Analysis of cerium substitution in Co-Sr based spinel ferrites for high frequency application

Spinel ferrites exhibit exceptional magnetic properties,making them a distinctive class of magnetic materials.The sol-gel technique was utilized for the synthesis of spinel ferrites with the chemical formula Co_(0.6)Sr_(0.4)Ce_(x)Fe_(2-x)O_(4). Following that,a comprehensive X-ray diffraction analysis unveiled the crystalline cubic structure of the synthesized materials.Through the utilization of the M-H loop approach,the ferromagnetic attributes of ferrites were assessed,and the assimilation of rare earth elements led to substantial enhancements in saturation magnetization,remanence,and coercivity.Spinel ferrites with a high concentration of rare earth elements have improved direct current resistivity and activation energy.The logarithm of a material's resistance increased from 5.29 to 8.12 Ω·cm as cerium is added.With a change in the amount of cerium,the activation energy goes up from 0.19 to 0.29.By changing the frequency from 5.5 to 9.5 GHz,the dielectric characteristics were determined.As the frequency goes up,the dielectric constant goes down.Spinel ferrites that have been made better in every way can be used in high-frequency applications.

Study on Road Greening in the Main Urban Area of Chongqing City Based on Plant Diversity

The greening situation of 242 road greenbelts in 7 administrative regions in the main urban city of Chongqing City was investigated by field survey, and the plant composition, application frequency, species richness and diversity of plants used for road greening in the main urban area were analyzed. The results show that there were 105 species of plants used for road greening(not including seasonal flowers displayed temporarily) in the main urban area of Chongqing City, belonging to 80 genera, 47 families. Among them, there were 95 species of woody plants and 10 species of perennial herbs, accounting for 90.47% and 9.53% of the total number respectively. Some suggestions were put forward according to the current situation and problems of road greening in the main urban area of Chongqing City.

Fabrication and magnetic properties of NiFe-ZnO nano-granular films

Excellent soft magnetic and high frequency prop- erties were obtained successfully in the （Ni75Fe25）x（ZnO）1-x granular films fabricated on the glass substrate by RF magnetron oblique sputtering. The microstructure, mag- netic and high frequency properties were investigated systematically. High resolution transmission electron micrographs show that the film consists of fcc Ni75Fe25 particles uniformly embedded in an amorphous insulating matrix ZnO with particle size a few nanometers. The （Ni75Fe25）x（ZnO）1-x films exhibit excellent soft magnetic properties in a widex range from 0.50 to 0.80 with coer- civity not exceeding 5 × 10^-4 T, which is ascribed to the exchange coupling between magnetic particles. Especially for the sample with x = 0.64, coercivities in hard and easy axes are 5.0 ×10^-5 and 3.6 × 10^-4 T, respectively, and the electric resistivity ρ reaches 1,790 μΩ.cm. The dependence of complex permeability u = u′- ju″on frequency f shows that the real part u′ is more than 130 below 500 MHz, and the ferromagnetic resonance fre- quency fr reaches 1.32 GHz, implying the promising for high frequency application.

Acoustic transfer function of cavity and its application to rapid evaluation of sound field at low frequency band

A new method to obtain numerical solution of Acoustic Transfer Function (ATF) by BEM is presented. For a simply supported panel backed by a rectangular cavity at low frequency band (0-200 Hz), the frequency property of ATF is analyzed. The relation between the accuracy of the rapid evaluation of sound field and the discretization schemes of the vibrational panel is discussed. The result shows that the method to obtain ATF and the rapid evaluation of sound field using the ATF is suitable to low frequency band. If an appropriate discretization scheme is choosed based on the frequency involved and the effort to obtain ATF, the accuracy of the rapid evaluation of sound field is acceptable.

Sandwich-type composite multilayer films of strontium titanate and barium strontium titanate and their controllable dielectric properties

It is a challenge to reduce the dielectric loss and increase the tunability of pure barium strontium titanate(BST)films for microwave tunable application because these two properties change simultaneously.Herein,a novel composite of strontium titanate(ST)and potassium-doped BST(KBST)has been designed as ST/KBST/ST sandwich-type film with various ST and KBST layers.X-ray diffraction patterns show that the film exhibits cubic perovskite polycrystalline structure composed of BST and ST phase,mainly grow along(110)crystal plane with average grain size of less than 20 nm and decreasing BST phase/ST phase ratio with increasing film thickness.Scanning electron microscope shows that no interfacial layer can be observed,indicating that ST and KBST are fully compounded.Low dielectric loss and high tunability at-10-10 V and stable and excellent dielectric properties at 1 GHz are achieved,meeting the needs of microwave tunable application at high frequency.The surface structures are also studied by other analysis methods,and ST/MgBST/ST sandwich-type film is compared.