WC-10Co cemented carbides with finer WC and narrower grain size distributions are produced by using(Cr,V)_(2)(C,N)as grain growth inhibitors.As a result,with the increase of(Cr_(0.9),V_(0.1))_(2)(C,N)and(V_(0.9),Cr_(0...WC-10Co cemented carbides with finer WC and narrower grain size distributions are produced by using(Cr,V)_(2)(C,N)as grain growth inhibitors.As a result,with the increase of(Cr_(0.9),V_(0.1))_(2)(C,N)and(V_(0.9),Cr_(0.1))_(2)(C,N),the grains size of WC and mean free path of Co phase decrease,and adjacency of WC increases.Refinement and homogenization of grains enhance the transverse rupture strength(TRS)and the hardness.Meanwhile,the deflection and bridging of cracks keep the fracture toughness at a respectable level.The WC-10Co-0.6(Cr_(0.9),V_(0.1))_(2)(C,N)-0.025(V_(0.9),Cr_(0.1))_(2)(C,N)cemented carbides exhibit excellent comprehensive mechanical properties with the TRS of 4602.6 MPa,hardness of 1835 kg/mm^(2),and fracture toughness of 10.39 MPa·m^(1/2),respectively.However,the large pores are caused by excess N larger than 0.03 wt%and deteriorates the mechanical properties.We provide a new approach to WC-Co cemented carbides preparation with a narrow grain size distribution by adding novel grain growth inhibitors.展开更多
A Cr/Cr2N/CrN multilayer coating with a thickness of 24.4 μm was deposited by multi-arc ion plating. The coating was systematically characterized by field emission scanning electron microscopy(FESEM), X-ray photoelec...A Cr/Cr2N/CrN multilayer coating with a thickness of 24.4 μm was deposited by multi-arc ion plating. The coating was systematically characterized by field emission scanning electron microscopy(FESEM), X-ray photoelectron spectrometry(XPS), energy dispersive spectroscopy(EDS), X-ray diffraction(XRD) and transmission electron microscopy(TEM). Hardness and adhesion were tested by nanoindentation and scratch tester, respectively. The friction properties were investigated by a reciprocating UMT-3MT ball-on-disk tribometer in air and seawater. The results showed that the multilayer coating consisted of three different layers, with Cr,Cr2N and CrN phases, respectively. Compared with CrN single layer coating, the adhesion of the multilayer coating was improved significantly, the hardness of the multilayer coating was(21±2) GPa. The corrosion resistance of the multilayer coating was also improved in artificial seawater. The friction coefficient of multilayer coating was lower than that of CrN single layer coating both in air and seawater.展开更多
Effects of VC/Cr3C2 on the microstructure and mechanical properties of Ti（C,N）-based cermets were studied. The microstructure was investigated by means of optical microscopy, X-ray diffractometry as well as scanning...Effects of VC/Cr3C2 on the microstructure and mechanical properties of Ti（C,N）-based cermets were studied. The microstructure was investigated by means of optical microscopy, X-ray diffractometry as well as scanning electron microscopy in combination with energy dispersive spectrometry. Mechanical properties, such as transverse rupture strength, hardness and fracture toughness, were measured. The results show that there are black core-grey rim structure and white core-grey rim structure in the microstructure. The grains become fine due to the VC/Cr3C2, and the grains of cermet added with 0.75VC/0.25Cr3C2 are refined most remarkably. The black core becomes finer with the increase of VC addition and rim phase becomes thicker with the decrease of Cr3C2 addition. The porosity increases with the increase of VC addition in VC/Cr3C2. Compared with the cermet free of VC/Cr3C2, the transverse rupture strength and hardness of cermets with VC/Cr3C2 are both improved, and the maximum values are both found for the cermet with 0.25VC/0.75Cr3C2. The fracture toughness can be effectively promoted by adding VC/Cr3C2 with an appropriate ratio of VC to Cr3C2, and the maximum value is found for the cermet with 0.5VC/0.5Cr3C2.展开更多
利用电化学工作站测试N80和Cr13两种钢在饱和CO_2油田采出液中添加不同浓度的ZK缓蚀剂的腐蚀行为,分析缓蚀剂用量对其腐蚀行为的影响规律,用高温高压反应釜借助失重法和腐蚀形貌观察确定最佳缓蚀剂用量下两种钢的缓蚀性能。结果表明:静...利用电化学工作站测试N80和Cr13两种钢在饱和CO_2油田采出液中添加不同浓度的ZK缓蚀剂的腐蚀行为,分析缓蚀剂用量对其腐蚀行为的影响规律,用高温高压反应釜借助失重法和腐蚀形貌观察确定最佳缓蚀剂用量下两种钢的缓蚀性能。结果表明:静态时,N80和Cr13钢在饱和CO_2油田采出液中分别呈现活化和钝化特征,N80钢的ZK缓蚀剂最佳用量为500 m L/L,而Cr13钢则为1 000 m L/L;动态时,N80钢缓蚀效率达97.95%,而Cr13钢则为95.20%。展开更多
基金Funded by the 2021 Strategic Cooperation Project between Sichuan University and The People's Government of Zigong(No.2021CDZG-1)Major Science and Technology Research Projects of Panxi,Sichuan Province(No.2022PXZB-04)。
文摘WC-10Co cemented carbides with finer WC and narrower grain size distributions are produced by using(Cr,V)_(2)(C,N)as grain growth inhibitors.As a result,with the increase of(Cr_(0.9),V_(0.1))_(2)(C,N)and(V_(0.9),Cr_(0.1))_(2)(C,N),the grains size of WC and mean free path of Co phase decrease,and adjacency of WC increases.Refinement and homogenization of grains enhance the transverse rupture strength(TRS)and the hardness.Meanwhile,the deflection and bridging of cracks keep the fracture toughness at a respectable level.The WC-10Co-0.6(Cr_(0.9),V_(0.1))_(2)(C,N)-0.025(V_(0.9),Cr_(0.1))_(2)(C,N)cemented carbides exhibit excellent comprehensive mechanical properties with the TRS of 4602.6 MPa,hardness of 1835 kg/mm^(2),and fracture toughness of 10.39 MPa·m^(1/2),respectively.However,the large pores are caused by excess N larger than 0.03 wt%and deteriorates the mechanical properties.We provide a new approach to WC-Co cemented carbides preparation with a narrow grain size distribution by adding novel grain growth inhibitors.
基金Project(51475449)supported by the National Natural Science Foundation of China
文摘A Cr/Cr2N/CrN multilayer coating with a thickness of 24.4 μm was deposited by multi-arc ion plating. The coating was systematically characterized by field emission scanning electron microscopy(FESEM), X-ray photoelectron spectrometry(XPS), energy dispersive spectroscopy(EDS), X-ray diffraction(XRD) and transmission electron microscopy(TEM). Hardness and adhesion were tested by nanoindentation and scratch tester, respectively. The friction properties were investigated by a reciprocating UMT-3MT ball-on-disk tribometer in air and seawater. The results showed that the multilayer coating consisted of three different layers, with Cr,Cr2N and CrN phases, respectively. Compared with CrN single layer coating, the adhesion of the multilayer coating was improved significantly, the hardness of the multilayer coating was(21±2) GPa. The corrosion resistance of the multilayer coating was also improved in artificial seawater. The friction coefficient of multilayer coating was lower than that of CrN single layer coating both in air and seawater.
基金Project (090414185) supported by the Natural Science Foundation of Anhui Province, China
文摘Effects of VC/Cr3C2 on the microstructure and mechanical properties of Ti（C,N）-based cermets were studied. The microstructure was investigated by means of optical microscopy, X-ray diffractometry as well as scanning electron microscopy in combination with energy dispersive spectrometry. Mechanical properties, such as transverse rupture strength, hardness and fracture toughness, were measured. The results show that there are black core-grey rim structure and white core-grey rim structure in the microstructure. The grains become fine due to the VC/Cr3C2, and the grains of cermet added with 0.75VC/0.25Cr3C2 are refined most remarkably. The black core becomes finer with the increase of VC addition and rim phase becomes thicker with the decrease of Cr3C2 addition. The porosity increases with the increase of VC addition in VC/Cr3C2. Compared with the cermet free of VC/Cr3C2, the transverse rupture strength and hardness of cermets with VC/Cr3C2 are both improved, and the maximum values are both found for the cermet with 0.25VC/0.75Cr3C2. The fracture toughness can be effectively promoted by adding VC/Cr3C2 with an appropriate ratio of VC to Cr3C2, and the maximum value is found for the cermet with 0.5VC/0.5Cr3C2.
文摘利用电化学工作站测试N80和Cr13两种钢在饱和CO_2油田采出液中添加不同浓度的ZK缓蚀剂的腐蚀行为,分析缓蚀剂用量对其腐蚀行为的影响规律,用高温高压反应釜借助失重法和腐蚀形貌观察确定最佳缓蚀剂用量下两种钢的缓蚀性能。结果表明:静态时,N80和Cr13钢在饱和CO_2油田采出液中分别呈现活化和钝化特征,N80钢的ZK缓蚀剂最佳用量为500 m L/L,而Cr13钢则为1 000 m L/L;动态时,N80钢缓蚀效率达97.95%,而Cr13钢则为95.20%。