During the hydration process, the Ultra-fine Cements present specific physical and chemical characteristics; they are, very short setting time and high heat release. For special applications, such as rapid hardening a...During the hydration process, the Ultra-fine Cements present specific physical and chemical characteristics; they are, very short setting time and high heat release. For special applications, such as rapid hardening and early high strength mortars or concretes, these characteristics can be considered advantageous. Some commercial products used for concrete reinforcement and repairs are the Rapid Hardening Mortars, these mortars must develop a time of setting up to 3 h and an initial compressive strength of about 3.5 MPa once the hardening of the paste is reached. The objective of the present research work is to use Ultra-fine Cement for the preparation of a series of different Rapid Hardening Mortars （with different percentages of Ultra-fine Cement）, these mortars required the addition of a polycarboxylate-base specification F Superplasticizer. It was observed that the optimum water/cement （W/C） ratio for the hydration of the Ultra-fine Cements is W/C = 0.385. The Ultra-fine Cements were obtained by the High Energy Ball-milling technique at laboratory scale, 90% of the Particle Size Distribution is below 11 μm and the Blaine Specific Surface Area is over 9000 cm^2/g.展开更多
文摘During the hydration process, the Ultra-fine Cements present specific physical and chemical characteristics; they are, very short setting time and high heat release. For special applications, such as rapid hardening and early high strength mortars or concretes, these characteristics can be considered advantageous. Some commercial products used for concrete reinforcement and repairs are the Rapid Hardening Mortars, these mortars must develop a time of setting up to 3 h and an initial compressive strength of about 3.5 MPa once the hardening of the paste is reached. The objective of the present research work is to use Ultra-fine Cement for the preparation of a series of different Rapid Hardening Mortars （with different percentages of Ultra-fine Cement）, these mortars required the addition of a polycarboxylate-base specification F Superplasticizer. It was observed that the optimum water/cement （W/C） ratio for the hydration of the Ultra-fine Cements is W/C = 0.385. The Ultra-fine Cements were obtained by the High Energy Ball-milling technique at laboratory scale, 90% of the Particle Size Distribution is below 11 μm and the Blaine Specific Surface Area is over 9000 cm^2/g.