Effect of welding temperature and duration on properties of 7075 Al to AZ31B Mg diffusion bonded joint

7075 Al alloy and AZ31B Mg alloy were joined by diffusion welding technique at pressure 29 MPa with various welding temperatures and durations. Scanning electron microscopy examination, shear tests and microhardness evaluation were conducted on the samples interface to find out the effect of welding temperatures and durations on the weldability. The results demonstrate that the AZ31B Mg/7075 Al composite plates are bonded well and the intermetallic phases such as Al_（12）Mg_（17） and Al_（3）Mg_（2） within the joint zone form. It is found that due to the grain coarsening and the formation of brittle compounds, high welding temperatures and long welding durations result in a decrease of shear strength and increase of interfacial welding hardness. The minimum shear strength of 15 MPa along with the maximum microhardness of HV 176 are obtained for the diffusion couple processed at 450 °C for 120 min. It is revealed that enhancing the temperature and choosing appropriate holding time makes a remarkable increase of interfacial welding thickness. Increasing the welding temperature from 430 to 450 °C along with long welding duration（120 min） results in the increase of interfacial welding thickness by 26% where this value is 6% at the welding performed for 60 min.

Three dimensional numerical simulation of welding temperature fields in stainless steel

Three kinds of mathematical models representing welding heat sources are presented. Among them, Gaussian model and double ellipsoidal model are used to analyze the thermal distributions with finite element method. At the same time, this paper analyzed the influences of the heat source models, the latent heat and the welding parameters on the temperature distributions. The comparisons between the simulated results and the experiments show double ellipsoidal model is good for three-dimensional numerical simulations. Furthermore, the adaptive mesh technique is applied in the three-dimensional model which greatly reduces the number of nodes and elements in the simulation.

Real-time measurement of welding temperature field and closed loop control of penetration

Colormetric method of images by using two different wavelength images is a new measuring method for welding temperature field on the basis of ordinary colorimetric method, which depends little on the measuring distance, emissivity of body etc. In this paper the real time measuring system and measuring principle of welding temperature field are described, the whole welding temperature field is real time measured, so the temperature distribution at the welding direction and its cross section is obtained, then parameters of thermal cycle. With data from the temperature closed loop control system of the parameters of temperature field is developed and tested. Experimental results prove that it has high measurement speed (time of a field within 0.5 s ) and good dynamic response quality. Weld penetration can be controlled satisfactorily under the variation of welding condition such as welding thickness, welding speed and weldment gap etc.

Welding temperature field analysis for featheredged cylinder based upon conformal transformation

The accurate calculation and measurement of welding temperature field is an important precondition for welding metallurgical analysis and welding process controlling. In this paper, the conformal transformation is firstly used to analyze the welding temperature field of featheredged cylinder. The center of the cylinder is chosen as the origin of column coordinate system, and every point may be expressed as complex field vector. The branch isogonality counterchanges the line parallel with the fusion line in half-infinite z-plane to the circle concentric with the fusion line in infinite cylinder. The Laplace equation and Poisson＇s equation still keep validity, so the temperature field equation can be solved. The conformal transformation and equation solution is processed by Matlab program language. It shows that the obtained analytical modeling of temperature field for featheredged cylinder based on conformal transformation is effective and accurate.

SIMULATION-MEASUREMENT INVERSION OF ENVIRONMENT PARAMETERS DURING WELDING

The manual selection of environment parameters during welding simulation will bring a significant error to the simulation result of welding temperature field. By a combination of finite element method （FEM） and infrared thermography, these environment parameters were inversed mathematically in place of previous manual selection. First, FEM model of the welding process was constructed, and the temperature field was computed with initial environment parameters. Then, a real welding process was conducted and the temperature field was measured by infrared thermography. Last, the simulation and measurement results were compared, and the environment parameters were adjusted continuously with the genetic algorithm （ GA ） until the simulation matched the measurement best. Parameters according to the best-matched simulation results were considered as the most appropriate parameters.

DIFFUSION WELDING FOR 6061 Al REINFORCED WITH SiCw WHISKER

The weldability of SiCw/6061Al -was investigated. From the results of experiments, it is found that the strength of joint is mainly influenced by welding temperature, and high strength of joint is obtained under melding temperature between liquidus and solidus of matrix alloy. Diffusion welding of SiCw/6061Al was successfully realized with appropriate ivelding parameters.

DEVELOPMENT AND APPLICATION OF ADAPTIVE MESH TECHNIQUE IN THREE DIMENSIONAL NUMERICAL SIMULATION OF WELDING PROCESS

The adaptive mesh mesh technique is developed and applied in three dimensional numerical simulation of welding process on the base of the commercial software. Special user subroutine is worked out to accom- plish this function.This technique can make the dense mesh moving simultaneously with the heat source while the other area of the structure with much coarser mesh, greatly reducing the number of nodes and elements in the analysis.Temperature field,displacement and stress distributions during welding pro- cess me analyzed by FEM method with adaptive mesh and the analysis is also conducted with normal FEM method. The temperature field,displacement and stress distributions obtained with both methods are shown in contrast. The results show that the temperature fields and the displacement distributions of simulation on adaptive mesh correspond wery well with that of without adaptive mesh. Though the stress distributions have some difference,but the trends of the stress distribution are corresponding.The com- parison of the computing time of the two meshes indicates that the adaptive that the adaptive mesh can greatly reduce the calculation time when used for welding process.

Comparative study on local and global mechanical properties of bobbin tool and conventional friction stir welded 7085-T7452 aluminum thick plate

7085-T7452 plates with a thickness of 12 mm were welded by conventional single side and bobbin tool friction stir welding （SS-FSW and BB-FSW, respectively） at different welding parameters. The temperature distribution, microstructure evolution and mechanical properties of joints along the thickness direction were investigated, and digital image correlation （DIC） was utilized to evaluate quantitatively the deformation of different zones during tensile tests. The results indicated that heat-affected zone （HAZ）, the local softening region, was responsible for the early plastic deformation and also the fracture location for SS-FSW samples, while a rapid fracture was observed in weld nugget zone （WNZ） before yield behavior for all BB-FSW specimens. The ultimate tensile strength （UTS） of SS-FSW joints presented the highest value of 410 MPa, 82% of the base material, at a rotational speed of 300 rpm and welding speed of 60 mm/min, much higher than that of BB-FSW joints, with a joint efficiency of only 47%. This should be attributed to the Lazy S defect produced by a larger extent of heat input during the BB-FSW process, The whole joint exhibited a much higher elongation than the slices. Scanning electron microscopic （SEM） analysis of the fracture morphologies showed that joints failed through ductile fracture for SS-FSW and brittle fracture for BB-FSW.

Simulation study on heat-affected zone of high-strain X80 pipeline steel

The microstructure evolution and impact-toughness variation of heat-affected zone（HAZ）in X80 highstrain pipeline steel were investigated via a welding thermal-simulation technique,Charpy impact tests,and scanning electron microscopy observations under different welding heat inputs and peak temperatures.The results indicate that when heat input was between 17 and 25kJ·cm^（-1）,the coarse-grained heat-affected zone showed improved impact toughness.When the heat input was increased further,the martensite-austenite（M-A）islands transformed from fine lath into a massive block.Therefore,impact toughness was substantially reduced.When the heat input was 20kJ·cm^（-1） and the peak temperature of the first thermal cycle was between 900 and 1300°C,a higher impact toughness was obtained.When heat input was 20kJ·cm^（-1） and the peak temperature of the first thermal cycle was 1300°C,the impact toughness value at the second peak temperature of 900°C was higher than that at the second peak temperature of 800°C because of grain refining and uniformly dispersed M-A constituents in the matrix of bainite.