The New Niobate Ba5NdTi3Nb7O30 was synthesized by solid state reaction at 1250℃ for 48h. The crystal structure and dielectric properties of Ba5NdTi3Nb7O30 were determined by X ray powder diffraction and dielectric me...The New Niobate Ba5NdTi3Nb7O30 was synthesized by solid state reaction at 1250℃ for 48h. The crystal structure and dielectric properties of Ba5NdTi3Nb7O30 were determined by X ray powder diffraction and dielectric measurements. The results show that Ba5NdTi3Nb7O30 belongs to ferroelectric phase of tetragonal tungsten bronze structure at room temperature with unit cell parameters: a=1.24424(4)nm, c=0.39476(2)nm, calculated density 5.719g·cm-3. Ba5NdTi3Nb7O30 belongs to relaxor ferroelectrics. The phase transition temperature (Tc) of Ba5NdTi3Nb7O30 from ferroelectric to paraelectric is found to shift toward higher temperature side at higher frequency, and Tc is 90℃ at 1kHz. At room temperature, the dielectric constant (εr) and dielectric loss of Ba5NdTi3Nb7O30 decrease with the increase of frequency, and Ba5NdTi3Nb7O30 ceramic have high dielectric constant 489 at 1kHz.展开更多
A niobate was synthesized by doping Bi3＋ in the ternary system BaO- N O- Nb2O5. The crystal structure was determined by X- ray powder diffraction,and it belongs to tetragonal tungsten bronze structure at room tempera...A niobate was synthesized by doping Bi3＋ in the ternary system BaO- N O- Nb2O5. The crystal structure was determined by X- ray powder diffraction,and it belongs to tetragonal tungsten bronze structure at room temperature with unit cell parameters a=1.24777 (2) nm,c=0.39266(1) nm,α =β =γ =90° .Measurements of dielectric properties indicate that phase transitions of Ba3NaBiNb10O30 from paraelectric to ferroelectric occurs at 400℃ ,which is lower than that of B NaNb5O30.展开更多
A New Niobate Ba 6 LaTi 3 Nb 3 O 21 was synthesized by high temperature solid state reaction in the BaO - La 2 O 3 - TiO 2 - Nb 2 O 5 system.The chemical compositions,crystal structure,microstructure,density and melti...A New Niobate Ba 6 LaTi 3 Nb 3 O 21 was synthesized by high temperature solid state reaction in the BaO - La 2 O 3 - TiO 2 - Nb 2 O 5 system.The chemical compositions,crystal structure,microstructure,density and melting point of the new compound were characterized by EPMA,XRD,DTA and so on.Ba 6 LaTi 3 Nb 3 O 21 crystallizes the rhombohedral system with unit cell parameters a=0.57388(2)nm,c=4.9283(3)nm,and space group R3m,Z=3.The structure may be described as six(Nb,Ti)O 6 octahedra corner - sharing along c - axis to form perovskite layer connected by Ba atoms.The Ba 6 LaTi 3 Nb 3 O 21 ceramics exhibits high dielectric of74.1,low dielectric loss of4.7 × 10 -4 and small temperature coefficient of dielectric constant of-69ppm · K -1 at1MHz due to its close structure and relative high dielectric polarizabilities of Ba 2+ ,La 3+ ,Ti 4+ and Nb 5+ .Ba 6 LaTi 3 Nb 3 O 21 might be a suitable candidate of highε r mi - crowave dielectric ceramics.展开更多
A New Niobate Ba 5LaTi 2Nb 3O 18 was synthesized by a high temperature solid state reaction in the BaO-La 2O 3-TiO 2-Nb 2O 5 system. The chemical compositions, crystal structure, microstructure, density and melting po...A New Niobate Ba 5LaTi 2Nb 3O 18 was synthesized by a high temperature solid state reaction in the BaO-La 2O 3-TiO 2-Nb 2O 5 system. The chemical compositions, crystal structure, microstructure, density and melting point of the new compound were characterized by EPMA, XRD, SEM, DTA and so on. Ba 5LaTi 2Nb 3O 18 crystallizes the rhombohedral system with unit cell parameters a=0 573 25(2) nm, c=4 213 9(2) nm, and space group R3m, Z=3. The structure may be described as five (Nb,Ti)O 6 octahedra corner-sharing along c axis to form perovskite layer connected by Ba atoms. The Ba 5LaTi 2Nb 3O 18 ceramic exhibits a high dielectric constant of 80.5, low dielectric loss of 6.5×10 -4 and small temperature coefficient of dielectric constant of -78×10 -6 K -1 at 1 MHz due to its close structure and relative high dielectric polarizabilities of Ba 2+, La 3+, Ti 4+ and Nb 5+. Ba 5LaTi 2Nb 3O 18 might be a suitable candidate of high ε r microwave dielectric ceramics.展开更多
文摘The New Niobate Ba5NdTi3Nb7O30 was synthesized by solid state reaction at 1250℃ for 48h. The crystal structure and dielectric properties of Ba5NdTi3Nb7O30 were determined by X ray powder diffraction and dielectric measurements. The results show that Ba5NdTi3Nb7O30 belongs to ferroelectric phase of tetragonal tungsten bronze structure at room temperature with unit cell parameters: a=1.24424(4)nm, c=0.39476(2)nm, calculated density 5.719g·cm-3. Ba5NdTi3Nb7O30 belongs to relaxor ferroelectrics. The phase transition temperature (Tc) of Ba5NdTi3Nb7O30 from ferroelectric to paraelectric is found to shift toward higher temperature side at higher frequency, and Tc is 90℃ at 1kHz. At room temperature, the dielectric constant (εr) and dielectric loss of Ba5NdTi3Nb7O30 decrease with the increase of frequency, and Ba5NdTi3Nb7O30 ceramic have high dielectric constant 489 at 1kHz.
文摘A niobate was synthesized by doping Bi3＋ in the ternary system BaO- N O- Nb2O5. The crystal structure was determined by X- ray powder diffraction,and it belongs to tetragonal tungsten bronze structure at room temperature with unit cell parameters a=1.24777 (2) nm,c=0.39266(1) nm,α =β =γ =90° .Measurements of dielectric properties indicate that phase transitions of Ba3NaBiNb10O30 from paraelectric to ferroelectric occurs at 400℃ ,which is lower than that of B NaNb5O30.
文摘A New Niobate Ba 6 LaTi 3 Nb 3 O 21 was synthesized by high temperature solid state reaction in the BaO - La 2 O 3 - TiO 2 - Nb 2 O 5 system.The chemical compositions,crystal structure,microstructure,density and melting point of the new compound were characterized by EPMA,XRD,DTA and so on.Ba 6 LaTi 3 Nb 3 O 21 crystallizes the rhombohedral system with unit cell parameters a=0.57388(2)nm,c=4.9283(3)nm,and space group R3m,Z=3.The structure may be described as six(Nb,Ti)O 6 octahedra corner - sharing along c - axis to form perovskite layer connected by Ba atoms.The Ba 6 LaTi 3 Nb 3 O 21 ceramics exhibits high dielectric of74.1,low dielectric loss of4.7 × 10 -4 and small temperature coefficient of dielectric constant of-69ppm · K -1 at1MHz due to its close structure and relative high dielectric polarizabilities of Ba 2+ ,La 3+ ,Ti 4+ and Nb 5+ .Ba 6 LaTi 3 Nb 3 O 21 might be a suitable candidate of highε r mi - crowave dielectric ceramics.
文摘A New Niobate Ba 5LaTi 2Nb 3O 18 was synthesized by a high temperature solid state reaction in the BaO-La 2O 3-TiO 2-Nb 2O 5 system. The chemical compositions, crystal structure, microstructure, density and melting point of the new compound were characterized by EPMA, XRD, SEM, DTA and so on. Ba 5LaTi 2Nb 3O 18 crystallizes the rhombohedral system with unit cell parameters a=0 573 25(2) nm, c=4 213 9(2) nm, and space group R3m, Z=3. The structure may be described as five (Nb,Ti)O 6 octahedra corner-sharing along c axis to form perovskite layer connected by Ba atoms. The Ba 5LaTi 2Nb 3O 18 ceramic exhibits a high dielectric constant of 80.5, low dielectric loss of 6.5×10 -4 and small temperature coefficient of dielectric constant of -78×10 -6 K -1 at 1 MHz due to its close structure and relative high dielectric polarizabilities of Ba 2+, La 3+, Ti 4+ and Nb 5+. Ba 5LaTi 2Nb 3O 18 might be a suitable candidate of high ε r microwave dielectric ceramics.