The effect of solvents on the morphology and properties of styrene-butadiene-styrene（SBS, \{Mn=\}99 575, Mw/Mn=1.3, S/B=3∶7） triblock copolymer films was studied in this paper. The solvents used in the study are: e...The effect of solvents on the morphology and properties of styrene-butadiene-styrene（SBS, \{Mn=\}99 575, Mw/Mn=1.3, S/B=3∶7） triblock copolymer films was studied in this paper. The solvents used in the study are: ethylmethylketone, a preferential solvent for the PS block; toluene, a non-preferential solvent for both the PS and the PB blocks; and mixed hexane/cyclohexane（2/5, in volume ratio）, a preferential solvent for the PB block. The morphology of samples cast from solutions from different solvents and then stained by RuO4 was observed by TEM. Moreover, the tensile properties and deformation recovery behavior for these samples were measured and the results are explained according to the microstructures observed.展开更多
Thermal evolution behavior of solution cast film of Poly(2,6 dimethyl 1,4 phenylene oxide)(PPO)/polystyrene(PS) blend was investigated by conventional and modulated differential scanning calorimetry. It was found that...Thermal evolution behavior of solution cast film of Poly(2,6 dimethyl 1,4 phenylene oxide)(PPO)/polystyrene(PS) blend was investigated by conventional and modulated differential scanning calorimetry. It was found that the original PPO/PS blend film is actually composed by a crystalline PPO phase and a non crystalline compatible PPO PS phase. The phase segregated structure state(A) will evolve to non crystalline homogenous structure(B) by subsequent thermal treatment. The effect of annealing temperature on the evolution process was discussed.展开更多
文摘The effect of solvents on the morphology and properties of styrene-butadiene-styrene（SBS, \{Mn=\}99 575, Mw/Mn=1.3, S/B=3∶7） triblock copolymer films was studied in this paper. The solvents used in the study are: ethylmethylketone, a preferential solvent for the PS block; toluene, a non-preferential solvent for both the PS and the PB blocks; and mixed hexane/cyclohexane（2/5, in volume ratio）, a preferential solvent for the PB block. The morphology of samples cast from solutions from different solvents and then stained by RuO4 was observed by TEM. Moreover, the tensile properties and deformation recovery behavior for these samples were measured and the results are explained according to the microstructures observed.
文摘Thermal evolution behavior of solution cast film of Poly(2,6 dimethyl 1,4 phenylene oxide)(PPO)/polystyrene(PS) blend was investigated by conventional and modulated differential scanning calorimetry. It was found that the original PPO/PS blend film is actually composed by a crystalline PPO phase and a non crystalline compatible PPO PS phase. The phase segregated structure state(A) will evolve to non crystalline homogenous structure(B) by subsequent thermal treatment. The effect of annealing temperature on the evolution process was discussed.