In this study, biosilica of high purity was successfully prepared from marine diatom （Nitzschia closterium and Thalassiosira） biomass using an optimized novel method with acid washing treatment followed by thermal t...In this study, biosilica of high purity was successfully prepared from marine diatom （Nitzschia closterium and Thalassiosira） biomass using an optimized novel method with acid washing treatment followed by thermal treatment of the biomass. The optimal condition of the method was 2% diluted HCl washing and baking at 600℃. The SiO2 contents of N. closterium biosilica and Thalassiosira biosilica were 92.23% and 91.52%, respectively, which were both higher than that of diatomite biosilica. The SiO2 morphologies of both biosilica are typical amorphous silica. Besides, IV. closterium biosilica possessed micropores and fibers with a surface area of 59.81 m^2/g. And Thalassiosira biosilica possessed a mesoporous hierarchical skeleton with a surface area of 9.91 m^2/g. The results suggest that the biosilica samples obtained in this study present highly porous structures. The prepared porous biosilica material possesses great potential to be used as drug delivery carrier, biosensor, biocatalyst as well as adsorbent in the future.展开更多
It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The le...It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The leaching mechanism ofdifferent valuable metals was studied.The results revealed that the leaching rates of Ag,Pb,Cu,Fe,As and Zn were99.91%,99.25%,95.12%,90.15%,87.58%and58.15%,respectively with6mol/L HCl and L/S ratio of10:1at60°C for120min.The actionof SiO2in leaching solution was also studied.The results showed that the precipitation and settlement of SiO2(amorphous)adsorbedpart of metal ions in solution,which greatly inhibited the leaching of Cu,Fe,As and Zn,so it is crucial to control the precipitation ofamorphous SiO2.展开更多
文摘利用溶胶 凝胶技术,控制钛酸四丁酯(TBOT)与硅酸乙酯(TEOS)的水解速度,使其共同水解成溶胶、凝胶,以乙醇为溶剂进行超临界干燥,经过一定温度热处理后,得到暗黄色透明的块体材料·进行了透射电镜观察和X衍射分析,表明锐钛矿结构的纳米TiO2均匀地分散于无定形SiO2基质中·FT IR光谱分析发现纳米TiO2与SiO2基质之间存在着Ti O Si键·在对罗丹明B水溶液的光催化降解中,此块体材料显示较好的光催化活性,在1h内催化降解86%的罗丹明B·此材料克服了粉状TiO2在实际水污染治理应用中的局限性,有着广泛的应用前景·
基金Supported by the Public Science and Technology Research Funds Projects of Ocean,China(No.201305022)the PhD Start-up Fund of Natural Science Foundation of Guangdong Province,China(No.2014A030310326)
文摘In this study, biosilica of high purity was successfully prepared from marine diatom （Nitzschia closterium and Thalassiosira） biomass using an optimized novel method with acid washing treatment followed by thermal treatment of the biomass. The optimal condition of the method was 2% diluted HCl washing and baking at 600℃. The SiO2 contents of N. closterium biosilica and Thalassiosira biosilica were 92.23% and 91.52%, respectively, which were both higher than that of diatomite biosilica. The SiO2 morphologies of both biosilica are typical amorphous silica. Besides, IV. closterium biosilica possessed micropores and fibers with a surface area of 59.81 m^2/g. And Thalassiosira biosilica possessed a mesoporous hierarchical skeleton with a surface area of 9.91 m^2/g. The results suggest that the biosilica samples obtained in this study present highly porous structures. The prepared porous biosilica material possesses great potential to be used as drug delivery carrier, biosensor, biocatalyst as well as adsorbent in the future.
基金Project(51404307)supported by the National Natural Science Foundation of ChinaProject(2014CB643400)supported by the National Basic Research Program of China
文摘It is taken as a novel prospective process to treat iron concentrate from hydrometallurgical zinc kiln slag forcomprehensive utilization of valuable metals by a hydrochloric acid leaching-spray pyrolysis method.The leaching mechanism ofdifferent valuable metals was studied.The results revealed that the leaching rates of Ag,Pb,Cu,Fe,As and Zn were99.91%,99.25%,95.12%,90.15%,87.58%and58.15%,respectively with6mol/L HCl and L/S ratio of10:1at60°C for120min.The actionof SiO2in leaching solution was also studied.The results showed that the precipitation and settlement of SiO2(amorphous)adsorbedpart of metal ions in solution,which greatly inhibited the leaching of Cu,Fe,As and Zn,so it is crucial to control the precipitation ofamorphous SiO2.