High piezoelectric composite films composed of poly(vinylidene fluoride-co-hexafluoropropylene)(PVDF-HFP)and ferromagnetic cobalt ferrite(CoFe_(2)O_(4))(0.00 wt%to 0.2 wt%)are prepared by a solution casting method acc...High piezoelectric composite films composed of poly(vinylidene fluoride-co-hexafluoropropylene)(PVDF-HFP)and ferromagnetic cobalt ferrite(CoFe_(2)O_(4))(0.00 wt%to 0.2 wt%)are prepared by a solution casting method accompanied by uniaxial stretching and high electric field poling.The decisive effect of the poling electric field on the power generating capability was confirmed by the experiments.For pure PVDF-HFP films,when the maximum electric field Emax is 120 MV/m,the calibrated open circuit voltage reaches 2.93 V,which is much higher than those poled at lower electric fields(70 MV/m:1.41 V;90 MV/m:2.11 V).Furthermore,the addition of CoFe_(2)O_(4)also influences the piezoelectricity dramatically.In the samples containing 0.15 wt%CoFe_(2)O_(4),the calibrated open circuit voltage increases to the maximum value of 3.57 V.Meanwhile,the relative fraction of theβ-phase and the crystallinity degree are 99%and 48%,respectively.The effects of CoFe_(2)O_(4)nanoparticles on initial crystallization,uniaxial stretching and high electric field poling are investigated by XRD,FTIR and DSC.展开更多
Electromagnetic interference,which necessitates the rapid advancement of substances with exceptional capabilities for bsorbing electromagnetic waves,is of urgent concern in contemporary society.In this work,CoFe_(2)O_...Electromagnetic interference,which necessitates the rapid advancement of substances with exceptional capabilities for bsorbing electromagnetic waves,is of urgent concern in contemporary society.In this work,CoFe_(2)O_(4)/residual carbon from coal gasification fine slag(CFO/RC)composites were created using a novel hydrothermal method.Various mechanisms for microwave absorption,including conductive loss,natural resonance,interfacial dipole polarization,and magnetic flux loss,are involved in these composites.Consequently,compared with pure residual carbon materials,this composite offers superior capabilities in microwave absorption.At 7.76GHz,the CFO/RC-2 composite achieves an impressive minimum reflection loss(RL_(min))of-43.99 dB with a thickness of 2.44 mm.Moreover,CFO/RC-3 demonstrates an effective absorption bandwidth(EAB)of up to 4.16 GHz,accompanied by a thickness of 1.18mm.This study revealed the remarkable capability of the composite to diminish electromagnetic waves,providing a new generation method for microwave absorbing materials of superior quality.展开更多
基金supported by National Natural Science Foundation of China(No.51703015)Fundamental Research Funds for the Central Universities(No.2020CDJQY-A008).
文摘High piezoelectric composite films composed of poly(vinylidene fluoride-co-hexafluoropropylene)(PVDF-HFP)and ferromagnetic cobalt ferrite(CoFe_(2)O_(4))(0.00 wt%to 0.2 wt%)are prepared by a solution casting method accompanied by uniaxial stretching and high electric field poling.The decisive effect of the poling electric field on the power generating capability was confirmed by the experiments.For pure PVDF-HFP films,when the maximum electric field Emax is 120 MV/m,the calibrated open circuit voltage reaches 2.93 V,which is much higher than those poled at lower electric fields(70 MV/m:1.41 V;90 MV/m:2.11 V).Furthermore,the addition of CoFe_(2)O_(4)also influences the piezoelectricity dramatically.In the samples containing 0.15 wt%CoFe_(2)O_(4),the calibrated open circuit voltage increases to the maximum value of 3.57 V.Meanwhile,the relative fraction of theβ-phase and the crystallinity degree are 99%and 48%,respectively.The effects of CoFe_(2)O_(4)nanoparticles on initial crystallization,uniaxial stretching and high electric field poling are investigated by XRD,FTIR and DSC.
基金financially supported by the Key Project of Natural Science Research in Colleges and Universities of Anhui Province,China(No.2022AH050816)the Open Research Grant of Joint National-Local Engineering Research Centre for Safe and Precise Coal Mining(Nos.EC2023013 and EC2022018)+1 种基金the National Natural Science Foundation of China(No.52200139)the Introduction of Talent in Anhui University of Science and Technology,China(Nos.2021yjrc18 and 2023yjrc79)。
文摘Electromagnetic interference,which necessitates the rapid advancement of substances with exceptional capabilities for bsorbing electromagnetic waves,is of urgent concern in contemporary society.In this work,CoFe_(2)O_(4)/residual carbon from coal gasification fine slag(CFO/RC)composites were created using a novel hydrothermal method.Various mechanisms for microwave absorption,including conductive loss,natural resonance,interfacial dipole polarization,and magnetic flux loss,are involved in these composites.Consequently,compared with pure residual carbon materials,this composite offers superior capabilities in microwave absorption.At 7.76GHz,the CFO/RC-2 composite achieves an impressive minimum reflection loss(RL_(min))of-43.99 dB with a thickness of 2.44 mm.Moreover,CFO/RC-3 demonstrates an effective absorption bandwidth(EAB)of up to 4.16 GHz,accompanied by a thickness of 1.18mm.This study revealed the remarkable capability of the composite to diminish electromagnetic waves,providing a new generation method for microwave absorbing materials of superior quality.