcination were investigated by means of Fourier transform infrared spectroscopy （FT-IR）, X-ray diffraction （XRD）, field emission scanning electron microscopy （FESEM）, thermogravimetric analysis （TGA）, and differential scanning calorimetry （DSC）. The major diffraction patterns of 0.5Li2MnO3·0.5LiMn0.5Ni0.5O2 powder calcinated at 720℃ for 15 h are indexed to the hexagonal structure with a space group of R3m, and the clear splits of doublets at （006）/（102） and （108）/（110） indicate that the sample adopts a well-layered structure. FESEM images show that the size of the agglomerated particles of the sample ranges from 100 to 300 nm.

Synthesis of Mesoporous Chromium Aluminophosphate (CrAlPO) via Solid State Reaction at Low Temperature

Mesoporous chromium aluminophosphate （CrAIPO） was successfully synthesized via solid state reaction （SSR） route at low temperature in the presence of a cationic surfactant cetyltrimethyl ammonium bromide （CTAB） and inorganic sources such as A1C13 · 6H20, CrCI3 · 6H20 and NaH2PO4 · 2H20. Characterizations by means of powder X-ray diffraction （XRD）, N2 adsorption- desorption, high resolution transmission electron microscopy （HR-TEM）, scanning electron micrography （SEM）, energy dispersion spectroscopy （EDS）, thermo-gravimetry （TG）, Fourier transform infrared spectroscopy （FT-IR）, and ultraviolet visible light spectroscopy （UV-Vis） were carried out to understand both the pore characteristics and electron transition route of these obtained materials. The experimental results show that the meso-CrA1PO materials with various Cr/A1 molar ratios possess a mesostructure and a specific surface area of 193 to 310 m2/g corresponding to an average pore size of 5.5 to 2.2 rim, respectively. The maxium content of Cr in meso-CrA1PO materials synthesized via SSR route can achieve 16.7wt%, being significantly higher than that of the meso-CrA1PO prepared via a conventional sol-gel route. Meanwhile, the formation mechanism of the meso-CrA1PO was also proposed.

Synthesis of MgO-Al_2O_3/ZSM-5 by Solid State Reaction for Propane Dehydrogenation

Solid-state grinding is a simple and effective method to introduce guest species into the channels of microporous materials through filling.The structure and the surface acidity of the materials were obtained from BET isotherms and NH3-TPD,respectively.XRD,UV-vis,UV diffuse-reflectance,and TEM were used to characterize the phases,and the morphology,respectively.The clustered layers of MgO-Al2O3phases were formed in the internal pore surface and were highly dispersed inside the channels of the ZSM-5 host.So the volume of MgO-Al2O3/ZSM-5 composite was larger than the ZSM-5 zeolite itself and some mesoporous channels appeared when Mg/Al species entered the channels.Meanwhile,new acid sites emerged in MgO-Al2O3/ZSM-5 composite and the acid amount of the sample changed.The improved Pt dispersion and the increased acid content would cause the increase of propane conversion and the modification of selectivity during the reaction.

Chemical Kinetic Aspects of Solid State Reaction Producing Wollastonite from Rice Husk Silica and Limestone

An industrial mineral wollastonite (CaSiO3) was produced under solid state conditions from rice husk silica and limestone. Reaction was carried out at 900'C to 1300'C for 1 h. The product batches were subjected to XRD and chemical analysis techniques specific for wollastonite. Mole fractions of different product batches were calculated on the basis of accumulated data to study the kinetics. Specific rate constants and reaction rate were also found out. Various probable models of mechanism for reaction were considered and testified with the laid down criterion for suggesting the suitable one. The resulting data were treated with Arrhenius equation as well and activation energy was calculated--therefrom. In addition to finding it's value from the slope of Arrhenius curve, an alternate method was also applied for this purpose. Both of the values were observed to be comparable. The activation energy required for performed reaction was found to be almost one third of that reported for synthesizing CaSiO3 by using quartz. This referred to the economical preparation of wollastonite by using rice husk as a source of silica instead of quartz.

Synthesis of Lanthanide β-Diketonates by Solid State Reaction at Low Heating Temperature

Solid state reactions between β diketones (HPMBP, HDBM) and LnAc 3· x H 2O(La,Nd: x =3/2;Tb: x =4) have been investigated at low heating temperature. Pure compounds of Ln(PMBP) 3 and Ln(DBM) 3 are obtained by solid state reaction, and characterized by elemental analysis, infrared radiation (IR),X ray diffraction (XRD) and photoacoustic spectra. The solid state reaction properties of β diketones and their influences on the structures of products are discussed.

Coating of LiNi_(1/3)Mn_(1/3)Co_(1/3)O_2 cathode materials with alumina by solid state reaction at room temperature

Alumina coated LiNi1/3Mn1/3Co1/3O2 particles were obtained by a simple method of solid state reaction at room temperature. The reaction mechanism of solid state reaction at room temperature was investigated. The structure and morphology of the coating materials were investigated by XRD, SEM and TEM. The electrochemical performances of uncoated and Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials were studied within a voltage window of 3.00?4.35 V at current density of 30 mA/g. SEM, TEM and EDS analytical results indicate that the surface of LiNi1/3Mn1/3Co1/3O2 particles is coated with very fine Al2O3 composite, which leads to the improved cycle ability though a slight decrease in the first discharge capacity is observed. It is proposed that surface treatment by solid state reaction at room temperature is a simple and effective method to improve the cycle performance of LiNi1/3Co1/3Mn1/3O2 particles.

Influence of FeO and sulfur on solid state reaction between MnO-SiO_2-FeO oxides and an Fe-Mn-Si solid alloy during heat treatment at 1473 K

To clarify the influence of Fe O and sulfur on solid state reaction between an Fe-Mn-Si alloy and Mn O-Si O2-Fe O oxides under the restricted oxygen diffusion flux, two diffusion couples with different sulfur contents in the oxides were produced and investigated after heat treatment at 1473 K. The experimental results were also compared with previous work in which the oxides contained higher Fe O. It was found that although the Fe O content in the oxides decreased from 3wt% to 1wt% which was lower than the content corresponding to the equilibrium with molten steel at 1873 K, excess oxygen still diffused from the oxides to solid steel during heat treatment at 1473 K and formed oxide particles. In addition, increasing the sulfur content in the oxides was observed to suppress the diffusion of oxygen between the alloy and the oxides.

Solid State Reaction Synthesis and Thermoelectric Properties ofMg_2Si doped with Sb and Te

Doped with Sb and Te, Mg2Si based compounds were prepared respectively by solid state reaction at 823 K for 8 h. Effects of dopants of Sb and Te on the structure and thermoelectric properties of the compounds were investigated. By calculating the values of the electrical conductivity for Sb-doped sample, the mechanism of electric conduction at 625 K is different. The figure of merit for sample doped with 0.4 wt% Te at500K is 2.4 × 10-3W/mK2,and it reaches 3. 3 ×10-3 W/mK2 at 650K for the sample doped with 0. 5wt% Sb. The values are more than 1.4 times and 2.3 times of the pure Mg2 Si sample.

STUDIES ON SOLID STATE REACTIONS OF COORDINATION COMPOUNDS(LXⅡ)Solid state synthesis and crystal structure of the complex ICu_(0.84)Au_(0.16)(PPh_3)_2(SC(Ph)NHPh)CIJ·0.5CS_2

[Cu_(0.84)Au_(0.16)(PPh_3)_2(SC(Ph)NHPh)Cl]·0.5CS_2=,Mr=895.79,monoclinic,space group P2_1/a,a=17.231(3),b=14.611(2),c=18.000(3) ,β=105.56(2)°,V=4365(1) ~3, Z=4,D_c=1.37g/cm^3.,λ(MoK_α)=0.71073 ,μ=12.15cm^(-1),F(000)=1855,R=0.052, R_W=0.045 for 3930 observed reflections with Ⅰ>1.5σ(Ⅰ).The central metal atom has a dis. torted tetrahedral geometry with bond lengths Cu-S=2.384(2) (Au-S=2.389(4)), Cu-Cl=2.481(3)(Au-Cl=2.474(1))and Cu-P=2.269(2)-2.289(2)(Au-P=2.270(4)-2.279(4)) .

Structure Analysis of Beta-alumina Synthesized by Solid State Reaction

The crystal structure of a solid electrolyte, beta-A12O3, was investigated by XRD analysis and demonstrated by Diamond software. Its chemical formula was verified by the Ag ion molten salt exchange method and X-ray fluorescence analysis （XRF）. The chemical formula of β- A12O3 is Na2O·8.52A12O3, and its crystal is of hexagonal, space group P63/mmc, with a = 5.5941 A and c = 22.5300 A. The chemical formula of β-Al20 is Na2O·6.03A12O3, and its crystal is of trigonal, space group R3m, with a = 5.6017 A and c = 33.6219 A. The maximum span in the sodion migration of β-phase （2.4283 A） is only about a third of that for the β-phase （6.9037 A）, so the β-phase has higher ionic conductivity than the r-phase.

Ag3PO4 Microcrystals Synthesized by Room-Temperature Solid State Reaction:Enhanced Photocatalytic Activity and Photoelectronchemistry Performance

Ag3PO4 microcrystals with highly enhanced visible light photocatalytic activity are prepared by a facile and simple solid state reaction at room temperature. The composition, morphology and optical properties of the asprepared Ag3PO4 microcrystMs are characterized by x-ray diffraction, scanning electron microscopy and UV-vis diffuse reflectance spectra. The photocatalytie properties of Ag3PO4 are investigated by the degradation of both methylene blue and methyl orange dyes under visible light irradiation. The as-prepared Ag3PO4 microcrystals possess high photocatalytic oxygen production with the rate of 673μmolh-1g-1. Moreover, the as-prepared Ag3PO4 microcrystals show an enhanced photoelectrochemistry performance under irradiation of visible light.

Preparing Nano-ZnS by Solid State Reaction at Room Temperature

ZnS nanoparticles were prepared by using solid-state reaction method at room temperature in agate mortar for the first time. The average particle size was about 20nm. This reaction is affected by the structure of reactant, crystal water and defects.

Microstructural evolution of NiFe_2O_4-10NiO powder prepared by high temperature solid state reaction

The NiFe2O4-10NiO powder for inert anode of aluminium electrolysis was prepared by high temperature solid state reaction. The microstructural evolution from the raw materials NiO and Fe2O3 to the NiFe2O4-10NiO powder was studied by SEM. The results show that the domain structure making up of the agglomerate particles of Fe2O3 remains after high temperature solid state reaction, and the diffusion of Ni2+ into Fe2O3 structure is the control step of the reaction process. A microstructure with compact structure and fine grain inside the particle results from the sintering of NiFe2O4-10NiO powder.

Microwave direct synthesis and thermoelectric properties of Mg_(2)Si by solid-state reaction

In order to reduce the oxidation and volatilization caused by Mg element in the traditional methods for synthesizing Mg2Si compounds,Mg2Si thermoelectric materials were prepared by solid state reaction and microwave radiation techniques.Structure and phase composition of the materials were investigated by X-ray diffraction.The electrical conductivity,Seebeck coefficient and thermal conductivity were measured as a function of temperature from 300 to 700 K.It is found that high purity Mg2Si powders can be obtained with excessive content of 8% Mg from the stoichiometric Mg2Si at 853 K and 2.5 kW for 30 min.A maximum dimensionless figure of merit,ZT,of about 0.13 was obtained for Mg2Si at 600 K.

Solid state interfacial reactions in electrodeposited Ni/Sn couples

Ni/Sn couples, prepared by sequentially electroplating Ni layers and Sn layers on metallized Si wafers, were employed to study the microstructures and growth kinetics of Ni-Sn intermediate phases, when the Ni/Sn couples were aged at room temperature or armealed at temperatures from 150 to 225℃ for various times. The results show that the NiSn phase and Ni3Sn4 phase are formed, respectively, in the aged couples and annealed couples. The Ni3Sn4 layer is continuously distributed between the Ni and Sn sides in the annealed Ni/Sn couples. The Ni3Sn4 growth follows parabolic growth kinetics with an apparent activation energy of 39.0 kJ/mol.

SYNTHESIS OF SnO_2 NANOCRYSTALS BY SOLID STATE REACTION FOLLOWED BY CALCINATION

Nanocrystalline SnO2 was synthesized by direct mixing and grinding of SnCl45H2O and NaOH at room temperature, followed by calcination at different temperatures for different times in air. Product samples were character-ized by X-ray diffraction and transmission electron microscope, revealing that the amorphous precursor SnO2 was transformed to crystals at 200 oC for 3 h, and that the average particle size increased upon raising the calcining tem-perature or prolonging the calcining time. The mechanism of the phase transformation of the products is discussed.

The solid state reactions of o-aminobenzoic acid with Zn(Ⅱ), Cu(Ⅱ), Ni(Ⅱ), Mn(Ⅱ) acetate hydrate at room temperature

The solid-solid state reactions of o-aminobenzoic acid with Zn(OAc)2.2H2O, Cu(OAc)2 .H2O, Ni(OAc)2.4H2O and Mn(OAc)2.4H2O result in the formation of corresponding complexes M(OAB)2 (M = Zn(Ⅱ), Cu(Ⅱ), Ni(Ⅱ), Mn(IⅡ)). XRD, IR and elemental analysis methods have been used to characterize the solid products. The activation energies of these reactions, which are calculated from the kinetic data obtained by means of the isothermal electrical conductivity measurement method, have been found to increase in the order: Cu(OAc)2.H2O(37.7 kJ.mol-1)~Mn(OAc)2.4H2O (39.7kJ.mol-1) < Zn(OAc)2.2H2O (56.3 kJ.mol-1) < Ni(OAc)2.4H2O (85.2 kJ.mol-1). The trend is related to their crystal structures.

Solid state reaction of aromatic ketones with heteroaromatics

The solid state reactions of p-nitroacetophenone, acetyl-ferrocene with indole were catalyzed by anhydrous zinc chloride or aluminum chloride, and gave exclusively the 1:2 condensation products. The solid state condensation of aromatic ketones with 1-phenyl-3-methyl-5-pyrazolone was also investigated, and the 1:1 and 2:1 condensation products were obtained. The structures of eleven new products were determined by IR, MS, H-1 NMR and elemental analysis.